Strategies for a scalable multi-robot large scale wire arc additive manufacturing system
Not Available
36 MATERIALS SCIENCE↗
Engineering topics
Vaughan, Derek
Publications and source records attributed to Vaughan, Derek.
Development of Surface Treatment Solutions for Stamping Tools Fabricated via Additive Manufacturing
Oak Ridge National Laboratory (ORNL) and H.E.F. USA, Inc. (HEF) partnered to develop wear resistant surface treatment of additive manufactured steels for stamping die applications under CRADA agreement NFE-19-07909. This project aimed at evaluating the ARCOR® process, developed by HEF, to improve the surface behavior of 410SS (stainless steel), 410NiMo SS, 630 SS, and Maraging 250 steel coupons and demo components, fabricated via wire arc additive manufacturing (WAAM), with and without post print heat treatment. The peak hardness achieved was ~1000 HV and above (Up to 1300 HV) for all materials under proper processing parameters, and far exceeded the target hardness of 746 HV (60 HRC). Finally, stamping tools were printed and nitrocarburized with the optimum parameters, and then went through 500 fabrication cycles. Characterization of the used 17-4PH stamping tool discovered no crack or delamination in the nitrocarburized layer and the interface between the nitrocarburized layer and substrate.
36 MATERIALS SCIENCE↗
Prediction and understanding of non-linear distortion on large curved wall manufactured by wire-arc direct energy deposition
Not Available
36 MATERIALS SCIENCE↗
Mechanical responses of 316L stainless steel printed by wire arc additive manufacturing with different thermal histories
In this paper, 316L stainless steel walls were printed using single-bead pass and multiple-bead pass wire arc additive manufacturing (WAAM), which represent the internal basket wall and external wall of a spent nuclear fuel (SNF) canister; respectively. Scanning electron microscopy (SEM) microstructure characterization and tensile tests at room temperature (21 °C) and elevated temperature (250 °C) were performed on specimens extracted along the length and height directions of the printed walls. Results showed that grain morphology, grain angles, and retained ferrite are different between the two printed walls, which received different heat input in WAAM. The single-bead pass printed wall exhibited higher yield strength than the multiple-bead pass printed wall because of more retained ferrite and larger portion of random-high angle boundaries (RHAB) grains.
Tang, Wei↗
Effects of lead and lean in multi-axis directed energy deposition
Here, the present study examines the effect of varying laser incidence angles on textural, microstructural, and geometric characteristics of directed energy deposition (DED) processed materials, providing a more comprehensive outlook on participating laser-matter interaction phenomena and ultimately devising strategies to ameliorate print performance. In this study, single-layer, single-/multi-track specimens were processed to examine the effect of non-orthogonal angular configurations on bead morphology, microstructure, phase composition, and textural representation of DED-processed 316L stainless steel materials. It was observed that bead size decreased at increasing lead and lean angles. Asymmetry in the distribution of the bead morphology as a function of lead angle indicates better catchment for acute lead angle configurations over obtuse configurations. No significant differences in phase composition, texture, and microstructure were observed in moderate off-axis configurations. When the penetration depth for the deposits was below 20 μm, columnar structures dominated the microstructure of the deposited material. At deeper penetration depths, columnar and equiaxed structures were observed at the bead-substrate interface and center of the bead, respectively. Compared to powder-blown DED, wire-DED dilution profiles were found to be asymmetric in both orthogonal and non-orthogonal wire DED samples.
36 MATERIALS SCIENCE↗
316L Stainless Steel Wire Arc Additive Manufacturing and Characterization for Potential SNF Canister Production
In this paper, 316L stainless steel (316L SS) straight walls, curved walls, and vessels were printed by wire arc additive manufacturing (WAAM) using the 316L SS welding wire, to demonstrate the feasibility of spent nuclear fuel (SNF) canisters using this advanced manufacturing technique. Helium leak test with leak tight criteria of 1 × 10-7 ref-cc/s were performed on printed vessels with various wall thickness, and testing pressures were from 0.345 MPa (50 psi) to 1.724 MPa (250 psi). Printed wall microstructures were characterized using optical microscopy (OM) and scanning electron microscopy (SEM). Tensile specimens were machined out from printed walls along the length, height, and thickness directions, respectively, and tested at different temperature conditions, room temperature, 80 °C, 150 °C and 250 °C, respectively. Results showed t hat, all five WAAM-printed canisters with different thickness passed the helium leaktight criteria of radioactive materials containers by the ANSI N14.5; Dispersed micrometer-level size inclusions/voids were observed at printed wall cross sections, dendritic microstructures were found with grain size variation through the welding torch shifting direction, and very small amount of δ-ferrite and σ-phase were also observed in those cross sections; The printed walls were ductile, all tensile specimens broke with large plastic deformation/elongation and without brittle failure, and printed specimens yield strengths and tensile strengths under room temperature and 80 °C conditions are higher than minimum values of 316L SS for pressure vessels and for general applications at room temperature required by the ASTM standard, respectively.
