Epitaxially Grown Single-Crystalline SrTiO 3 Membranes Using a Solution-Processed, Amorphous SrCa 2 Al 2 O 6 Sacrificial Layer
Water-soluble sacrificial layers based on epitaxially-grown, single crystalline (Ca, Sr, Ba) 3 Al 2 O 6 layer are widely used for creating free-standing perovskite oxide membranes. However, obtaining these sacrificial layers with intricate stoichiometry remains a challenge, especially for molecular beam epitaxy (MBE). In this study, we demonstrate the hybrid MBE growth of epitaxial, single crystalline SrTiO 3 films using a solution processed, amorphous SrCa 2 Al 2 O 6 sacrificial layer onto SrTiO 3 (001) substrates. Prior to the growth, the oxygen plasma exposure was used to first create the crystalline SrCa 2 Al 2 O 6 layer with well-defined surface crystallinity. Utilizing reflection high energy electron diffraction, x-ray diffraction, and atomic force microscopy, we observe an atomic layer-by-layer growth of epitaxial, single crystalline SrTiO 3 film on the SrCa 2 Al 2 O 6 layer with atomically smooth surfaces. The SrCa 2 Al 2 O6 layer was subsequently dissolved in de-ionized water to create free-standing SrTiO3 membranes that were transferred onto a metal-coated Si wafer. Membranes created with Sr-deficiency revealed ferroelectric-like behavior measured using piezo force microscopy whereas stoichiometric films remained paraelectric-like. Furthermore, these findings underscore the viability of using ex-situ deposited amorphous SrCa2Al2O6 for epitaxial, single crystalline growth, as well as the importance of point defects in determining the ferroic properties in membranes.