Additive‐Free Aqueous MXene Inks for Thermal Inkjet Printing on Textiles
Abstract Direct printing of functional inks onto flexible substrates allows for scalable fabrication of wearable electronics. However, existing ink formulations for inkjet printing require toxic solvents and additives, which make device fabrication more complex, limit substrate compatibility, and hinder device performance. Even water‐based carbon or metal nanoparticle inks require supplemental surfactants, binders, and cosolvents to produce jettable colloidal suspensions. Here, a general approach is demonstrated for formulating conductive inkjet printable, additive‐free aqueous Ti 3 C 2 T x MXene inks for direct printing on various substrates. The rheological properties of the MXene inks are tuned by controlling the Ti 3 C 2 T x flake size and concentration. Ti 3 C 2 T x ‐based electrical conduits and microsupercapacitors (MSCs) are printed on textile and paper substrates by optimizing the nozzle geometry for high‐resolution inkjet printing. The chemical stability and electrical properties of the printed devices are also studied after storing the devices for six months under ambient conditions. Current collector‐free, textile‐based MSCs show areal capacitance values up to 294 mF cm −2 (2 mV s −1 ) in poly(vinyl alcohol)/sulfuric acid gel electrolyte, surpassing reported printed MXene‐based MSCs and inkjet‐printed MSCs using other 2D nanomaterials. This work is an important step toward increasing the functional capacity of conductive inks and simplifying the fabrication of wearable textile‐based electronics.
Scalable Synthesis of Ti 3 C 2 T x MXene
Scaling the production of synthetic 2D materials to industrial quantities has faced significant challenges due to synthesis bottlenecks whereby few have been produced in large volumes. These challenges typically stem from bottom‐up approaches limiting the production to the substrate size or precursor availability for chemical synthesis and/or exfoliation. In contrast, MXenes, a large class of 2D transition metal carbides and/or nitrides, are produced via a top‐down synthesis approach. The selective wet etching process does not have similar synthesis constraints as some other 2D materials. The reaction occurs in the whole volume; therefore, the process can be readily scaled with reactor volume. Herein, the synthesis of 2D titanium carbide MXene (Ti 3 C 2 T x ) is studied in two batch sizes, 1 and 50 g, to determine if large‐volume synthesis affects the resultant structure or composition of MXene flakes. Characterization of the morphology and properties of the produced MXene using scanning electron microscopy, X‐ray diffraction, dynamic light scattering, Raman spectroscopy, X‐ray photoelectron spectroscopy, UV–visible spectroscopy, and conductivity measurements show that the materials produced in both batch sizes are essentially identical. This illustrates that MXenes experience no change in structure or properties when scaling synthesis, making them viable for further scale‐up and commercialization.