ZrF4-BaF2-LaF3-AIF3-NaF (ZBLAN) optical fiber was flown on board the NASA's KC-135 microgravity aircraft to determine the effects of microgravity on crystal growth in this material. Fiber samples were placed in evacuated quartz ampoules and heated to the crystallization temperature in 0g, 1g, and 2g. The 1g and 2g samples were observed to slump and crystallize. The 0g samples showed no evidence of crystallization.
Glass-fiber-drawing apparatus designed for studies of effect of gravitation on drawing process. Clear plastic housing surrounds fiber-drawing equipment and some of associated electronic instrumentation. External rack holds video monitor, personal computer, keyboard, videotape recorder, and power switch panel. Mounted in research aircraft, apparatus makes continuous video recordings of formation of fiber at effective gravitational accelerations ranging from 0.001 to 2 times normal Earth gravitational acceleration as aircraft dives, then pulls out of dives. Also records pertinent process data on video image.
The effects of a 5.8-y exposure to low-earth-orbit environment upon the mechanical properties of five commercial glasses and a low-expansion-coefficient glass-ceramic have been examined. The radiation components of the earth-orbit environment did not degrade the mechanical strength of the samples examined within the limits of experimental error. Statistical problems arising from the low frequency of micrometeorite or space debris impacts upon the samples precluded statistically valid measurement of impacted sample strengths. Upper bounds for the magnitude of the impact event damage upon the strengths for impacted samples have been determined.
The effects of a 5.8 year exposure to low earth orbit environment upon the mechanical properties of commercial optical fused silica, low iron soda-lime-silica, Pyrex 7740, Vycor 7913, BK-7, and the glass ceramic Zerodur were examined. Mechanical testing employed the ASTM-F-394 piston on 3-ball method in a liquid nitrogen environment. Samples were exposed on the Long Duration Exposure Facility (LDEF) in two locations. Impacts were observed on all specimens except Vycor. Weibull analysis as well as a standard statistical evaluation were conducted. The Weibull analysis revealed no differences between control samples and the two exposed samples. We thus concluded that radiation components of the Earth orbital environment did not degrade the mechanical strength of the samples examined within the limits of experimental error. The upper bound of strength degradation for meteorite impacted samples based upon statistical analysis and observation was 50 percent.
Disclosed here is a process for making mullite fibers wherein a hydrolizable silicon compound and an aluminum compound in the form of a difunctional aluminum chelate are hydrolized to form sols using water and an alcohol with a catalytic amount of hydrochloric acid. The sols are mixed in a molar ratio of aluminum to silicon of 3 to 1 and, under polycondensation conditions, a fibrous gel is formed. From this gel the mullite fibers can be produced.
The effects of solar radiation of selected glasses are reported. Optical property degradation is studied using UV-Vis spectrophotometry. Strength changes are measured using a concentric ring bend test. Direct fracture toughness measurements using an indentation test are planned.
Proposed process makes continuous mullite fibers retaining structural integrity at temperatures up to and somewhat beyond 1,300 degrees C. Process makes highly pure mullite fibers, without melting and without dangerous solvent.
An experimental design matrix was constructed to determine the effects of time and temperature water soak on the strength of Zerodur glass-ceramic. It was found that strength does increase in a nonlinear manner which is consistent with existing theories of crack tip blunting and residual stress reduction.
The processing parameters and mechanical properties of glass fibers pulled from simulated lunar basalt are tested. The simulant was prepared using a plasma technique. The composition is representative of a low titanium mare basalt (Apollo sample 10084). Lunar gravity experiments are to be performed utilizing parabolic aircraft free-fall maneuvers which yield 30 seconds of 1/6-g per maneuver.
The development of a continuous ceramic fiber which could be used in rocket engine and rocket boosters applications was investigated at the Marshall Space Flight Center. Methods of ceramic fiber production such as melt spinning, chemical vapor deposition, and precursor polymeric fiber decomposition are discussed and compared with sol-gel processing. The production of ceramics via the sol-gel method consists of two steps, hydrolysis and polycondensation, to form the preceramic, followed by consolidation into the glass or ceramic structure. The advantages of the sol-gel method include better homogeneity and purity, lower preparation temperature, and the ability to form unique compositions. The disadvantages are the high cost of raw materials, large shrinkage during drying and firing which can lead to cracks, and long processing times. Preparation procedures for aluminosilicate sol-gel and for continuous mullite fibers are described.
A dynamic fatigue study was performed on a Li2O-Al2O3-SiO2 glass-ceramic in order to assess its susceptibility to delayed failure. Fracture mechanics techniques were used to analyze the results for the purpose of making lifetime predictions for optical elements made from this material. The material has reasonably good resistance (N = 20) to stress corrosion in ambient conditions. Analysis also indicated the elements should survive applied stresses incurred during grinding and polishing operations.
Report discusses mechanical tests measuring parameters of strength and fracture mechanics of optical glasses. To obtain required tables of mechanical properties of each glass of interest, both initial-strength and delayed-fracture techniques used. Modulus of rupture measured by well-known four-point bending method. Initial bending strength measured by lesser-known double-ring method, in which disk of glass supported on one face near edge by larger ring and pressed on its other face by smaller concentric ring. Method maximizes stress near center, making it more likely specimen fractures there, and thereby suppresses edge effects. Data from tests used to predict reliabilities and lifetimes of glass optical components of several proposed spaceborne instruments.
The inherent brittleness of glass invariably leads to a large variability in strength data and a time dependence in strength. Leading rate plays a large role in strength values. Glass is found to be weaker when supporting loads over long periods of time as compared to glass which undergoes rapid leading. These properties complicate the structural design allowables for the utilization of glass components in an application such as Advanced X-ray Astrophysics Facility (AXAF). The test methodology to obtain parameters which can be used to predict the reliability and life time of Zerodur glass-ceramic which is to be used for the mirrors in the AXAF is described.
The inherent brittleness of glass invariably leads to a large variability in strength data and a time dependence in strength (i.e., static fatigue). Loading rate plays a large role in strength values. Glass is found to be weaker when supporting loads over long periods as compared to glass which undergoes rapid loading. In this instance the purpose of rapid loading is to fail the glass before any significant crack growth occurs. However, a decrease in strength occurs with a decrease in loading rate, pursuant to substantial crack extension. These properties complicate the structural design allowable for the utilization of glass components in applications such as mirrors for the Space Telescope and AXAF for Spacelab and the space station.