Adsorption and activation of CO 2 on Pt/CeOx/TiO 2 (110): Role of the Pt-CeO x interface

The adsorption and dissociation of CO 2 on TiO 2 (110), CeO x /TiO 2 (110) and Pt/CeO x /TiO 2 (110) surfaces has been examined using Ambient Pressure X-ray Photoelectron Spectroscopy (AP-XPS). The substrates under study exhibited different degrees of complexity which were tested for the binding of the adsorbate and the cleavage of C-O bonds. The surfaces were prepared by depositing CeO x (0.1 ML) onto TiO 2 (110) to form a mixed oxide support, onto which Pt nanoparticles (0.2 ML) were deposited. This configuration yields a complex set of interfaces between metal and oxides and we have systematically titrated the active role of each component (Pt 4f, Ce 3d and Ti 2p regions) and the arising surface intermediates (C 1s and O 1s regions). CO 2 barely bonds to stoichiometric TiO 2 (110). It heals oxygen vacancies of this oxide surface (CO 2,gas → CO gas + O a ) and does not form stable carbonates. A stable carbonate was seen upon adsorption of CO 2 on CeO x /TiO 2 (110) and on this type of substrate the adsorbate also removed O vacancies leading to the oxidation of Ti 3+ and Ce 3+ sites. Pt nanoparticles dispersed on CeO x /TiO 2 (110) were highly effective for the binding and dissociation of CO 2 , with the formation of CO 3 , CO, C and CH x species on the Pt/CeO x /TiO 2 (110) system. The results of theoretical calculations based on density-functional theory (DFT) show that Pt/CeOx/TiO2(110) binds CO2 much stronger than surfaces of bulk platinum {(111), (100), (110)} or other late transition metals. On a Pt-CeO x interface, the molecule adsorbs with a bent configuration (~ 130° O-C-O bond angle) and with a substantial elongation (~ 0.1 Å) of the C-O bonds, facilitating its transformation into high value chemicals.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Enhanced Catalysis under 2D Silica: A CO Oxidation Study

Abstract Interfacially confined microenvironments have recently gained attention in catalysis, as they can be used to modulate reaction chemistry. The emergence of a 2D nanospace at the interface between a 2D material and its support can promote varying kinetic and energetic schemes based on molecular level confinement effects imposed in this reduced volume. We report on the use of a 2D oxide cover, bilayer silica, on catalytically active Pd(111) undergoing the CO oxidation reaction. We “uncover” mechanistic insights about the structure–activity relationship with and without a 2D silica overlayer using in situ IR and X‐ray spectroscopy and mass spectrometry methods. We find that the CO oxidation reaction on Pd(111) benefits from confinement effects imposed on surface adsorbates under 2D silica. This interaction results in a lower and more dispersed coverage of CO adsorbates with restricted CO adsorption geometries, which promote oxygen adsorption and lay the foundation for the formation of a reactive surface oxide that produces higher CO 2 formation rates than Pd alone.

Eads, Calley N.↗
DOE OSTI2021

In situ ambient pressure XPS study of Pt/Cu(111) single-atom alloy in catalytically relevant reaction conditions

The presence of multiple reactant gases as well as reaction intermediates in a heterogeneous catalytic reaction results in a complex interaction between different components of the catalyst with each gas, which can alter the surface and chemical state of the catalyst differently than in the presence of an individual gas alone. In this study, we used in situ ambient pressure x-ray photoelectron spectroscopy to study the surface state of Pt/Cu(111) single-atom alloy model system in two catalytically relevant reaction conditions: CO 2 hydrogenation and CO oxidation. We found that the activation of CO 2 results in the formation of CO, which adsorbs on Pt sites at up to 400 K. In the presence of CO 2 and H 2 , Pt catalyzes the reverse water–gas shift reaction, which produces more CO and further stabilizes surface Pt atoms at 450 K. On the other hand, in CO oxidation condition, the presence of O 2 results in the formation of a thick Cu 2 O layer at higher temperatures, and Pt atoms are no longer detected in the surface and subsurface layers. When O 2 is introduced to the sample before CO, the formation of a complete Cu 2 O layer that covers all Pt atoms occurs immediately at room temperature. Finally, however, when CO is introduced at room temperature before O 2 , the presence of adsorbed CO on Pt sites stabilizes the surface Pt atoms and prevents the formation of a complete Cu 2 O layer, thus exposing the Pt atoms in 'holes' in the Cu 2 O layer.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Local Modulation of Single-Atomic Mn Sites for Enhanced Ambient Ammonia Electrosynthesis

