Aromatic polyamides with improved nonflammability characteristics are produced by contacting a polyamide substrate with a gaseous medium comprising a minor amount of a haloolefinic material and an inert diluent in the presence of light having sufficient energy to effect chemical addition of the haloolefin to the polyamide substrate.
Flame resistance treatment for acid resistant polyamide fibers involving photoaddition of fluorocarbons to surface has been scaled up to treat 10 yards of commercial width (41 in.) fabric. Process may be applicable to other low cost polyamides, polyesters, and textiles.
Technology which renders aramid fibrous structures flame resistant through chemical modification was developed. The project scaled up flame resistant treatment from laboratory fabric swatches of a few inches to efficiently producing ten yards of commercial width (41 inches) aromatic polyamide. The radiation intensity problem of the processor was resolved. Further improvement of the processor cooling system was recommended for two reasons: (1) To advance current technology of flame proofing Nomex fabric to higher oxygen enriched atmospheres; and (2) To adapt the processor for direct applicability to low cost commercial fabrics.
Economical process improves flame resistance and resistance to acids of polyamide fibers, without modifying colors of mechanical properties. Process improves general safety of garments and other items made from polyamide fibers and makes them suitable for applications requiring exposure to oxygen-rich atmosphere or corrosive acids. Halo-olefins are added to surface of fibers by photoadditon in sealed chamber. Process could be used with films and other forms of polyamide.
Flame resistant fibrous materials for space shuttle application were developed through chemical modification of commercially available aromatic polyamide fibrous products. The new surface treatment was achieved in the laboratory by ultraviolet activation of the fabric in the presence of fluoroolefin monomers and a diluent gas. The monomers grafted under these conditions provide the improved properties of the fabric in flame resistance, chemical inertness, and nonwettability without the sacrifice of color or physical properties. The laboratory reaction vessel was scaled-up to a batch continuous process, which treats ten yards of the commercial width textiles. The treated commercial width Nomex (HT-10-41) from the scaled-up reactor is self-extinguishing in an oxygen-enriched environment, water-repellent, soft, silky, and improved in chemical resistance. Unlike most textile processes, the grafting unit operates under dry conditions and no chemical by-products have to be washed out of the finished product.
The reaction oxygen difluoride, OF2, with ethylenically unsaturated fluorocarbon compounds is examined. Depending upon the fluorocarbon material and reaction conditions, OF2 can chain extend fluoropolyenes, convert functional perfluorovinyl groups to acyl fluoride and/or epoxide groups, and act as a monomer for an addition type copolymerization with diolefins.
The present deficiencies in the fluorocarbon sulfonic acid membrane used as the solid polymer electrolyte in the H2/O2 fuel cell are studied. Considered are: Adhesives selection, elastomeric formulations, scavenger exploration, and membrane characterization. The significant data are interpreted and recommendations are given for both short and long range further investigations in two of the four major areas: membrane adhesives and membrane stabilization.
Peroxide catalyst under mild conditions initiates homopolymerization of perfluoro butadiene to new linear perfluoro polyenes and vulcanizable fluoro elastomers. Resulting polyperfluoro butadiene serves as hard elastomer for good chemical resistance, as intermediate in graft polymerizations, and as crosslink for high molecular weight materials.
Oxygen difluoride synthesis is a much simpler, higher-yield procedure than reactions originally followed to synthesize various fluorinated organic compounds. Extreme care is taken in working with oxygen difluoride as its reactions present severe explosion hazard.
Two-step process for preparing fluorocarbon materials includes - /1/ adding gaseous fluorine to a polyperfluoropolyene to create fluorocarbon radicals, with reactive sites at unsaturated carbon atoms, and /2/ introducing a monomer, after evacuation of fluorine gas, and allowing copolymerization with the free radicals.
Diisopropyl peroxydicarbonate dissolved in liquid perfluorobutadiene is conducted in a sealed vessel at the autogenous pressure of polymerization. Reaction temperature, ratio of catalyst to monomer, and amount of agitation determine degree of polymerization and product yield.
Polyperfluorobutadiene reactions for developing oxidation resistant elastomers for space propulsion
Synthesis of polyfluorobutadiene by polymerization of perfluorobutadiene with diisopropyl peroxydicarbonate
Low pressure perfluorobutadiene polymerization with peroxide catalysts