DOE OSTI2021

Ion irradiation induced strain and structural changes in LiTaO 3 perovskite

LiTaO 3 crystals irradiated with 3 MeV and 1.162 GeV Au ions were studied by single crystal x-ray diffraction and Raman scattering measurements. The maximum lattice strains after 3 MeV Au ion irradiation to a fluence of 1.2 × 10 13 cm -2 were 1.2% and 0.6% along the c- and a-/b-axes, respectively. Two effects were observed in 1.162 GeV Au ion irradiated samples: (i) the (0006) and (1120) Bragg peaks were split into doublets, which suggested a subtle structural change due to slight modification of chemical composition; and (ii) the pre-damaged 1.2% lattice strain along the c-axis was relaxed to 0.9% after subsequent irradiation with 1.162 GeV Au ions, while relaxation along the a- or b-axis was not obvious. A distinct change in the Raman spectrum of the <0001> oriented LiTaO 3 crystals was observed after 1.162 GeV Au ion irradiation, but no obvious change was observed in the <1120> oriented samples or in 3 MeV Au ion irradiated samples. Strain and structural changes in crystalline LiTaO3, with or without pre-existing defects, upon ion irradiation are delineated in its responding to inelastic ionization and elastic nuclear collisions.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Local structure of Ni 80 X 20 (X: Cr, Mn, Pd) solid-solution alloys and its response to ion irradiation

In this work, the local structure of Ni 80 X 20 (X: Cr, Mn, Pd) solid-solution alloys was investigated with x-ray absorption and total scattering x-ray diffraction methods. Atomic pair distribution function (PDF) analysis indicated that the local lattice distortion is strongly relevant to the atomic size mismatch, and the local lattice distortion in Ni80Pd20 alloy is obviously larger than that in other solid-solution alloys. The bond length of different atomic pairs was derived from the fitting of extended x-ray absorption fine structure spectra. Quantitative analysis of the local bonding environment in Ni 80 Cr 20 during Ni ion irradiation suggested that Cr atoms tend to form clusters in Ni 80 Cr 20 with the increase of ion dose.

36 MATERIALS SCIENCE↗
DOE OSTI2017

Local Structure and Short-Range Order in a NiCoCr Solid Solution Alloy

Multi-element solid solution alloys are intrinsically disordered on the atomic scale, and many of their advanced properties originate from the unique local structural characteristics. We measured the local structure of a NiCoCr solid solution alloy with X-ray/neutron total scattering and extended X-ray absorption fine structure (EXAFS) techniques. The atomic pair distribution function analysis (PDF) did not exhibit distinct structural distortion. But, EXAFS analysis suggested that the Cr atoms are favorably bonded with Ni and Co in the solid solution alloys. This short-range order (SRO) plays a role in the distinct low values of electrical and thermal conductivities in Ni-based solid solution alloys when Cr is incorporated. Both the long-range and local structures of the NiCoCr alloy upon Ni ion irradiation were studied and an irradiation-induced enhancement of SRO was found.