Rationally tuning the local structures of single-atomic active sites for the electrocatalytic N 2 reduction reaction (NRR) remains an urgent but worthwhile research topic. Herein, we accomplish the local modulation of single-atomic Mn sites and construct single Mn–O 3 N 1 sites anchored on porous carbon (Mn–O 3 N 1 /PC) by delicately controlling the Mn–O bonding conditions. Furthermore, the constructed structures are confirmed via the combination of atomic-scale imaging, Raman spectroscopy, synchrotron radiation-based soft and hard X-ray absorption spectroscopies, and X-ray photoelectron spectroscopy. The Mn–O 3 N 1 /PC catalyst yields an NH 3 yield rate of 66.41 μg h –1 mg cat. –1 (corresponding to 1.56 mg h –1 mg Mn –1 ) at -0.35 V versus reversible hydrogen electrode, which is about four times that on the control Mn–N 4 /PC catalyst. The enhanced NRR performance is ascribed to its unique geometry and electronic structures, which not only facilitate the adsorption and activation of the N 2 molecule but also lower the free energy change of the potential-determining step.

36 MATERIALS SCIENCE↗
DOE OSTI2020

A Surface Se-Substituted LiCo[O 2-δ Se δ ] Cathode with Ultrastable High-Voltage Cycling in Pouch Full-Cells

Cycling LiCoO 2 to above 4.5 V for higher capacity is enticing; however, hybrid O anion- and Co cation-redox (HACR) at high voltages facilitates intrinsic O α - (α < 2) migration, causing oxygen loss, phase collapse, and electrolyte decomposition that severely degrade the battery cyclability. Hereby, commercial LiCoO 2 particles are operando treated with selenium, a well-known anti-aging element to capture oxygen-radicals in the human body, showing an “anti-aging” effect in high-voltage battery cycling and successfully stopping the escape of oxygen from LiCoO 2 even when the cathode is cycled to 4.62 V. Furthermore, ab initio calculation and soft X-ray absorption spectroscopy analysis suggest that during deep charging, the precoated Se will initially substitute some mobile O α - at the charged LiCoO 2 surface, transplanting the pumped charges from O α - and reducing it back to O 2- to stabilize the oxygen lattice in prolonged cycling. As a result, the material retains 80% and 77% of its capacity after 450 and 550 cycles under 100 mA g -1 in 4.57 V pouch full-cells matched with a graphite anode and an ultralean electrolyte (2 g Ah -1 ).

36 MATERIALS SCIENCE↗
DOE OSTI2020

Thermally Driven Interfacial Degradation between Li 7 La 3 Zr 2 O 12 Electrolyte and LiNi 0.6 Mn 0.2 Co 0.2 O 2 Cathode

