DOE OSTI2024

A comparative analysis of residual stresses from friction stir processing of aluminum cast 380 and wrought 7075 alloy sheets: experimental characterization and modeling

Residual stresses are often overlooked in friction stir processing (FSP), but their significant impact on fatigue performance necessitates their consideration in optimizing processing parameters. The first step in this effort is understanding how process conditions influence residual stress distributions, especially across different alloys. This study focuses on determining and explaining the through-thickness residual stress variations and the effect of process temperature on the residual stress magnitude in wrought AA7075 and cast AA380.0 alloys. Additionally, for AA380.0, the impact of a second FSP pass was investigated. To achieve this, hole-drilling electronic speckle pattern interferometry (ESPI) and the thermal pseudo-mechanical (TPM) model within finite element analysis were employed to study the 3D distributions of in-plane residual stresses in processed samples under various conditions. A key finding was the varying impact of process temperatures on residual stress magnitudes. Higher process temperatures reduced stresses in AA380.0 but increased them in AA7075. Additionally, the through-thickness stress distributions differed between the two alloys. Further analysis revealed that yield stresses are crucial in explaining these phenomena and the effects of additional FSP passes. Further, this fundamental understanding will be vital in guiding the efforts to mitigate residual stresses and assess their impact on the performance of FSP aluminum alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Impact of Backing Plate and Thermal Boundary Conditions for High-Speed Friction Stir Welding of 25-mm Thick Aluminum Alloy 7175-T79

Here this study demonstrates high-speed (150 mm/min) single pass friction stir butt joining of 25 mm thick aluminum alloy 7175-T79. To understand the impact of quenching and cooling rate on process responses, joint strength, and grain size distributions across the weld thickness, we performed a series of friction stir welding (FSW) trials in air and with a trailing water spray using steel and composite backing plates (BP). Welds made in air and trailing water spray exhibit significantly different hardness distributions across the nugget, heat affected zone (HAZ), and HAZ minimum hardness as evidenced by detailed microhardness mapping. The effect of trailing water spray (TWS) on joint efficiency overshadows the influence of BP composition due to the vastly different contribution to quenching. TWS also resulted in a multifaceted effect on FSW such as lowering processing temperature, increasing X and Z forces while lowering Y force, and narrow heat affecting zone. Finally, digital image correlation (DIC)-based fracture mode analysis and grain size measurements correlate with the hardness distribution.

42 ENGINEERING↗

DOE OSTI2023

Phase Field Modeling of Corrosion for Design of Next-Generation Magnesium-Aluminum Vehicle Joints

In this study, WPI and its partners sought to understand galvanic corrosion in Mg-Al friction stir weld (FSW) joints. Unlike fusion welds, FSW is done in the solid state. This limits (but does not eliminate) the formation of brittle Al-Mg intermetallics, resulting in better joint strength and corrosion resistance. This study aimed to understand corrosion behavior of Mg-Al FSW joints by using a Cahn-Hilliard phase field electrochemistry model based on the work of Pongsaksawad et al. Its context challenge problem was an ultra-light door designed by Magna with 6061-Al sheet outer and ZEK100-Mg sheet inner panels, joined by an adhesive and FSW. Unlike most FSW joints, which weld through the softer material into the harder one, the Al sheet’s hem joint around Mg required the FSW tool to through the harder Al into the softer Mg, which was itself a challenge. Despite this challenge, PNNL succeeded in consistently making very strong FSW lap joints, by using a triflute tool and power control. Characterization showed mostly separate Al and Mg regions in the weld, usually with a hook protruding from Al into Mg, which likely contributed to high joint strength. Nanohardness mapping showed higher hardness in thin Mg swirls into the Al nugget, likely due to the intermetallics. The study used the industry standard SAE J2334 Cyclic Corrosion Test (CCT) to simulate corrosion conditions over the life of a vehicle, as well as linear polarization testing and ASTM G71 pitting corrosion testing. Corrosion reactions were: H 2 O + ½O 2 + 2e - → 2OH - at the Al cathode, and either Mg → Mg 2+ + 2e - or Mg + 2OH - → Mg(OH) 2 + 2e - at the Mg anode, with electron transfer through the joint. Mass loss increased with Al section length, supporting the hypothesis that galvanic corrosion in Al-Mg joints is limited by the cathodic reaction. Both pitting corrosion (first anode reaction) and hydroxide film formation (second reaction) were observed. The J2334 CCT test method was slightly modified, adding a chromium solution cleaning step after each week of corrosion testing, in order to remove Mg oxides and hydroxides and accurately measure mass loss over time. That said, FSW joints treated in this way did not did not exhibit significant reduction in lap shear strength of the joints vs. newly welded samples which had not undergone corrosion. Corrosion appeared to consist mainly of pitting in Mg in a way which did not directly affect the bond between the materials where the joints failed. A Cahn-Hilliard phase field model coupled with electrical potential described the electronically mediated galvanic corrosion electrochemical reactions described above in the four-component Al-Mg-H 2 O-(H 2 O+½O 2 ) system. This 2-D model successfully predicted Mg(OH)₂ formation at the anode in some circumstances, and Mg pitting corrosion in others, and showed the correct electric field directions in both cases. The model predicted Mg pit corrosion depth within a factor of two of measured pits.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗

