Torrez, Michael Albert

DOE OSTI2024

Alloying effects on deformation induced microstructure evolution in copper

In this work, we investigated the effects of alloying elements on plastic deformation and microstructure evolution in polycrystalline copper (Cu) and Cu alloyed with 1 wt. % lead (Cu-1 %Pb). These materials were selected due to the size mismatch between Cu and Pb, with the latter forming precipitates at grain boundaries. Multi-modal characterization techniques, including neutron diffraction, electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM), along with finite element simulations were employed to study the deformation behavior across multiple length scales. While both Cu and Cu-1%Pb exhibited similar macroscale response and final deformation textures, both dislocation line profile analysis and TEM revealed increased dislocation density in deformed Cu-1%Pb specimens. The presence of lead precipitates also significantly affected local plastic deformation during compression, with their influence diminishing with increasing strain. These results demonstrate the complex relationships between alloying elements, plastic deformation, microstructural evolution, and material behavior under load. The insights gained from this multi-scale and multi-technique approach contribute to the fundamental understanding of microstructural evolution in immiscible alloys and are valuable for tailoring the properties of structural materials for specific engineering applications.

36 MATERIALS SCIENCE↗

DOE OSTI2024

High-temperature structure, elasticity, and thermal expansion of ε-ZrH 1.8

Zirconium hydride is a promising candidate material for nuclear microreactor applications as a solid-state moderator component, owing to its favorable neutronics properties and good thermal stability over other metal hydrides. Here, in the present work, the crystal structure, thermal expansion, and elastic properties of the hydrogen-rich ε phase hydride were measured at elevated temperatures in the range 300–900 K. Samples were prepared by direct hydriding Zircaloy-4 metal – a nuclear-grade zirconium alloy. Room-temperature lattice parameters agree well with those reported from literature for unalloyed zirconium hydride and fall within an observed quadratic H-content dependence. The coefficients of thermal expansion, determined from lattice expansion and dilatometry, agree well within our work but were about 30 % lower than those reported by others for unalloyed hydrides. Density functional theory-based molecular dynamics simulations were used to compare with thermal expansion and elasticity measurements. Results showed lattice parameter temperature dependence and slope of thermal expansion align with those from measurements. Based on diffraction scans at select temperatures, ε phase remained stable in air up to at least 770 K. Likewise, dilatometry showed smooth thermal expansion up to the thermal decomposition temperature around 950 K. The precise decomposition temperature was not determined via diffraction due to sparse scanning. The complete elastic property measurements were gathered for ε-phase Ziracloy-4 hydride for the first time. Young's modulus was lower compared to the metal and δ hydride phases. High-temperature elasticity measurements were limited to <350 K due to acoustic dissipation effects.

36 MATERIALS SCIENCE↗