Solid-state batteries offer higher energy density and enhanced safety compared to the present lithium-ion batteries using liquid electrolytes. A challenge to implement them is the high resistances, especially at the solid electrolyte interface with the cathode. Sintering at elevated temperature is needed in order to get good contact between the ceramic solid electrolyte and oxide cathodes and thus to reduce contact resistances. Many solid electrolyte and cathode materials react to form secondary phases. It is necessary to find out which phases arise as a result of interface sintering and evaluate their effect on electrochemical properties. Herein, we assessed the interfacial reactions between LiNi 0.6 Mn 0.2 Co 0.2 O 2 (NMC622) and Li 7 La 3 Zr 2 O 12 (LLZO) as a function of temperature in air. We prepared model systems by depositing thin-film NMC622 cathode layers on LLZO pellets. The thin-film cathode approach enabled us to use interface-sensitive techniques such as X-ray absorption spectroscopy in the near-edge as well as the extended regimes and identify the onset of detrimental reactions. We found that the Ni and Co chemical environments change already at moderate temperatures, on-setting from 500 °C and becoming especially prominent at 700 °C. By analyzing spectroscopy results along with X-ray diffraction, we identified Li 2 CO 3 , La 2 Zr 2 O 7 , and La(Ni,Co)O 3 as the secondary phases that formed at 700 °C. The interfacial resistance for Li transfer, measured by electrochemical impedance spectroscopy, increases significantly upon the onset and evolution of the detected interface chemistry. Our findings suggest that limiting the bonding temperature and avoiding CO 2 in the sintering environment can help to remedy the interfacial degradation.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Bulk vs Intrinsic Activity of NiFeO x Electrocatalysts in the Oxygen Evolution Reaction: The Influence of Catalyst Loading, Morphology, and Support Material

We used a combination of ultrahigh vacuum surface science techniques, X-ray spectroscopy, electrochemistry, and density functional theory (DFT), to characterize the influence of catalyst morphology, loading/coverage, and substrate material on the bulk (all atoms) and intrinsic (electrochemically accessible atoms) activity of NiFeO x electrocatalysts in the oxygen evolution reaction (OER). NiFeO x catalysts were grown on both Au(111) and highly oriented pyrolytic graphite (HOPG) electrodes. DFT predicted Fe edge-site atoms at the NiFeO x /Au(111) interface to be the most thermodynamically favorable reaction center, and X-ray absorption spectroscopy data indicated small NiFeO x catalyst particles on Au(111) contained a high population of OER active Fe edge-site atoms. However, restructuring of the Au(111) surface due to repeated oxidation and reduction cycles of the OER CV measurements encapsulated small NiFeO x nanoparticles at catalyst loadings below ~1.5 nmol metal /cm 2 , passivated catalyst edges and reduced bulk OER activity of Au-supported NiFeO x compared with HOPG-supported ones. Analysis of intrinsic activity revealed that the Au(111) support strongly benefited electrochemically accessible NiFeO x atoms, and we observed a 2–3 fold activity enhancement compared with HOPG-supported catalysts for loadings above ~1 nmol metal /cm 2 . Overall, evaluating bulk vs intrinsic activity and identifying loading/coverage-dependent support effects is important for accurately probing fundamental interfacial chemistry, choosing suitable catalyst loadings and supports, and optimizing system parameters to maximize the performance of electrocatalyst systems.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Catalytic Oxidation of CO on a Curved Pt(111) Surface: Simultaneous Ignition at All Facets through a Transient CO-O Complex

The light-off of the CO oxidation is simultaneous on all Pt crystal surfaces vicinal to the (111) plane, regardless of the reaction conditions, and in contrast with the structural dependence of Pd. In this work, using ambient-pressure XPS we find that, immediately prior to ignition, atomic oxygen incorporates to the subsurface plane, leading to buckling of the topmost CO-Pt layer, and effectively equaling the CO desorption temperature at terraces and steps.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Nucleation and Initial Stages of Growth during the Atomic Layer Deposition of Titanium Oxide on Mesoporous Silica

A chemical approach to the deposition of thin films on solid surfaces is highly desirable but prone to affect the final properties of the film. To better understand the origin of these complications, the initial stages of the atomic layer deposition of titania films on silica mesoporous materials were characterized. Adsorption-desorption measurements indicated that the films grow in a layer-by-layer fashion, as desired, but initially exhibit surprisingly low densities, about one-quarter of that of bulk titanium oxide. Electron microscopy, X-ray diffraction, UV/visible, and X-ray absorption spectroscopy data pointed to the amorphous nature of the first monolayers, and EXAFS and 29 Si CP/MAS NMR results to an initial growth via the formation of individual tetrahedral Ti-oxide units on isolated Si-OH surface groups with unusually long Ti-O bonds. Here, density functional theory calculations were used to propose a mechanism where the film growth starts at the nucleation centers to form an open 2D structure.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Stabilized Co-Free Li-Rich Oxide Cathode Particles with An Artificial Surface Prereconstruction

