DOE OSTI2023

High-Energy X-ray Diffraction Microscopy for Nuclear Forensics (FY23 Project Report)

36 MATERIALS SCIENCE↗

DOE OSTI2023

Transition Metal Dissolution in Lithium-Ion Cells: A Piece of the Puzzle

Static leaching tests were performed using the chemically delithiated positive electrode materials, LiFePO 4 , LiCoO 2 , LiMn 2 O 4 , LiNiO 2 , and LiNi 0.8 Mn 0.1 Co 0.1 O 2 . Instead of the common electrolyte, which contains LiPF 6 , the solvent consisted of only ethylene carbonate (EC) and ethyl methyl carbonate (EMC), limiting the possible reactions to only those that depend on the solvent. The product liquids from these experiments showed that there were lithium-bearing species in common, such as Li(EC) + and Li(EMC) + . Interestingly, we found evidence of electrolyte degradation products in both the positive-and negative-ion mass spectral results. The positive-ion results showed that the products tended to coordinate to lithium. In conclusion, the negative-ion results showed that most of the products tended to complex with transition metals. It was difficult to discern which positive ion was associated with which negative ion.

25 ENERGY STORAGE↗

DOE OSTI2022

Exploring the Promise of Multifunctional “Zintl-Phase-Forming” Electrolytes for Si-Based Full Cells

Li-M-Si ternary Zintl phases have gained attention recently due to their high structural stability, which can improve the cycling stability compared to a bulk Si electrode. Adding multivalent cation salts (such as Mg 2+ and Ca 2+ ) in the electrolyte was proven to be a simple way to form Li-M-Si ternary phases in situ in Si-based Li-ion cells. To explore the promise of Zintl-phaseforming electrolytes, we systematically investigated their application in pouch cells via electrochemical and multiscale postmortem analysis. The introduction of multivalent cations, such as Mg 2+ , during charging can form Li x M y Si ternary phases. They can stabilize Si anions and reduce side reactions with electrolyte, improving the bulk stability. More importantly, Mg 2+ and Ca 2+ incorporate into interfacial side reactions and generate inorganic-rich solid- electrolyte interphase, thus enhancing the interfacial stability. Therefore, the full cells with Zintl-phase-forming electrolytes achieve higher capacity retentions at the C/3 rate after 100 cycles, compared to a baseline electrolyte. Additionally, strategies for mitigating the electrode-level fractures of Si were evaluated to make the best use of Zintl-phase-forming electrolytes. In conclusion, this work highlights the significance of synergistic impact of multifunctional additives to stabilize both bulk and interface chemistry in high-energy Si anode materials for Li-ion batteries.

25 ENERGY STORAGE↗

DOE OSTI2022

Extreme Fast Charging: Effect of Positive Electrode Material on Crosstalk

Extreme fast charging (XFC) is a key requirement for the adoption of battery-based electric vehicles by the transportation sector. However, XFC has been shown to accelerate degradation, causing the capacity, life, and safety of batteries to deteriorate. We tested cells containing five positive electrode chemistries, LFP (olivine structure), LMO (spinel), LCO (layered), NMC811 (layered) and NCA (layered), using fast-charging protocols. After testing, the negative electrodes from cells containing positive electrodes crystallizing with a layered structure were found to have more lithium deposited on their surfaces. Further, those crystallizing with a layered structure also tended to have a larger increase in impedance than those crystallizing with a spinel or olivine structure. Characterization of the negative electrodes by X-ray photoelectron spectroscopy showed that using the concentrations of LiF and Li x PO y F z as metrics, the concentration of LiF in the SEI from the cell with different positive electrodes is LFP > LMO > LCO ~ NMC811 > NCA; and for Li x PO y F z , the order is LMO > LFP > NCA > NMC811 > LCO. Clearly, the positive-electrode material was influencing the amounts of these materials formed.

25 ENERGY STORAGE↗

DOE OSTI2022

Radiochronometric analysis of an historic Cs-137 activity standard

In this work, a 137 Cs activity standard discovered during routine inventory was analyzed to determine its model age using radiochronometry. The aqueous activity standard was separated using an established separation method that employs commercially available Sr resin. The method was also tested against a nuclear forensics reference material developed specifically for benchmarking 137 Cs radiochronometry methods. Results of the analyses showed good agreement between the results and the certified values of the reference material. Analysis of the discovered activity standard were also in good agreement with the activity certification date, though uncertainty was higher due to natural Ba contaminating the sample and the stable 133 Cs used as a carrier during the standard’s production.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗

DOE OSTI2022

High-Energy X-ray Diffraction Microscopy for Nuclear Forensics FY2022 Project Report

