Pressure-induced shift of effective Ce valence, Fermi energy and phase boundaries in CeOs 4 Sb 12

Abstract CeOs 4 Sb 12 , a member of the skutterudite family, has an unusual semimetallic low-temperature L -phase that inhabits a wedge-like area of the field H —temperature T phase diagram. We have conducted measurements of electrical transport and megahertz conductivity on CeOs 4 Sb 12 single crystals under pressures of up to 3 GPa and in high magnetic fields of up to 41 T to investigate the influence of pressure on the different H – T phase boundaries. While the high-temperature valence transition between the metallic H -phase and the L -phase is shifted to higher T by pressures of the order of 1 GPa, we observed only a marginal suppression of the S -phase that is found below 1 K for pressures of up to 1.91 GPa. High-field quantum oscillations have been observed for pressures up to 3.0 GPa and the Fermi surface of the high-field side of the H -phase is found to show a surprising decrease in size with increasing pressure, implying a change in electronic structure rather than a mere contraction of lattice parameters. We evaluate the field-dependence of the effective masses for different pressures and also reflect on the sample dependence of some of the properties of CeOs 4 Sb 12 which appears to be limited to the low-field region.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗

DOE OSTI2022

Hot Hydride Superconductivity Above 550 K

The search for room temperature superconductivity has accelerated in the last few years driven by experimentally accessible theoretical predictions that indicated alloying dense hydrogen with other elements could produce conventional superconductivity at high temperatures and pressures. These predictions helped inform the synthesis of simple binary hydrides that culminated in the discovery of the superhydride LaH 10 with a superconducting transition temperature T c of 260 K at 180 GPa. We have now successfully synthesized a metallic La-based superhydride with an initial T c of 294 K. When subjected to subsequent thermal excursions that promoted a chemical reaction to a higher order system, the Tc onset was driven irreversibly to 556 K. X-ray characterization confirmed the formation of a distorted LaH 10 based backbone that suggests the formation of ternary or quaternary compounds with substitution at the La and/or H sites. The results provide evidence for hot superconductivity, aligning with recent predictions for higher order hydrides under pressure.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