DOE OSTI2025

Stress Corrosion Cracking of NaSICON Membranes in Aqueous Electrolytes for Redox-Flow Batteries

The sodium super-ionic conductor (NaSICON) has versatile applications as a ceramic electrolyte for energy storage, where it can serve as an impermeable separator in solid-state batteries and redox flow systems. In particular, NaSICON systems have been proposed to be relatively stable in contact with water, making them compatible with aqueous battery chemistries. However, owing to their brittle nature and metal oxide constituents, stress-corrosion cracking (SCC) is an important failure mechanism that has not been previously explored. In this study, we assess the fracture toughness of NaSICON membranes in contact with aqueous solutions that are relevant to redox flow systems. Microindentation was performed to generate visible surface cracks and residual stress, which were observed to grow in length after exposure to aqueous solutions. This allows for a quantitative measurement of fracture toughness, which decreases after exposure to water. To contextualize these results, we develop a simplified model of the fracture behavior in aqueous redox-flow batteries that incorporate NaSICON membranes, illustrating the importance of SCC in cell design. This work provides quantitative insights into SCC as a failure mode in NaSICON, enhancing our understanding of the chemo-mechanical behavior of ceramic electrolytes in contact with aqueous solutions.

Zhang, Mengyao↗
DOE OSTI2024

Understanding Process–Structure Relationships during Lamination of Halide Perovskite Interfaces

Fabrication of halide perovskite (HP) solar cells typically involves the sequential deposition of multiple layers to create a device stack, which is limited by the thermal and chemical incompatibility of top contact layers with the underlying HP semiconductor. One emerging strategy to overcome these restrictions on material selection and processing conditions is lamination, where two half-stacks are independently processed and then diffusion bonded to complete the device. Lamination reduces the processing constraints on the top side of the solar cell to allow new device designs, expanded use of deposition methods, and self-encapsulation of devices. While laminated perovskite solar cells with high efficiencies and novel interlayer combinations have been demonstrated, there is a limited understanding of how the lamination process parameters affect the diffusion-bond quality and material properties of the resulting HP layer. In this study, we systematically vary temperature, pressure, and time during lamination and quantify the resulting impacts on bonded area, grain domain size, and photoluminescence. A design of experiments is performed, and statistical analysis of the experimental results is used to quantitatively evaluate the resulting process–structure–property relationships. The lamination temperature is found to be the key parameter controlling these properties. Furthermore, a temperature of 150 °C enables successful bonding over 95% of the substrate area and also results in increases in apparent grain domain size and photoluminescence intensity. Based on these insights, the lamination temperature of functional perovskite solar cell devices is varied, demonstrating the importance of the resulting bond quality on device performance metrics.

14 SOLAR ENERGY↗
DOE OSTI2020

Influence of the Turing instability on the motion of domain boundaries

Turing's theory of pattern formation has provided crucial insights into the behavior of various biological, geographical, and chemical systems over the last few decades. Existing studies have focused on moving-boundary Turing systems for which the motion of the boundary is prescribed by an external agent. In this paper, we present an extension of this theory to a class of systems in which the front motion is governed by the physical processes that occur within the domain. Biological systems exhibiting apically dominant growth and corrosion of metals and alloys highlight some of the noteworthy examples of such systems. In this study, we characterize the nature of interaction between the moving front and the Turing-instability for both an activator-inhibitor and an activator-substrate model. Behavioral regimes of periodic, as well as nonperiodic (nonconstant), growth rates are obtained. Furthermore, the trends in the first show striking similarities with the cyclic-boundary-kinetics observed in experimental systems. In general, a stationary, periodic structure is also left behind the moving front. If the periodicity of the boundary kinetics agrees with the allowed range of the stable-periodic solutions, the pattern formed tends to persist. Lastly, it evolves to a nearby energy-minimum either by peak-splitting, peak-decay, or by settling down to a spatially homogeneous state.

99 GENERAL AND MISCELLANEOUS↗