DOE OSTI2023

Microstructure and texture evolution of friction stir lap welded dissimilar multi-aluminum stack

Here this work investigates the microstructural evolution of a dissimilar multiple-aluminum alloy stack (AA7055, AA7055, AA6022) produced by friction stir lap welding (FSLW). A through-thickness analyses of grain orientation map, grain size and distribution, strain distribution, and texture evolution by electron backscattered diffraction-based characterization technique were performed. Two different welding parameters (combination of tool rotation and traverse speed) were used to study the effects of the welding parameters on these microstructural characteristics. The study shows that higher welding speed and higher rotation speed of the FSLW tool yield finer grains. FSLW resulted in shear texture formation in the weld regions due to high welding speeds. This texture development in the nugget zone is consistent with shear deformation, and (111) pole figures show ideal shear texture components. The Stir Zone (SZ) exhibits shear texture (A/A ̅ and B/B ̅ components), consistent with other shear-assisted processes. Recrystallization mechanisms observed are CDRX in SZ and DDRX in TMAZ (Thermo-Mechanically Affected Zone). Interface analysis reveals the presence of oxide layers between different aluminum sheets, affecting joint mechanical performance. The mechanical property of the lap welded joints was presented in terms of microhardness distribution across the weld cross section. Slightly higher hardness in higher speed welding setup was observed throughout the SZ and AA6022 layer, indicating greater grain refinement and uniform grain structure distribution.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Investigating electrochemical corrosion at Mg alloy-steel joint interface using scanning electrochemical cell impedance microscopy (SECCIM)

Developing strategies to prevent corrosion at the interface of dissimilar metal alloys is challenging because of the presence of heterogenous distribution of galvanic couples and microstructural features that significantly change the corrosion rate. Devising strategies to mitigate this interfacial corrosion requires quantitative and correlative understanding of its surface electrochemical reaction. In this work, scanning electrochemical cell impedance microscopy (SECCIM) was employed to study location-specific corrosion in the interfacial region of dissimilar alloys, such as AZ31 (magnesium alloy) and DP590 (steel) welded using the Friction-stir Assisted Scribe Technique (FAST) processes. Herein, SECCM and SECCIM were used to perform correlative mapping of the local electrochemical impedance spectroscopic and potentiodynamic polarization to measure the effect of electronic and microstructural changes in the welded interfacial region on corrosion kinetics. Microstructural characterization including scanning electron microscopy and electron backscatter diffraction was performed to correlate changes in microstructural features and chemistry with the corresponding electronic properties that affect corrosion behavior. The variations in corrosion potential, corrosion current density, and electrochemical impedance spectroscopy behavior across the interface provide deeper insights on the interfacial region—which is chemically and microstructurally distinct from both bare AZ31 and DP590 that can help prevent corrosion in dissimilar metal structures.

59 BASIC BIOLOGICAL SCIENCES↗

DOE OSTI2023

An innovative and alternative approach toward gear fabrication

In this paper, we present the first demonstration of single-step gear manufacturing via an innovative in-situ friction stir forging approach. This novel process is a natural extension to the friction stir processing technique and relies on shear and normal stresses to form the complex shapes. Friction stir welding pin tool with shoulder is plunged at high revolutions per minute (rpm) into the sample to heat it to the desired temperature and enable plastic flow. Then, the tool is forged at high plunge rate to form the desired structurally-sound and defect free complex shapes. To better visualize the process the experiments are complemented by a 3D thermomechanically coupled, smoothed particle hydrodynamics (SPH) model to understand the material flow pattern both radially and through thickness in the gear teeth, plastic strain distribution, and temperature profile. We have demonstrated application of I-FSF to inherently poor formable AZ31 Mg, AA 7075-T6, and AA5083–10 vol% TiB 2 composite and fabricated 14-tooth spur gears from these materials with minimal farther machining. In conclusion, microstructure of the forged gears exhibited a directional material flow pattern due to the normal forging action and refinement of grains to 6–13 μm through dynamically recrystallization across the radial, through-thickness direction, which is in good agreement with the corresponding SPH simulation results.

42 ENGINEERING↗

DOE OSTI2023

Embedded anchoring of multi-material assemblies by friction riveting process

In this paper, we report on work that focused on extending the capability and broaden the applicability of the friction-riveting process for joining stacks composed of a wide range of multi-layer polymer-to-metals and similar and dissimilar metals. We first present direct experimental evidence of our use of this process to join aluminum-to-steel dissimilar metals with steel rivets. We have demonstrated for the first time the use of magnesium as a rivet material for joining carbon fiber reinforced polymer (CFRP) stacks, aluminum as a rivet material to laminate magnesium to CFRP, and aluminum-to-aluminum similar metal joining and aluminum-to-steel dissimilar metal joining with steel rivets. Our work sheds light on detailed process parameter optimization and the corresponding process response behavior, thus advancing our understanding of this complex joining method for a wide range of material combinations.

