DOE OSTI2024

Experimental Investigations into the Corrosion of Alloy 625 Using NaCl-PuCl3 Molten Salt in a Natural Circulation Microloop

Molten salt reactors (MSRs) can potentially revolutionize the nuclear industry by providing a path to a near-zero nuclear waste fuel cycle, contributing to more sustainable energy sources. As a plethora of MSR developers in the United States work toward an aggressive commercialization timeline, many of their fueled-salts—notably, chloride-based compositions—have limited operational testing with nuclear material. Licensing and operating these reactors require an understanding of corrosion effects on reactor materials of construction under operational conditions. The TerraPower Molten Chloride Fast Reactor (MCFR) is a liquid-fueled chloride-salt fast reactor which has received notable interest from the utility sector based on its desirable economic characteristics. The reactor operates at low pressure but does not require the use of highly reactive chemicals, leading to a reduced use of concrete and steel during construction. Additionally, liquid fuel allows for inherently stable behavior and natural circulation during a loss-of-site-power scenario. MCFR can be refueled while operating which makes it compatible with variable generation sources such as wind and solar. MCFR is a breed-and-burn in-situ reactor that does not implement any chemical processing or separations in the fuel cycle. Only mechanical filtration of noble metals and off-gassing of noble gases are utilized while the actinides stay mixed with the fuel at all times. The MCFR will require technology development to reach commercialization. With a breed-and-burn in-situ reactor like MCFR, the transmutation of fertile U-238 to fissile Pu-239 allows for much greater fuel utilization.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Imaging and Analysis of Insoluble Electrorefiner Material

Throughout pyroprocessing efforts at the Hot Fuel Examination Facility (HFEF), insoluble material has accumulated in the Electrorefiner (ER) vessel. The objective of this effort was to analyze the accumulated material to determine its origin. Material was removed from the ER salt bath and distilled to remove excess salt prior to performing analysis. Three samples were sent for chemical and isotopic analysis and underwent an ethyl acetate-bromine dissolution to segregate the oxide fraction from the metal fraction. Actinide concentrations were determined using a quadrupole–inductively coupled plasma–mass spectrometer (Q-ICP-MS). Three additional samples were sent for morphologic and elemental analysis by scanning electron microscopy (SEM) with Energy Dispersive X-ray (EDX) analysis at the Irradiated Materials Characterization Laboratory (IMCL). Analyses suggest that the material is primarily composed of UO2. with a small fraction of metal. This study draws no single conclusion as to the origin of the insoluble material in the ER. The particle sizes and morphologies observed in SEM micrographs indicate that the larger particles observed may be a result of introducing material to the ER that has not been completely reduced in Oxide Reduction (OR) operations, which precede electrorefining. Smaller particles may be due to reactions with oxygen and moisture present in HFEF. This research suggests that microscopic analysis of fuel particles before and after OR operations (including after distillation) as well as the uranium product collected on the cathode in the ER would increase understanding about particle morphology within the pyrochemical process.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Effect of heat treatment on the microstructure of medium burn-up U-Mo monolithic fuel foils

Using scanning electron microscopy (SEM), this study evaluates the microstructure evolution of U-Mo fuel foils made with and without heat treatment at medium burn-up (of approximately 5 x 10 21 f/cm 3 ). The impact of annealing treatments on critical microstructural properties of the U-Mo fuel foils, including porosity, grain structure, Mo homogeneity, and fuel interaction with the Zr interlayer, was examined using large area lift outs (LALOs). The heat-treated specimens presented less grain refining at these burnups when compared to the un-heated specimens. Grain refinement was associated with porosities and fission products precipitation. Heat treatment can reduce fuel swelling during irradiation. Chemical inhomogeneity (Mo banding) was found to persist in the un-heated samples but was not present in the heat-treated samples. Thus, heat-treated U-Mo foils allows for more predictable fuel behavior under irradiation with respect to un-heated foils. The U-Mo and Zr interaction layer appears to be thicker and more continuous in the heat-treated sample which has been associated with stronger interface integrity during irradiation, as also observed in previous studies. These observations may indicate an overall improved performance of heat-treated fuel foil in a reactor. Further, the effect of local burn-up on grain size/refinement and porosities in each LALO specimen, sampled from different positions in the fuel foil, was difficult to analyze due to the large standard deviation of these parameters. Finally, evidence of grain refinement by polygonization may be present in these specimens.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Contributions to the mechanistic understanding of the microstructural evolution in irradiated U-Mo dispersion fuel

