NASA NTRS1983

Analysis of grain boundary phase devitrification of Y2O3- and Al2O3-doped Si3N4

The present study has the objective to show that a Fourier Transform IR (FTIR) spectrometer in a single-beam reflection mode can be used for direct comparison of fractured vs nonfractured Si3N4 surfaces. This can be done because the FTIR method permits a digital summation of nearly 1000 scans of the fracture surface. Commercial-grade Si3N4, Y2O3, and Al2O3 were used in the study. The samples were heat treated in a vacuum induction heating furnace at either 1000 C for 10 h or 1200 C for 10 h each. Use of Fourier transform IR reflection spectroscopic analysis and X-ray diffraction shows that 10 h at 1200 C is sufficient to devitrify the amorphous grain boundary phase of Si3N4 containing 15 percent Y2O3 + 2 percent Al2O3 densification aids.

Hench, L. L.↗

NASA NTRS1983

Compositional effects on Si3N4 fracture surfaces

Surface analysis techniques (X-ray, infrared reflection spectroscopy, Auger electron spectroscopy) applied to the same samples reveal that fracture surfaces of Si3N4 with Y2O3 densification aids possess a higher concentration of oxygen than the bulk. The oxide densification aids thus concentrate in the grain boundaries, and even low-temperature fracture is seen as occurring preferentially within the oxygen-enriched grain boundaries. It is found that increasing the concentrations of Y2O3 and Al2O3 increases the oxygen content of the fracture surface. A range of 13-15 percent Y2O3 + 6 percent Al2O3 gives an amorphous grain-boundary phase that is resistant to devitrification. Fracture occurs through the amorphous phase, and heat treatment at 1000 C has little effect on the amorphous phase.

Hench, L. L.↗

NASA NTRS1982

Effect of Y2O3 and Al2O3 on the oxidation resistance of Si3N4

Oxidation of cold-pressed and sintered Si3N4 containing 15 wt% Y2O3 and 2, 4, 6, and 8% Al2O3 is observed at temperatures as low as 1000 C with IR reflection spectroscopy. Concentrations of Al2O3 in excess of 4% greatly retard the rate of oxidation and alter the mechanism of surface attack by promoting formation of a glassy layer on the surface containing mixed oxynitride bonds. The glassy layer retards heterogeneous attack and reduces the effect of an oxidation transition temperature between 1000 and 1100 C for these materials.

Hench, L. L.↗