Li-rich metal oxide (LXMO) cathodes have attracted intense interest for rechargeable batteries because of their high capacity above 250 mAh g –1 . However, the side effects of hybrid anion and cation redox (HACR) reactions, such as oxygen release and phase collapse that result from global oxygen migration (GOM), have prohibited the commercialization of LXMO. GOM not only destabilizes the oxygen sublattice in cycling, aggravating the well-known voltage fading, but also intensifies electrolyte decomposition and Mn dissolution, causing severe full-cell performance degradation. In this study, an artificial surface prereconstruction (ASR) for Li 1.2 Mn 0.6 Ni 0.2 O 2 particles with a molten-molybdate leaching is conducted, which creates a crystal-dense anion-redox-free LiMn 1.5 Ni 0.5 O 4 shell that completely encloses the LXMO lattice (ASR-LXMO). Differential electrochemical mass spectroscopy and soft X-ray absorption spectroscopy analyses demonstrate that GOM is shut down in cycling, which not only stabilizes HACR in ASR-LXMO, but also mitigates the electrolyte decomposition and Mn dissolution. ASR-LXMO displays greatly stabilized cycling performance as it retains 237.4 mAh g –1 with an average discharge voltage of 3.30 V after 200 cycles. More crucially, while the pristine LXMO cycling cannot survive 90 cycles in a pouch full-cell matched with a commercial graphite anode and lean (2 g A –1 h –1 ) electrolyte, ASR-LXMO shows high capacity retention of 76% after 125 cycles in full-cell cycling.

25 ENERGY STORAGE↗
DOE OSTI2020

Protonic solid-state electrochemical synapse for physical neural networks

Physical neural networks made of analog resistive switching processors are promising platforms for analog computing. State-of-the-art resistive switches rely on either conductive filament formation or phase change. These processes suffer from poor reproducibility or high energy consumption, respectively. Herein, we demonstrate the behavior of an alternative synapse design that relies on a deterministic charge-controlled mechanism, modulated electrochemically in solid-state. The device operates by shuffling the smallest cation, the proton, in a three-terminal configuration. It has a channel of active material, WO 3 . A solid proton reservoir layer, PdH x , also serves as the gate terminal. A proton conducting solid electrolyte separates the channel and the reservoir. By protonation/deprotonation, we modulate the electronic conductivity of the channel over seven orders of magnitude, obtaining a continuum of resistance states. Proton intercalation increases the electronic conductivity of WO 3 by increasing both the carrier density and mobility. This switching mechanism offers low energy dissipation, good reversibility, and high symmetry in programming.

36 MATERIALS SCIENCE↗
DOE OSTI2020

The Role of Electron Localization in Covalency and Electrochemical Properties of Lithium-Ion Battery Cathode Materials

Following the fundamental research conducted by J. B. Goodenough, the important role of electron localization induced by elemental substitution is studied. The size and electron negativity of host and substituting ions are two important factors in tuning material properties such as local structure and transition metal (TM) oxygen covalency. However, another factor, electron localization, which is widely studied in catalyst research but largely overlooked for battery materials, deserves systematic studies. A combined investigation using synchrotronbased X-ray spectroscopy and theoretical calculations is carried out on the Li-Co-Mn-O model system in which the substituting cation Mn 4+ , with its 3d 3 electronic structure, is used as a promoter for electron localization. Results indicate that electron localization greatly influences the Co - O bond by making it less covalent, which increases the delithiation voltage. It is also found that during charge/discharge, electron localization tends to make TM K-edge X-ray absorption near edge spectroscopy (XANES) spectra show a more “rigid shift” behavior while electron delocalization makes the XANES exhibit a “shape change.” It clearly explains why the K-edge XANES data of some TM oxides show no “rigid shift” while the nominal valence states changed. This work highlights the importance of electron localization with guidance for XANES interpretation.