Here, advanced microstructural characterization techniques, such as scanning electron microscopy (SEM) and scanning transmission electron microscopy - energy dispersive x-ray spectroscopy (STEM-EDS), were used to interpret the fuel microstructure evolution and fission products behavior in U-Mo dispersion fuel irradiated in the Advanced Test Reactor (ATR) as part of the European Mini-Plate Irradiation Experiment (EMPIrE) test. The larger as-fabricated fuel grain size achieved by heat-treating the U-Mo powder resulted in slower high burnup structure (HBS) development and reduced fission gas porosity. Slower HBS kinetics was observed at the fuel kernels’ periphery, which contained smaller and less fission gas bubbles at all fission densities (FDs) investigated and was attributed to a locally reduced damage density and fission products concentration, as corroborated with Monte Carlo simulations. The non-refined grains at the fuel kernel periphery hosted a perfectly ordered fission Gas Bubble Superlattice (GBS) up to 6.3 × 10 21 fissions/cm 3 . Nano-scale STEM-EDS analysis presented in this study provided useful information on the GBS characteristic morphology and evolution in U-Mo fuel. The concentration of fission gas in the GBS progressively increased with FD, pointing to an evolution of the nanobubble pressure status with irradiation. A possible connection between the GBS collapse and HBS onset is proposed for which there exists a threshold in the misorientation of the refined sub-grains above which the GBS stability during irradiation is no longer preserved, resulting in the GBS collapse.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Annealing influence on the microstructure of irradiated U-Mo monolithic fuel foils

In this study we compared the microstructure evolution of U-Mo fuel foils produced with and without heat treatment at low burn-up via advanced post-irradiation examination. The aim of this study is to observe after irradiation the ways in which the fabrication processes have influenced fuel behavior at early-stage irradiation, as for very low burn up microstructural studies are lacking. In this work it was observed that the larger grain size detected in the heat-treated samples before irradiation led to decreased grain refinement after irradiation. Grain refinement was associated with the presence of small nano-size bubbles and precipitates. This phenomenon is hypothesized to influence early fuel swelling during reactor irradiation. Grain refinement was also observed to increase in regions where γ-U decomposition was present. Thus, it was enhanced in the samples fabricated without heat treatment. The heat treatment also increased the thickness of the U-Mo/Zr interface, namely of the UZr 2 layer. However, the influence of this layer on fuel performance needs further investigation. On one side, it may contribute to better mechanical bonding; on the other, it may influence swelling and blistering in the interaction layer as porosity increases when this layer is increased. This was observed especially in the presence of increased area containing low Mo concentration, and thus containing a higher fraction of the α-U phase, which is highly susceptible to irradiation induced swelling. Strong evidence of reverse transformation under irradiation (α-U + γ'-U2Mo → bcc γ-U) was observed in these samples. While the precipitates (carbides and oxide) seem to be unaffected by the irradiation at these low burnups. However, further analyses are necessary at higher burn-up to assess the exact impact different heat treatments have on fuel performance.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

An investigation of the failure modes in U-10Mo monolithic fuel irradiated to high burnup

Here, this study investigated possible failure mode sequences in U-10Mo monolithic fuel irradiated to very-high-burnup. The U-Mo fuel plate used in this study was characterized using scanning electron microscopy (SEM), wavelength dispersive spectroscopy (WDS), and image analysis techniques to investigate how microstructural features may initiate crack formation and propagation through the microstructure, potentially leading to blistering. Distinctly large fission gas pores (FGPs) were observed to preferentially align 5-15µm away from the U-10Mo/Zr interface, parallel to the Zr diffusion barrier. Preferential growth, alignment, and interconnection of FGP could initiate blistering in the fuel plate by creating a fission gas channel, parallel to the U-Mo/Zr interface. FGP alignment in the fuel phase near the U-Mo/Zr interface is believed to be one of the precursors to crack and Type 2 blister formation in monolithic U-Mo fuels. The chemical maps revealed differences in fission product behavior near the U-Mo/Zr interface such that Nd remains in the fuel matrix at the FGP sites. On the other hand, other fission products like Xe and Cs can get trapped in FGPs by Nd in the fuel phase and/or diffuse toward the Zr diffusion barrier.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Engineering & Microstructure Scale PIE Report on EBR-II X441A Metallic Fuel Pins for the MORPH Experiment

The objectives of this project are to increase fundamental understanding of irradiation induced metallic U-Pu-Zr fuel behavior and to obtain data needed for the development of irradiation models for metallic fuels in MARMOT. The requested metallic fuel pins are from the X441A experiment irradiated in Experimental Breeder Reactor (EBR)-II and will be provided by the PIs for the duration of the experiment. The purpose of the pins irradiated in the X441A assembly was to vary Zr composition and fuel slug diameter in order to provide data for the metallic fuel performance code “LIFEMETAL” [ANL-IFR-125]. The fuels of interest to this project are metallic fuels with several Zr compositions (in wt.%): U-19Pu-6Zr, U-19Pu-10Zr, and U-19Pu-14Zr, which were irradiated to a peak burnup of approximately 11 at.%. The cladding was the same for all three fuel pins (austenitic stainless steel D9), which allows investigation of fuel-cladding interaction (FCI) phenomena. Varying Zr content in fuel pins enables investigation of the effect of Zr on fuel restructuring and fuel-cladding compatibility. Engineering and microstructure scale PIE activities will be focused on investigation of fundamental aspect of fuel performance such as species diffusion and migration, fission product behavior, and constituent redistribution. Obtained microstructural information will be used as the basis for the development of MARMOT models of U-Pu-Zr fuel performance at the mesoscale. Experimental data obtained through this proposal will be used to provide this fundamental understanding which will serve as the foundation of the development of radiation models for U-Pu-Zr in MARMOT. It will also provide a starting point for the design of new experiments to provide data for the validation of these MARMOT models.