Tang, Wei↗
Geometric Challenges in Designing Parts for Machining Using Wire-fed DED
Explore the source record for details and available documents.
Vaughan, Derek↗
Multi material/functionally graded wire arc additive manufacturing of high strength steel valves clad with nickel alloy 625 used for oil extraction
This Phase 1 technical collaboration project (ORNL/TM-2022/2683) began on August 1st, 2020 and concluded on July 31st, 2022. The collaboration partner Schlumberger is a large business enterprise assisting oil companies to extract oil from land and subsea cost competitively and safely. It is based in Houston, Texas USA. In this work as study of additive deposition of AWS EF100S-G and AWS ERNiCrMo-3 wires via wire-arc process was conducted.
36 MATERIALS SCIENCE↗
Large Scale Metal Additive Manufacturing for Stamping Dies
Oak Ridge National Laboratory (ORNL) worked with Dienamic Tooling Systems (DTS) in a follow-on Phase 2 effort to develop and demonstrate additively manufactured conformal cooling for hot stamping dies, providing a new industry capability that did not previously exist. Current approaches to die cooling are nonoptimal and based on what can be machined with traditional technologies. The printed approach to hot stamping cooling channels allows an analytical needs-based size and placement approach to cooling. Cooling is optimized and parts count is reduced producing a simpler more reliable faster to manufacture stamping tool. An additively manufactured hot stamping die with conformal cooling channels was manufactured and successfully tested in a real-world environment.
36 MATERIALS SCIENCE↗
Implementation of Sacrificial Support Structures for Hybrid Manufacturing of Thin Walls
Thin-walled features can be difficult to produce with traditional machining methods which often rely on excess stock material for stiffness. This challenge is increased in hybrid manufacturing where the feature is already near net shape before machining. Significant workpiece deflection can result in poor geometric and surface finish tolerances on the finished part. A potential solution to this problem is to implement sacrificial support structures to the as-printed geometry. The supports are then machined away during the finishing portion of the hybrid process. In the present work, several different design parameters for these sacrificial supports were evaluated to determine their impact on the quality of representative thin wall geometry samples. The angle, height, and spacing of triangular support structures were varied for each sample and then machined and examined. The addition of these supports relative to an unsupported configuration provided a deflection reduction of around 0.2 mm. Surface roughness was improved by approximately 1.5 µm. Increasing values of support height were found to correspond to reduced wall deflection. Similarly, decreasing values of support angle and support spacing improved geometric accuracy. Efficiency comparisons showed that increases in print time corresponded to rapidly diminishing gains in geometric accuracy but continued to improve surface roughness. Implications for hybrid finishing of additively manufactured thin-walled structures is briefly discussed.
36 MATERIALS SCIENCE↗
An experimental investigation of the effectiveness of Ar-CO 2 shielding gas mixture for the wire arc additive process
Wire arc additive manufacturing (AM) is the process by which a large, metallic structure is built layer-by-layer using a welding arc to melt a wire feedstock. A novel opportunity exists to alter the shielding gas composition to fabricate distinct geometrical features without altering the other AM parameters. In this paper, shielding gases with varied concentrations of Argon (Ar) and CO 2 was used to deposit three distinct geometric shapes (walls, infill, and overhang) using a wire-based additive manufacturing system utilizing the gas metal arc welding (GMAW) surface tension transfer (STT) process. Computer-aided design (CAD) models were sliced with a custom-built slicer, and the sliced algorithm was converted into optimal robotic toolpaths. A custom virtual instrument (VI) was built in LabVIEW to compare the temperature profiles on the surface during each deposition process. After each deposition, the geometric features were scanned, and the surface waviness value was evaluated. Tensile and Charpy impact coupons were extracted from the wall geometries in the longitudinal and transverse directions and tested. The results indicated that a higher CO 2 content produced higher melt pool temperatures to an extent, while lower contents of CO 2 resulted in a dimensionally accurate geometry. The data also indicated that the 2%/98% CO 2 /Ar blend produced scatter in tensile strength and the analysis of variance (ANOVA) shows significant difference. However, the intermediate range of CO 2 (5–10%) resulted in uniform tensile properties. Altogether, these results indicate that a 5%/95% CO 2 /Ar blend is the ideal shielding gas for lowering process temperatures and improving mechanical properties in wire arc additive manufacturing using the gas metal arc welding surface tension transfer process. Additionally, varying concentrations of Ar/CO 2 can be used within the same part in order to modify the local properties or process parameters such as strength, toughness, temperature, or dimensional features. This may improve overall manufacturing quality without sacrificing specific properties.
42 ENGINEERING↗