Phase II Development of the Surveillance Test Articles to Improve the Design, Fabrication, and Testing

Advanced reactors, such as the molten salt reactor (MSR), require materials that will withstand harsher environments than the materials used for lower temperature water reactors. Materials used in MSR construction need not only withstand elevated temperature, temperature cycling, and neutron radiation, but must be able to withstand the corrosive molten salt environment. Significant materials research has been driven by the materials needs of the MSR due to the harsh environment and the material data requirements to support licensing. Limited operation experience with MSRs has made this challenging work. Information is very limited on materials degradation due to irradiation, molten salt corrosion, elevated temperature, and the resulting fatigue, creep, and creep-fatigue loading during operation. While efforts are underway to better understand the effects of this harsh environment on construction materials, the Advanced Reactors Technologies (ART) Program has been working to develop materials surveillance test articles that could be used in a materials surveillance program and allow for the collection of information on the materials degradation during plant operation and could support timely licensing of these advanced reactors.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2022

Surveillance Test Articles Development

Material degradation in Advance Test Reactors (ATR) is governed by irradiation, corrosion, elevated temperature exposure and cyclic mechanical creep-fatigue loads. This degradation information during reactor operation condition is limited. Hence, material damage monitoring is a key aspect of the design, analysis and licensing of ATR components. The idea is to monitor material component operation conditions of component by using a surveillance test article. This test article is fabricated with bi-metal configuration with two different thermal expansion coefficients, and design is motivated by Simplified Model Test (SMT) specimen which can capture structure-like mechanical response. Upon raising temperature of the bi-metal test article configuration, expansion mismatch results tensile load on specimen. Thus, temperature dependent passively actuated loading is achieved. The idea is to place this surveillance test article in reactor at location ‘x’ to surveil the mechanical response at critical location ‘y’. By calibrating the test article design, material degradation at critical location can be surveilled through assessing the degradation in surveillance test article. This study presents test article development with different material combinations and follow-up experimental testing work through passively loading test article with temperature history. The test article geometry and observed test results are presented in presentation slides.

36 MATERIALS SCIENCE↗