NASA NTRS1980

Driver for solar cell I-V characteristic plots

A bipolar voltage ramp generator which applies a linear voltage through a resistor to a solar cell for plotting its current versus voltage (I-V) characteristic between short circuit and open circuit conditions is disclosed. The generator has automatic stops at the end points. The resistor serves the multiple purpose of providing a current sensing resistor, setting the full-scale current value, and providing a load line with a slope approximately equal to one, such that it will pass through the origin and the approximate center of the I-V curve with about equal distance from that center to each of the end points.

Turner, G. B.↗

NASA NTRS1979

Structure of deformed silicon and implications for low-cost solar cells

The paper reports on an investigation of the microstructure and minority carrier lifetime of silicon in uniaxially compressed silicon samples, the objective of which was to determine if it is feasible to produce silicon solar cells from sheet formed by high temperature deformation. It is reported that recrystallization was found to be incomplete in both fine and large grained materials, and that the major mode of recrystallization appears to be migration of existing boundaries into the deformed regions. Also, minority carrier diffusion length was found to be drastically reduced after deformation, perhaps due to contamination or cooling rate, and recovered only slightly with annealing. It is concluded that these results suggest that high temperature deformation of silicon for direct production of sheet for high efficiency solar cells is not practical. It is noted that potential may exist for its use as a coarse grained substrate.

Mardesich, N.↗

NASA NTRS1978

Structure of deformed silicon and implications for low cost solar cells

The microstructure and minority carrier lifetime of silicon were investigated in uniaxially compressed silicon samples. The objective of the investigation was to determine if it is feasible to produce silicon solar cells from sheet formed by high temperature rolling. The initial structure of the silicon samples ranged from single crystal to fine-grained polycrystals. The samples had been deformed at strain rates of 0.1 to 8.5/sec and temperatures of 1270-1380 C with subsequent annealing at 1270-1380 C. The results suggest that high temperature rolling of silicon to produce sheet for cells of high efficiency is not practical.

Mardesich, N.↗

NASA NTRS1978

Mechanisms of photon-induced changes in silicon solar cell parameters

Reversible changes in solar cell performance were induced by AM1 illumination and evaluated by measuring short-circuit current, weak light spectral response, and minority carrier diffusion length. In n(+)p cells the change manifests itself as a reduced short-circuit current, a loss of the red response, and a reduction in minority carrier diffusion length. In p(+)n cells there are two-photon induced effects: (1) enhancement of the blue spectral response, presumably occurring in the p(+) layer and (2) degradation in open-circuit voltage at low light levels due to increased leakage occurring only after the junction edge is exposed to bright light. Most of these photon effects are attributed to defects in the silicon.

Cheng, L. J.↗