Finely divided powder mixture produced by vapor deposition of CR on small ThO2 particles was hot pressed or pressure bonded. Resulting alloy has lower ductile-to-brittle transition temperature than pure chromium, and high strength and oxidation resistance at elevated temperatures, both in as-rolled condition and after annealing.
Unalloyed chromium and chromium containing approximately 3 wt % ThO2 were prepared from powder produced by a chemical vapor deposition process. When rolled to sheet and tested in tension, it was found that the thoriated material had a lower ductile-to-brittle transition temperature (DBTT) than unalloyed chromium. This ductilizing was evident both in the as-rolled condition and after the materials had been annealed for 1 hour at 1200 C. The improved ductility in thoriated chromium may be associated with several possible mechanisms: (1) particles may disperse slip, such that critical stress or strain concentrations for crack nucleation are more difficult to achieve; (2) particles may act as dislocation sources, thus providing mobile dislocations in this normally source-poor material, in a manner similar to prestraining; and (3) particles in grain boundaries may help to transmit slip across the boundaries, thus relieving stress concentrations and inhibiting crack nucleation.
Low temperature ductility and high temperature strength of pure chromium and chromium-thoria alloy prepared from vapor deposited powders
Hydrogen reduction of iodide chromium in vapor deposition of chromium on thorium oxide