Amorphous silicon thin films: The ultimate lightweight space solar cell

Progress is reported with respect to the development of thin film amorphous (alpha-Si) terrestrial solar cells for space applications. Such devices promise to result in very lightweight, low cost, flexible arrays with superior end of life (EOL) performance. Each alpha-Si cell consists of a tandem arrangement of three very thin p-i-n junctions vapor deposited between film electrodes. The thickness of this entire stack is approximately 2.0 microns, resulting in a device of negligible weight, but one that must be mechanically supported for handling and fabrication into arrays. The stack is therefore presently deposited onto a large area (12 by 13 in), rigid, glass superstrate, 40 mil thick, and preliminary space qualification testing of modules so configured is underway. At the same time, a more advanced version is under development in which the thin film stack is transferred from the glass onto a thin (2.0 mil) polymer substrate to create large arrays that are truly flexible and significantly lighter than either the glassed alpha-Si version or present conventional crystalline technologies. In this paper the key processes for such effective transfer are described. In addition, both glassed (rigid) and unglassed (flexible) alpha-Si cells are studied when integrated with various advanced structures to form lightweight systems. EOL predictions are generated for the case of a 1000 W array in a standard, 10 year geosynchronous (GEO) orbit. Specific powers (W/kg), power densities (W/sq m) and total array costs ($/sq ft) are compared.

Vendura, G. J., Jr.↗

NASA NTRS1984

Advances in large area polycrystalline solar cells

Polycrystaline silicon is presently routinely processed into low cost 10 cm by 10 cm solar cells. However assuming minimal handling difficulties, only minor equipment modifications and no increase in processing complexity, the fabrication of even larger geometries would be economically advantageous. This investigation addressed the feasibility of developing 10 cm by 15 cm solar cells from research through pilot line production stages. The major thrust was to minimize costing by using existing production equipment and proven techniques wherever possible. Accordingly methods were developed to section larger substrates from existing cast ingots, a simple solar cell was designed and low cost processes implemented. After numerous preliminary experiments, pilot line production of 1500 cells was completed. Of these approximately 62 percent exhibited efficiencies greater than 7.0 percent, 53 percent were greater than 8.0 percent and 15 percent were greater than 9.0 percent. Based on this study, the regular production of 10 cm by 15 cm solar cells was determined to be both feasible and cost effective using existing processing methods.

Vendura, G. J., Jr.↗