Studies of erosion of solar max samples of Kapton and Teflon

Several samples of Kapton and Teflon which was exposed to solar radiation were examined. The samples represent material behavior in near Earth space. Clues to the identity of erosive processes and the responsible species were searched for. Interest centered around oxygen atoms which are ubiquitous at these altitudes and are known to erode some metal surfaces. Three diagnostic methods were employed: optical microscopy, scanning electron microscopy, and fourier transform infrared spectroscopy. Two types of simulation were used: a flow containing low energy oxygen atoms and bombardment with 3000 volt Ar ions. Results and conclusions are presented.

Fristrom, R. M.↗
NASA NTRS1978

Techniques used for limiting degradation products of polymeric materials for use in the space environment

Techniques are discussed for limiting or controlling the degradation products (outgassing) of polymeric materials in the space environment. One technique, now ASTM E-595-77, is used to screen out those materials which lose greater than 1% Total Mass Loss when in vacuum for 24 hours at 125 C and which have more than 0.10% Collected Volatile Condensable Materials condensing on a collector surface at 25 C. Examples of silicone materials which are high and low in outgassing are given. The numerous mechanical motions in spacecraft experiments require liquid lubricants which also might degrade in space. Labyrinth seals and barrier films are utilized to limit the degradation of or from these lubricants. A recoverable in-flight experiment has been proposed for making definitive measurements of how effective these techniques are in limiting the amounts and escape paths of outgassed molecules.

Vest, C. E.↗
NASA NTRS1976

Tests of a sputtered MoS2 lubricant film in various environments

This paper discusses conditions and results of several tests of a DC sputtered MoS2 dry lubricant film. The test components were miniature precision ball bearings and rings and blocks; the surrounding atmospheres were laboratory air, pure helium, vacuum to 10 to the -8th power torr, and a perfluoroalkylpolyether oil. The results showed that the lubricant would perform satisfactorily under lightly loaded (450 gm) ball bearings in vacuum and would not perform well under a 66-kg load in air, a 132-kg load in helium, or a 330-kg load under oil. These tests and others show that the sputtered MoS2 film has some desirable features for space applications as well as some definite limitations.

Vest, C. E.↗
NASA NTRS1973

Evaluation of several additional dry lubricants for spacecraft applications

Four transfer-film ball-bearing retainer materials were evaluated for their lubricating ability and wear capability under conditions of 120-gram radial load, 450-gram axial load, 3600-rpm unidirectional rotation, 23 C ambient temperature, and less than .1 microtorr pressure, using R-2 sized unshielded ball bearings. The 'stop-test' criterion was a total of one billion revolutions or a torque buildup greater than 18 gm-cm per bearing pair. A PTFE-fiberglass-MoS2 composite, a PTFE-bronze composite, and a tantalum-molybdenum-MoS2 composite operated for one billion revolutions without reaching the 18-gram torque limit. A p-oxybenzoyl polymer-MoS2 composite operated sixteen million revolutions before reaching the 18-gm cm stop-test torque. The first three materials are considered as suitable lubricants under the test conditions employed.

Vest, C. E.↗
NASA NTRS1973

Friction, wear, and noise of slip ring and brush contacts for synchronous satellite use.

A program is being conducted for testing of slip rings for synchronous orbit application. Instrumentation systems necessary for monitoring electrical noise, friction, and brush wear at atmospheric pressure and at less than 50 nanotorr have been developed. A multiplex scheme necessary for the simultaneous recording of brush displacement, friction, and electrical noise has also been developed. Composite brushes consisting of silver-molybdenum disulfide-graphite and silver-niobium diselenide-graphite have been employed on rings of coin silver and rhodium plate. Brush property measurements made included measurement of density, electrical resistivity, shear strength, and microstructure.

Lewis, N. E.↗
NASA NTRS1972

Friction, wear and noise of slip ring and brush contacts for synchronous satellite use.

A program is being conducted for testing of slip rings for synchronous orbit application. Instrumentation systems necessary for monitoring electrical noise, friction, and brush wear at atmospheric pressure and at less than 50 ntorr have been developed. A multiplex scheme necessary for the simultaneous recording of brush displacement, friction, and electrical noise has also been developed. Composite brushes consisting of silver-molybdenum disulfide-graphite and silver-niobium diselenide-graphite have been employed on rings of coin silver and rhodium plate. Four contact combinations have been tested during an ambient condition run-in at 150 rpm and a humidity sequence at 0.1 rpm. The first six months of the two year vacuum test at 0.1 rpm have been completed. Electrical noise, friction and brush wear data recorded during these periods have been analyzed.

Lewis, N. E.↗
NASA NTRS1971

Meeting the challenge of a 50000-hour-life-time requirement

Space mission requirements for the 70's have established a 50,000-hour-lifetime challenge for the mechanisms designer. This challenge may be met by two approaches: (1) development of new materials for wear-prone elements, and (2) design innovation of new electromechanical devices that do not include mechanical wear-prone components. Present state-of-the-art materials require restricted operation regarding load, speed, and power for gears, bearings, and brush-slipring components. These restrictions are discussed, and methods of improvement are suggested. The design-innovations approach is discussed and is illustrated by the design of an experimental magnetically suspended motor.

Vest, C. E.↗