Thermal Spray toolpath development for a capped cylinder (“cake pan”) substrate

A near net shape coating is desired to be applied to the outer surface of a capped cylinder (“cake pan”) type substrate using thermal spray technology. A capped cylinder geometry is more complex than simple coupon-level substrate substrates (e.g., flat panels, cylinders) and thus requires a more complex toolpath to deposit a uniform coating. This report documents a practical theoretical approach to calculating relative torch-to-substrate speeds for coating the cylindrical, corner, and cap region of a rotating capped cylinder based on fundamental thermal spray toolpath principles. A preliminary experimental test deposited a thermal spray coating onto a mock substrate using toolpath speeds calculated by the theoretical approach proposed. The mock substrate was metallographically inspected to assess coating uniformity across the cylindrical, corner, and cap region. Inspection of the mock substrate revealed qualitatively uniform coating microstructure and thickness where theoretically predicted, demonstrating the viability of the proposed toolpath method and associated calculations. Pathways forward to optimizing coating uniformity at the cap center are proposed as near term suggested future work.

42 ENGINEERING↗

DOE OSTI2023

Residual stress of controlled atmosphere plasma spray blended metal deposits measured via in-situ substrate curvature method

The preliminary use of the in-situ curvature measurement technique for analyzing the planar stress evolution of controlled atmosphere plasma spray (CAPS) refractory metal deposits was performed with SNL-NM org. 1834’s CAPS system. A porous refractory metal exemplar of Ta-Nb was sprayed onto Ni-200, Ti-6Al-4V, and Al 7075-T6 substrates using a constant plasma torch parameter setting and deposition toolpath. Residual stresses of the deposits were found to be largely influenced by the substrate coefficient of thermal expansion and were calculated to be 49, 90, and -136 MPa for Ni 200, Ti-6Al-4V, and Al 7075-T6, respectively. The “Evolving stress” of the Ta-Nb deposits, which more accurately describes the mean intrinsic splat quenching stress of the spray material during deposition, was calculated to be 67, 92, and 129 MPa for Ni-200, Ti-6Al-4V, and Al 7075-T6, respectively. Notable difference in curvature measurement for the 1st coating pass for the Al 7075- T6 substrate was observed, with interface micrograph evidence suggesting potential softening and/or melting of the Al 7075-T6 substrate surface during deposition. Substrate temperature measurements prior to Ta-Nb deposition were used to calculate thermal energy absorbed from the hot gas plume by the different substrates and were found to correlate to the substrate’s thermal effusively. These calculated thermal energies were also found to be ~10 to 15% of the calculated energy output from the plasma torch’s nozzle exit for these experimental conditions.

36 MATERIALS SCIENCE↗