Low-Cost, High Performance Catalyst Coated Membranes for PEM Water Electrolyzers (Final Technical Report)
In this project, the objective was to develop reduced-cost manufacturing techniques capable of producing proton exchange membrane water electrolyzer (PEMWE) catalyst coated membranes (CCMs) with further improved performance relative to then-current 3M CCM technology. Processes to be developed would enable 1) production of 0.5 m wide CCMs (approximately 2x wider than produced by the current laboratory/pilot-scale processes) and 2) 3x higher net-effective linear rates (lineal-meters of CCM produced per cumulative process time) than the baseline CCM process. In combination, the wider width CCM and increased net-effective linear rates would result in a 6-fold decrease in CCM manufacturing cost (defined as cumulative machine and labor time) per m 2 of CCM produced. PEMWE CCMs produced with these optimized processes were targeted to produce 1) 0.25 A/cm 2 or greater at 1.5 V, 2) 2.0 A/cm 2 or greater at 1.75 V and 3) 4 A/cm 2 or greater at 1.95V, 4) with total catalyst platinum-group metal (PGM) loadings of ≤ 0.50 mg/cm 2 , measured in a cell with 50 cm 2 active area (or larger) at 80°C cell temperature and ambient outlet pressures.