Morphological information on nuclear material has been identified using visible light and scanning electron microscopy. These identify qualitative differences in particle morphology. Three-dimensional imaging of materials through alternating scanning electron microscopy imaging and focused ion beam milling has also been used. Unfortunately, these techniques are time- and labor-intensive, with significant sample preparation required and lengthy analysis times. Further, the resulting 3D images are qualitative, require manual identification, and do not capture statistically-representative populations. High energy X-ray 3D imaging using a direct-beam or diffracted-beam (High-Energy Diffraction Microscopy) have been developed at the Advanced Photon Source and can produce quantitative information on grains (phase, location, etc.) and pores (size distribution, sphericity) in a material. These techniques require only minutes to characterize a sample volume and are non-destructive, thus suitable for a wide range of existing samples and for confirmatory analyses to be carried out using conventional microscopy techniques. In this first year of the project, all uranium oxide samples were synthesized and characterized using conventional analyses by the analytical chemistry laboratory. Conventional analysis methods included powder x-ray diffraction, scanning electron microscopy, impurity analysis via inductively coupled plasma mass spectrometry, and infrared spectroscopy. Impurity analysis shows a drop in boron content from UO 3 to the lowest U 3 O 8 calcination temperature, but otherwise no appreciable difference in any sample. Analysis of diffraction data shows a flip of peaks from UO 3 dominated for the 600 °C calcined sample to U 3 O 8 dominated at 700 °C and 800 °C. Analysis of scanning electron microscopy images shows that with increased calcination temperature the size distribution of particles seems to increase and broaden. Both of these last findings are in line with previously published data, though this work used significantly fewer particles to simply show similar trends instead of getting truly quantitative particle analysis. Infrared analysis similarly shows ingrowth of U 3 O 8 as calcination temperature is increased, along with depression of peaks associated with UO 3 and water. Samples were prepared for analysis at the Advanced Photon Source at beamline 1-ID. It is anticipated that analysis will occur in November of 2022. AI/ML techniques to de-noise data coming out of 1-ID during the analyses was also developed during this time using previously gathered data. Preliminary results using a self-supervision technique called Noise2Selfshow good de-noising of data. Once the uranium oxide samples are analyzed, real data will be used to test the de-noising and other AI/ML techniques that may be developed in the second year of the project.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Across-Depth Heterogeneity and Irreversibility of Fast-Charge-Driven Lithium Plating

Enabling fast charging in lithium-ion batteries (LIBs) is a key factor for resolving consumers’ “range anxiety” concerns in choosing an electric vehicle over a gasoline-powered one. The best-known issue in the fast charging of current LIBs (based on LiNi x Mn y Co 1–x–y O 2 /graphite) is lithium plating, which is barely reversible and is accompanied by capacity loss over time. Therefore, understanding the reasons for the irreversibility of lithium plating driven by fast charging is critical to enhancing the fast-charging capability of LIBs. Here, a study of the irreversibility and heterogeneity of lithium plating is carried out by using electrochemical analyses, inductively coupled plasma mass spectroscopy, and X-ray photoelectron spectroscopy. Further, the study shows that the majority of the lithium plated during fast charging remains inactive even with very slow discharging rates, implying that most of the plated lithium is irreversibly lost. The study also reveals that chemical compounds such as LiF, Li 2 O and Li 2 (CO 3 ) are formed heterogeneously within the lithium plating and are responsible for some of the irreversibility of the plated lithium.

33 ADVANCED PROPULSION SYSTEMS↗

DOE OSTI2022

A Comprehensive Understanding of the Aging Effects of Extreme Fast Charging on High Ni NMC Cathode

As the battery industry shifts toward high Ni content cathodes, such as LiNi 0.8 Mn 0.1 Co 0.1 O 2 [NMC811], a complete understanding of the degradation mechanisms of NMC811 under extreme fast charging (XFC) (XFC, ≤10–15 min charging) conditions is needed. Such comprehensive understanding would identify the most critical materials gaps that need to be addressed for enabling XFC long-life cells for electric vehicles. This study maps out the key aging mechanisms for NMC811 cycled at different XFC conditions (between 1C and 9C) for up to 1000 cycles. To acquire a fundamental understanding of utilization and degradation, cells are evaluated using a range of electrochemical techniques, and multimodal and multiscale microscopy techniques to quantify chemical, structural, and crystallographic degradation as a function of cycling conditions for the NMC cathode. When comparing NMC811 to NMC532, it is observed that NMC811 has a greater subsurface crystallographic degradation and displays a similar magnitude of subparticle cracking. However, the NMC811 maintains superior performance despite those advanced degradations. Here, the superior cycle life performance is attributed to the NMC811 particles having radially oriented grains and improved transport properties. NMC811 shows between 4.6× and 3.15× reduction in capacity fade than NMC532 for charging rates between 4C (e.g., 15-min charging) and 6C (10-min charging).

25 ENERGY STORAGE↗

DOE OSTI2022

Age determination of a 75 Se gamma radiography source for nuclear forensics

Here, two methods were used to evaluate the age of 75 Se sealed source material. Both methods utilized gamma spectroscopy to determine the quantity of parent 75 Se present, but they differed in the technique used to determine the quantity of daughter 75 As. In one method, 75 As was quantified using inductively coupled plasma-mass spectrometry (ICP-MS) after using chromatographic techniques to separate the parent and daughter isotopes. In the other method, total As was measured using optical emission spectroscopy (OES), which did not require separation prior to measurement. The OES method was faster and gave slightly lower uncertainties, but required more daughter material to be present because of higher concentration requirements, making it unsuitable for young material. Both methods are hampered by the monoisotopic nature of As, but still gave reasonable model ages that were in agreement with each other.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