5 records

DOE OSTI2022

Quasi-static and dynamic response of a Cu/Nb composite following equal channel angular extrusion

The article presents a study of the plastic properties of a Cu–18%Nb composite following equal channel angular extrusion under both low- and high-strain rate loadings. The microstructures are characterized by optical and scanning electron microscopy as well as electron backscatter diffraction. Comparisons are also made with a Cu–50%Nb laminate made by accumulative roll bonding. Textures obtained within the respective phases in the extruded composite closely mimic those previously reported for the pure components alone (Cu, Nb). Grain sizes of the major phase (Cu) exhibit broad distributions, due largely to partial recrystallization during the extrusion process. Further re-crystallization is obtained within localized deformation bands produced at high strain rates (3 × 10 3 s –1 ). While the degree of anisotropy and the strain rate sensitivity of the composite response are similar to those of pure Cu after extrusion, the strength levels of the composite are somewhat greater, falling broadly between those obtained in the pure components after extrusion to comparable plastic strains. Furthermore, the implications for selection of composite composition and processing for achieving higher strengths are briefly discussed.

36 MATERIALS SCIENCE↗

DOE OSTI2017

Structure/property (constitutive and spallation response) of additively manufactured 316L stainless steel

For additive manufacturing (AM) of metallic materials, the certification and qualification paradigm needs to evolve as there is currently no broadly accepted “ASTM- or DIN-type” additive manufacturing certification process or AM-produced material specifications. Accordingly, design, manufacture, and subsequent implementation and insertion of AM materials to meet engineering applications requires detailed quantification of the constitutive (strength and damage) properties of these evolving materials, across the spectrum of metallic AM methods, in comparison/contrast to conventionally-manufactured metals and alloys. For this paper, cylindrical samples of 316L SS were produced using a LENS MR-7 laser additive manufacturing system from Optomec (Albuquerque, NM) equipped with a 1 kW Yb-fiber laser. The microstructure of the AM-316L SS was characterized in both the “as-built” AM state and following a heat-treatment designed to obtain full recrystallization to facilitate comparison with annealed wrought 316L SS. The constitutive behavior as a function of strain rate and temperature was characterized and is compared to that of annealed wrought 316L SS plate material. The dynamic shock-loading-induced damage evolution and failure response of all three 316L SS materials was quantified using flyer-plate impact driven spallation experiments at peak stresses of 4.7 and 6.5 GPa. The spall strength of AM-produced 316L SS and the recrystallized-AM-316L SS were found to decrease with increasing peak shock stress while the annealed wrought 316L SS spall strength remained essentially constant. Finally, the damage evolution, characterized using optical metallography and electron-backscatter diffraction (EBSD), was found to vary significantly across the three 316L SS microstructures while the three samples loaded to a peak shock stress of 6.5 GPa displayed only ~12% differences in spall strength.

316L SS↗

DOE OSTI2017

Constitutive modeling of the dynamic-tensile-extrusion test of PTFE

Use of polymers in defense, aerospace and industrial applications under extreme loading conditions makes prediction of the behavior of these materials very important. Crucial to this is knowledge of the physical damage response in association with phase transformations during loading and the ability to predict this via multi-phase simulation accounting for thermodynamical non-equilibrium and strain rate sensitivity. The current work analyzes Dynamic-Tensile-Extrusion (Dyn-Ten-Ext) experiments on polytetrafluoroethylene (PTFE). In particular, the phase transition during loading and subsequent tension are analyzed using a two-phase rate sensitive material model implemented in the CTH hydrocode. The calculations are compared with experimental high-speed photography. Deformation patterns and their link with changing loading modes are analyzed numerically and correlated to the test observations. It is concluded that the phase transformation is not as critical to the response of PTFE under Dyn-Ten-Ext loading as it is during the Taylor rod impact testing.

36 MATERIALS SCIENCE↗

DOE OSTI2016

Characterization and modeling of mechanical behavior of single crystal titanium deformed by split-Hopkinson pressure bar

Single crystal titanium samples were dynamically loaded using split-Hopkinson pressure bar (SHPB) and the resulting microstructures were examined. Characterization of the twins and dislocations present in the microstructure was conducted to understand the pathway for observed mechanical behavior. Electron backscatter diffraction (EBSD) was used to measure textures and quantify twinning. Microstructures were profusely twinned after loading, and twin variants and corresponding textures were different as a function of initial orientation. Focused ion beam (FIB) foils were created to analyze dislocation content using transmission electron microscopy (TEM). Large amounts of dislocations were present, indicating that plasticity was achieved through slip and twinning together. Viscoplastic self-consistent (VPSC) modeling was used to confirm the complex order of operations during deformation. The activation of different mechanisms was highly dependent upon crystal orientation. For [0001] and View the MathML source[101¯1]-oriented crystals, compressive twinning was observed, followed by secondary tensile twinning. Furthermore, dislocations though prevalent in the microstructure, contributed to final texture far less than twinning.

36 MATERIALS SCIENCE↗

DOE OSTI2015

Dynamic failure in two-phase materials

Previous experimental research has shown that microstructural features such as interfaces, inclusions, vacancies, and heterogeneities can all act as voidnucleation sites. However, it is not well understood how important these interfaces are to damage evolution and failure as a function of the surrounding parentmaterials. In this work, we present results on three different polycrystallinematerials: (1) Cu, (2) Cu-24 wt. %Ag, and (3) Cu-15 wt. %Nb which were studied to probe the influence of bi-metal interfaces onvoidnucleation and growth. These materials were chosen due to the range of difference in structure and bulk properties between the two phases. The initial results suggest that when there are significant differences between the bulk properties (for example: stacking fault energy, melting temperature, etc.) the type of interface between the two parent materials does not principally control the damage nucleation and growth process. Rather, it is the “weaker” material that dictates the dynamic spall strength of the overall two-phase material.

36 MATERIALS SCIENCE↗