Friction-riveting, magnesium rivet, carbon fiber r↗

DOE OSTI2023

Microstructural, Corrosion, and Mechanical Characterization of Friction Stir Welded Al 6022-to-ZEK100 Mg Joints

Friction stir welded (FSW) aluminum–magnesium lightweight vehicle joints have gained significant interest due to their high strength-to-weight ratio. In this work, the corrosion resistance of this material is analyzed through electrochemical tests, which include open circuit potential (OCP) inspection and potentiodynamic polarization (PD) scanning. Weight loss measurements tested the corrosion rate of the FSW weld through cyclic corrosion testing (CCT) according to the standard SAEJ 2334. Mechanical properties were also investigated, including lap-shear strength, micro- and nano-hardness mapping, and true stress–strain curves as a function of local processing history. The electrochemical results indicate that the center weld zone’s corrosion property stays between the two base alloys. Indentation-based testing demonstrated that the weld zone behaves differently from base alloys. Lap shear strength surprisingly did not drop much even after eight weeks of cyclic corrosion tests, indicating that the joint did not allow any ingress of the electrolyte.

36 MATERIALS SCIENCE↗

DOE OSTI2023

THE ROLE OF FRACTURE PROPERTIES ON LAP JOINT STRENGTH OF FRICTION STIR WELDED AA7055-T6 SHEETS

Friction stir lap welded (FSLW) joints have weight-saving potential in aluminum-intensive automotive assembly. However, FSLW also modifies the material microstructure close to the joint. Optimizing the FSLW process requires understanding the relationship between the strength and the joint's microstructure. In previous studies, efforts have been dedicated to determining the effects of local softening, the shape of the oxide line, and porosity. However, the impact of changes to the fracture properties on the joint's strength has not been studied. In this work, strength testing, and simulations, aided by material characterization, were used to determine the role of fracture properties on the shear strength of a 3-sheet (aluminum alloys 7055-7055-6022) lap joint. Characterization involved testing for fracture properties in the weld region. This data was then implemented into finite element simulations. As a result, the joint strength was predicted with a deviation of less than 6% from the experimental value. Comparison with strength prediction using only the base metal properties indicates that fracture property in the nugget region determines the strength of AA7055 FSLW.

Finite element analysis, Friction stir welding, ma↗

DOE OSTI2023

High speed butt joining of 1” thick 2139-T8

Thick plate (=1”) butt joining of Al alloys is challenging due to high tool forces, uneven material flow, and heat distribution in the through-thickness direction. Tool design and welding parameters used for executing thick plate butt joining have remained mostly static over the past decade. Reported welding speeds that produce viable joint strength (mostly on 6xxx alloys) typically range below 100 mm/min (4inches /min). Researchers at Pacific Northwest National Laboratory (PNNL) in association with Ground Vehicle Systems Center (US Army GVSC) have been working to demonstrate greater joining efficiency at higher welding speeds in a 1” thick AA2139-T8 plate. Using innovative tool features and effective force and temperature control a joint efficiency of 80% was demonstrated at a welding speed of 7 inches /min (178mm/min).

Das, Hrishikesh↗

DOE OSTI2023

Assemblies, riveted assemblies, methods for affixing substrates, and methods for mixing materials to form a metallurgical bond

Riveted assemblies are provided that can include a substrate extending between two ends to define opposing substrate surfaces having a first opening extending between the opposing substrate surfaces; a metal-comprising substrate extending between two ends to define opposing metal-comprising substrate surfaces having a second opening extending between the opposing metal-comprising substrate surfaces. The riveted assemblies can further provide that the first and second openings complement one another when the substrate and metal-comprising substrate are engaged; and a rivet shaft extends through the openings and engages the substrate with the rivet head and the metal-comprising substrate with the rivet stop head, at least a portion of the stop head being mixed with, and forming a metallurgical bond with the metal-comprising substrate. Assemblies are provided that can include a rivet stop head mixed with, and metallurgically bonded with a metal-comprising substrate.Methods for affixing substrates to one another are also provided. The methods can include providing a substrate defining an opening configured to receive a rivet shaft; providing a metal-comprising substrate defining a complimentary opening; operatively engaging the substrates with the rivet shaft; and forming a stop head from the rivet shaft to affix the substrates. The method further includes that the stop head mixes with, and forms a metallurgical bond with the metal-comprising substrate. Methods for mixing materials to form a metallurgical bond are also provided. The methods can include forming a metallurgical bond between a stop head of a rivet and a metal-comprising substrate.