DOE OSTI2023

Coal-based Bricks & Blocks (CBBs): Process Development to Prototype Fabrication Coupled with Techno-Economic Analysis and Market Survey

Coal-based bricks and blocks (CBBs) were formulated using anthracite and thermoplastic binder. Lab scale test composites were formed by hot-press molding and commercial extrusion for test articles and for a full-scale prototype. Formulations and test matrices followed a systematic experimental design to examine the effects of and interactions among three primary independent variables: a) thermoplastic type, b) weight fractions of binder relative to the total anthracite weight, and c) relative proportions of large versus small (milled) anthracite size fractions. Technical performance metrics include compressive strength, modulus, porosity/permeability and density. These DoE studies establish composition-property relations and identify the best combination for any desired property of interest – in particular, strength. Based on CBB composition and fabrication process, validated against technical performance metrics, a techno-economic analysis was constructed which incorporated a process flow model, engineering design (with scaling), and calculated capital plus operating costs. Based on measured property metrics and estimated process economics and a projected price by TEA (techno-economic analysis), building and construction target markets were identified by a market survey assessment. With known cost, price, performance metrics and competitive advantages for CBBs matched with commercial applications/uses, a technical gap analysis was performed to identify further development required for scale-up and commercialization.

01 COAL, LIGNITE, AND PEAT↗

DOE OSTI2023

Thermo-Catalytic Decomposition Comparisons: Carbon Catalyst Structure, Hydrocarbon Feed and Regeneration

Thermo-catalytic decomposition (TCD) activity and stability depend upon the initial carbon catalyst structure. However, further transitions in the carbon structure depend on the carbon material (structure and composition) originating from the TCD process. In this article, reaction data are presented that illustrates the time-dependent TCD activity as TCD-formed carbon contributes and then dominates conversion. A variety of initial carbon catalysts are compared, including sugar char, a conductive carbon black (AkzoNobel Ketjenblack), a rubber-grade carbon black (Cabot R250), and its graphitized analogue as formed and partially oxidized. Regeneration of carbon catalysts by partial oxidation is evaluated using nascent carbon black as a model, coupled with subsequent comparative TCD performance relative to the nascent, non-oxidized carbon black. Activation energies for TCD with nascent and oxidized carbons are evaluated by a leading-edge analysis method applied to TCD. Given the correlation between nanostructure and active sites, two additional carbons, engine soots, are evaluated for regeneration and dependence upon nanostructure. Active sites are quantified by oxygen chemisorption, followed by X-ray photoelectron spectroscopy (XPS). The structure of carbon catalysts is assessed pre- and post-TCD by high-resolution transmission electron microscopy (HRTEM). Last, energy dispersive X-ray analysis mapping (EDS) is carried out for its potential to visualize oxygen chemisorption.