25 ENERGY STORAGE↗
DOE OSTI2020

CO Oxidation Mechanisms on CoO x -Pt Thin Films

The reaction of CO and O 2 with submonolayer and multilayer CoO x films on Pt(111), to produce CO 2 , was investigated at room temperature in the mTorr pressure regime. Here, using operando ambient pressure X-ray photoelectron spectroscopy and high pressure scanning tunneling microscopy, as well as density functional theory calculations, we found that the presence of oxygen vacancies in partially oxidized CoO x films significantly enhances the CO oxidation activity to form CO 2 upon exposure to mTorr pressures of CO at room temperature. In contrast, CoO films without O-vacancies are much less active for CO 2 formation at RT, and CO only adsorbed in the form of carbonate species that are stable up to 260 °C. On submonolayer CoO x islands, the carbonates form preferentially at island edges, deactivating the edge sites for CO 2 formation, even while the reaction proceeds inside the islands. These results provide a detailed understanding of CO oxidation pathways on systems where noble metals such as Pt interact with reducible oxides.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Accelerated Cu2O Reduction by Single Pt Atoms at the Metal-Oxide Interface§

The reducibility of metal oxides, when serving as the catalyst support or the active sites themselves, plays an important role in heterogeneous catalytic reactions. Here we present an integrated experimental and theoretical study that reveals how the addition of small amounts of atomically dispersed Pt at the metal/oxide interface dramatically enhances the reducibility of a Cu2O thin film by H2. X-ray photoelectron spectroscopy (XPS) and temperature-programmed desorption (TPD) results reveal that upon oxidation, a PtCu single-atom alloy (SAA) surface is covered by a thin Cu2O film and is therefore unable to dissociate H2. Despite this, in situ studies using ambient pressure (AP) XPS reveal that the presence of a small amount of Pt under the oxide layer can, at the single-atom limit, promote the reduction of Cu2O by H2 at room temperature. We build two density functional theory based surface models to better understand these experimental findings: A Cu2O/Cu(111)-like surface oxide layer, known as the ‘29’ oxide, in which Pt is alloyed into the Cu(111) surface as well as a PtCu SAA. Our calculations suggest that the increased activity is due to the presence of atomically dispersed Pt under the surface oxide layer, which weakens the Cu-O bonds in its immediate vicinity, thus making the interface between subsurface Pt and the surface oxide a nucleation site for the formation of metallic Cu. This initial step in the reduction process results in the presence of surface Pt atoms surrounded by metallic Cu patches, and the Pt atoms become active in H2 dissociation, which consequently accelerates the reduction of the oxide layer. This work demonstrates how isolated Pt atoms at the metal/oxide interface of a Cu-based catalyst accelerate the reduction of the oxide and, therefore, helps maintain the active, reduced state of the catalyst under reaction conditions, as is required for the synthesis of methanol from CO2 hydrogenation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

Interfacial engineering for stabilizing polymer electrolytes with 4V cathodes in lithium metal batteries at elevated temperature

Poly (ethylene oxide) (PEO) polymer electrolytes are promising candidates for next-generation rechargeable lithium batteries. However, the poor interfacial stability between 4 V cathodes and PEO electrolytes impedes their applications in 4 V lithium batteries with high energy density. Here, we demonstrate a facile and effective strategy to enhance the interfacial stability by the synergy of Li 1.5 Al 0.5 Ge 1.5 (PO 4 ) 3 (LAGP) coating on the cathode surface, and salt combination in the electrolyte, even with a cut-off voltage of 4.25–4.4 V vs. Li + /Li. Nano-LAGP coated Li|PEO|LiCoO 2 cell delivers stable cycling with a capacity retention of 81.9%/400 cycles and 84.7%/200 cycles at 60 °C when charged to 4.25 and 4.3 V in pure polyether electrolyte, respectively. Steady cycling is also demonstrated at room temperature and with LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NCM523) cathode. This work offers a viable and scalable approach to improve the stability between PEO electrolytes and 4 V cathodes and open up new possibilities for practical application of 4 V lithium metal batteries.

25 ENERGY STORAGE↗