Characterization of 3C-SiC Films Grown on 4H- and 6H-SiC Substrate Mesas During Step-Free Surface Heteroepitaxy

This paper reports detailed structural characterization of 3C-SiC heteroepitaxial films grown on 4H- and 6H-SiC mesa surfaces. 3C-SiC heterofilms grown by the "step-free surface heteroepitaxy" process, free of double-positioning boundary (DPB) and stacking-fault (SF) defects, were compared to less-optimized 3C-SiC heterofilms using High Resolution X-ray Diffraction (HRXRD), High Resolution Cross-sectional Transmission Electron Microscopy (HRXTEM), molten potassium hydroxide (KOH) etching, and dry thermal oxidation. The results suggest that step free surface heteroepitaxy enables remarkably benign partial lattice mismatch strain relief during heterofilm growth.

Neudeck, Philip G.↗

NASA NTRS2002

Growth of Defect-Free 3C-Sic on 4H- and 6H-SIC Mesas Using Step-Free Surface Heteroepitaxy

A new growth process, herein named step-free surface heteroepitaxy, has achieved 3C-SiC films completely free of double positioning boundaries and stacking faults on 4H-SiC and 6H-SiC substrate mesas. The process is based upon the initial 2-dimensional nucleation and lateral expansion of a single island of 3C-SiC on a 4H- or 6H-SiC mesa surface that is completely free of bilayer surface steps. Our experimental results indicate that substrate-epilayer in-plane lattice mismatch (Delta/a = 0.0854% for 3C/4H) is at least partially relieved parallel to the interface in the initial bilayers of the heterofilm, producing an at least partially relaxed 3C-SiC film without dislocations that undesirably thread through the thickness of the epilayer. This result should enable realization of improved 3C-SiC devices.

Neudeck, Philip G.↗

NASA NTRS2001

Growth of Defect-Free 3C-SiC on 4H- and 6H-SiC Mesas Using Step-Free Surface Heteroepitaxy

A new growth process, herein named step-free surface heteroepitaxy, has achieved 3CSiC films completely free of double positioning boundaries and stacking faults on 4H-SiC and 6H-SiC substrate mesas. The process is based upon the initial 2-dimensional nucleation and lateral expansion of a single island of 3C-SiC on a 4H- or 6H-SiC mesa surface that is completely free of bilayer surface steps. Our experimental results indicate that substrate-epilayer in-plane lattice mismatch (delta a/a = 0.0854% for 3C/4H) is at least partially relieved parallel to the interface in the initial bilayers of the heterofilm, producing an at least partially relaxed 3C-SiC film without dislocations that undesirably thread through the thickness of the epilayer. This result should enable realization of improved 3C-SiC devices.