DOE OSTI2023

First Results from Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System

A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950 {\deg}C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn phase and Nb (substrate). No peaks from any Nb3Sn compound other than Nb3Sn were detected. Later three 2.6 GHz Nb SRF cavities are coated with ~1 $\mu$m thick Nb3Sn. The first Nb3Sn coated cavity reached close to Eacc = 8 MV/m, demonstrating a quality factor Q0 of 3.2 x 108 at Tbath = 4.4 K and Eacc = 5 MV/m, about a factor of three higher than that of Nb at this temperature. Q0 was close to 1.1 x 109, dominated by the residual resistance, at 2 K and Eacc = 5 MV/m. The Nb3Sn coated cavities demonstrated Tc in the range of 17.9 - 18 K. Here we present the commissioning experience, system optimization, and the first results from the Nb3Sn fabrication on flat samples and SRF cavities.

43 PARTICLE ACCELERATORS↗

DOE OSTI2023

First Results From Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System

A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950 °C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn phase and Nb (substrate). No peaks from any Nb- Sn compound other than Nb3Sn were detected. Later three 2.6 GHz Nb SRF cavities are coated with ~1 μm thick Nb3Sn. The first Nb3Sn coated cavity reached close to Eacc = 8 MV/m, demonstrating a quality factor Q0 of 3.2 × 108 at Tbath = 4.4 K and Eacc = 5 MV/m, about a factor of three higher than that of Nb at this temperature. Q0 was close to 1.1 × 109, dominated by the residual resistance, at 2 K and Eacc = 5 MV/m. The Nb3Sn coated cavities demonstrated Tc in the range of 17.9 – 18 K. Here we present the commissioning experience, s ystem optimization, and the first results from the Nb3Sn fabrication on flat samples and SRF cavities.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗

DOE OSTI2023

First Results From Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System

A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950°C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn phase and Nb (substrate). No peaks from any Nb- Sn compound other than Nb3Sn were detected. Later three 2.6 GHz Nb SRF cavities are coated with ~1 μm thick Nb3Sn. The first Nb3Sn coated cavity reached close to Eacc = 8 MV/m, demonstrating a quality factor Q0 of $3.2 \times 108$ at Tbath = 4.4 K and Eacc = 5 MV/m, about a factor of three higher than that of Nb at this temperature. Q0 was close to $1.1 \times 109$, dominated by the residual resistance, at 2 K and Eacc = 5 MV/m. The Nb3Sn coated cavities demonstrated Tc in the range of $17.9 -- 18$ K. Here we present the commissioning experience, system optimization, and the first results from the Nb3Sn fabrication on flat samples and SRF cavities.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗

DOE OSTI2022

Nb₃Sn Coating of a 2.6 GHz SRF Cavity by Sputter Deposition Technique

Nb₃Sn is of interest as a coating for SRF cavities due to its higher transition temperature Tc ~18.3 K and superheating field Hsh ~400 mT, both are twice that of Nb. Nb₃Sn coated cavities can achieve high-quality factors at 4 K and can replace the bulk Nb cavities operated at 2 K. A cylindrical magnetron sputtering system was built, commissioned, and used to deposit Nb₃Sn on the inner surface of a 2.6 GHz single-cell Nb cavity. With two identical cylindrical magnetrons, this system can coat a cavity with high symmetry and uniform thickness. Using Nb-Sn multilayer sequential sputtering followed by annealing at 950°C for 3 hours, polycrystalline Nb₃Sn films were first deposited at the equivalent positions of the cavity’s beam tubes and equator. The film’s composition, crystal structure, and morphology were characterized by energy dispersive spectroscopy, X-ray diffraction, and atomic force microscopy. The Tc of the films was measured by the four-point probe method and was 17.61 to 17.76 K. Based on these studies, ~1.2 micron thick Nb₃Sn was deposited inside a 2.6 GHz Nb cavity. We will discuss first results from samples and cavity coatings, and the status of the coating system.

43 PARTICLE ACCELERATORS↗

DOE OSTI2022

3rd harmonic magnetometry assessment of NbTiN-based SIS structures

In the quest for alternative superconducting materials to bring accelerator cavity performance beyond the bulk niobium (Nb) intrinsic limits, a promising concept proposes that superconductor-insulator-superconductor (SIS) thin film structures can delay magnetic flux penetration in accelerator cavities to higher fields [1]. NbTiN is a candidate superconductor for such structures. We have demonstrated high quality NbTiN and AlN deposited by reactive direct current magnetron sputtering (DCMS), both for individual layers and multilayers. Interface quality has been assessed for bi-layer stacks with various NbTiN and AlN thicknesses from 500 and 30 nm down to 3 and 1 nm. These SIS structures show continued sharp interfaces. The Hfp enhancement of the films was examined with 3rd harmonic magnetometry. The system was designed and built in an ongoing collaboration with CEA Saclay. It can measure 1? to 2? samples on a temperature controlled stage. This contribution presents the assessment of the first penetration field enhancement with 3rd harmonic magnetometry for standalone films and multilayer nanostructures.

Valente, Anne-Marie↗

DOE OSTI2020

Nb 3 Sn multicell cavity coating system at Jefferson Lab

Superconducting radio frequency niobium cavities are the building blocks of modern accelerators for scientific applications. Lower surface resistance, higher fields, and high operating temperatures advance the reach of the future accelerators for scientific discovery as well as potentially enabling cost-effective industrial solutions. We describe the design and performance of an Nb 3 Sn coating system that converts the inner surface of niobium cavities to an Nb 3 Sn film. The niobium surface, heated by radiation from the niobium retort, is exposed to Sn and SnCl 2 vapor during the heat cycle, which results in about 2 μm Nb 3 Sn film on the niobium surface. Film composition and structure as well as radio frequency properties with 1-cell R&D cavities and 5-cell practical accelerator cavities are presented.

47 OTHER INSTRUMENTATION↗