Silicon implantation and annealing in β -Ga 2 O 3 : Role of ambient, temperature, and time
Optimizing thermal anneals of Si-implanted β-Ga 2 O 3 is critical for low resistance contacts and selective area doping. Here we report the impact of annealing ambient, temperature, and time on the activation of room temperature ion-implanted Si in β-Ga 2 O 3 at concentrations from 5 × 10 18 to 1 × 10 20 cm −3 , demonstrating full activation (>80% activation, mobilities >70 cm 2 /V s) with contact resistances below 0.29 Ω mm. Homoepitaxial β-Ga 2 O 3 films, grown by plasma-assisted molecular beam epitaxy on Fe-doped (010) substrates, were implanted at multiple energies to yield 100 nm box profiles of 5 × 10 18 , 5 × 10 19, and 1 × 10 20 cm −3 . Anneals were performed in an ultra-high vacuum-compatible quartz furnace at 1 bar with well-controlled gas compositions. To maintain β-Ga 2 O 3 stability, p O2 must be greater than 10 −9 bar. Anneals up to p O2 = 1 bar achieve full activation at 5 × 10 18 cm −3, while 5 × 10 19 cm −3 must be annealed with p O2 ≤ 10 −4 bar, and 1 × 10 20 cm −3 requires p O2 < 10 −6 bar. Water vapor prevents activation and must be maintained below 10 −8 bar. Activation is achieved for anneal temperatures as low as 850 °C with mobility increasing with anneal temperatures up to 1050 °C, though Si diffusion has been reported above 950 °C. At 950 °C, activation is maximized between 5 and 20 min with longer times resulting in decreased carrier activation (over-annealing). This over-annealing is significant for concentrations above 5 × 10 19 cm −3 and occurs rapidly at 1 × 10 20 cm −3 . Rutherford backscattering spectrometry (channeling) suggests that damage recovery is seeded from remnant aligned β-Ga 2 O 3 that remains after implantation; this conclusion is also supported by scanning transmission electron microscopy showing retention of the β-phase with inclusions that resemble the γ-phase.