DOE OSTI2022

Critical differences between electron beam melted and selective laser melted Ti-6Al-4 V

Effective optimization of the production of Ti-6Al-4 V using AM requires a fundamental understanding of the relative importance of different microstructural features to the deformation and failure mechanisms, particularly features that vary between production methods. In this study, the tensile response and deformation mechanisms of electron beam melted (EBM) AM Ti-6Al-4 V material loaded in different orientations and produced using various powder sizes were compared to those of selective laser melted (SLM) AM Ti-6Al-4 V material. The density and morphology of pores, phase fractions, prior-β grains, and defect microstructures were evaluated using scanning electron microscopy, X-ray computed tomography, electron backscatter diffraction, and transmission electron microscopy before and after deformation. The results were used to evaluate the relative importance of each feature on strengthening, deformation, and failure initiation mechanisms. Results focused primarily on coarse-powder EBM materials indicated that phase distribution and defect density were most influential for determining material yield strength as well as maximum possible strain to failure. Porosity was lower overall in EBM Ti-6Al-4 V than in SLM, allowing for occasional increases in part strain to failure, but remained a limiting factor determining overall part ductility.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Tailoring Microstructure and Mechanical Properties of Additively-Manufactured Ti6Al4V Using Post Processing

Additively-manufactured Ti-6Al-4V (Ti64) exhibits high strength but in some cases inferior elongation to those of conventionally manufactured materials. Post-processing of additively manufactured Ti64 components is investigated to modify the mechanical properties for specific applications while still utilizing the benefits of the additive manufacturing process. The mechanical properties and fatigue resistance of Ti64 samples made by electron beam melting were tested in the as-built state. Several heat treatments (up to 1000 °C) were performed to study their effect on the microstructure and mechanical properties. Phase content during heating was tested with high reliability by neutron diffraction at Los Alamos National Laboratory. Two different hot isostatic pressings (HIP) cycles were tested, one at low temperature (780 °C), the other is at the standard temperature (920 °C). The results show that lowering the HIP holding temperature retains the fine microstructure (~1% β phase) and the 0.2% proof stress of the as-built samples (1038 MPa), but gives rise to higher elongation (~14%) and better fatigue life. The material subjected to a higher HIP temperature had a coarser microstructure, more residual β phase (~2% difference), displayed slightly lower Vickers hardness (~15 HV10N), 0.2% proof stress (~60 MPa) and ultimate stresses (~40 MPa) than the material HIP’ed at 780 °C, but had superior elongation (~6%) and fatigue resistance. Heat treatment at 1000 °C entirely altered the microstructure (~7% β phase), yield elongation of 13.7% but decrease the 0.2% proof-stress to 927 MPa. The results of the HIP at 780 °C imply it would be beneficial to lower the standard ASTM HIP temperature for Ti6Al4V additively manufactured by electron beam melting.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Visualization of texture components using MTEX

Knowledge of the appearance of texture components and fibres in pole figures, in inverse pole figures and in Euler space is fundamental for texture analysis. For cubic crystal systems, such as steels, an extensive literature exists and, for example, the book by Matthies, Vinel & Helming [Standard Distributions in Texture Analysis: Maps for the Case of Cubic Orthorhomic Symmetry, (1987), Akademie-Verlag Berlin] provides an atlas to identify texture components. For lower crystal symmetries, however, equivalent comprehensive overviews that can serve as guidance for the interpretation of experimental textures do not exist. Here, this paper closes this gap by providing a set of scripts for the MTEX package [Bachmann, Hielscher & Schaeben (2010). Solid State Phenom.160, 63–68] that allow the texture practitioner to compile such an atlas for a given material system, thus aiding orientation distribution function analysis also for non-cubic systems.

36 MATERIALS SCIENCE↗