Giant uniaxial negative thermal expansion in FeZr 2 alloy over a wide temperature range
Negative thermal expansion (NTE) alloys possess great practical merit as thermal offsets for positive thermal expansion due to its metallic properties. However, achieving a large NTE with a wide temperature range remains a great challenge. Herein, a metallic framework-like material FeZr 2 is found to exhibit a giant uniaxial (1D) NTE with a wide temperature range (93-1078 K, $\overline{α}_{l}$=–34.01×10 –6 K –1 ). Such uniaxial NTE is the strongest in all metal-based NTE materials. The direct experimental evidence and DFT calculations reveal that the origin of giant NTE is the couple with phonons, flexible framework-like structure, and soft bonds. Interestingly, the present metallic FeZr 2 excites giant 1D NTE mainly driven by high-frequency optical branches. It is unlike the NTE in traditional framework materials, which are generally dominated by low energy acoustic branches. In the present study, a giant uniaxial NTE alloy is reported, and the complex mechanism has been revealed. It is of great significance for understanding the nature of thermal expansion and guiding the regulation of thermal expansion.
Negative and zero thermal expansion in α-(Cu 2-x Znx)V 2 O 7 solid solutions
Negative or zero thermal expansion (NTE or ZTE) of materials is intriguing for controllable thermal expansion. In this work, we report a series of orthorhombic α-Cu 2- x Zn x V 2 O 7 ( x = 0, 0.1, 0.2), in which the volumetric coefficients of thermal expansion are successfully tuned from -10.19 × 10 -6 K -1 to -1.58 × 10 -6 K -1 in the temperature range of 100–475 K by increasing the content of Zn 2+ . It has been revealed that the transverse vibrations of oxygen bonded with vanadium are dominant in the contraction of the bc plane, leading to the overall volume NTE in α-Cu 2 V 2 O 7 . The introduction of Zn 2+ densifies the crystal structure, which is presumed to suppress the space of transverse vibrations and results in the ZTE in α-Cu 1.8 Zn 0.2 V 2 O 7 . This work presents an effective method to realize ZTE in anisotropic framework systems.