Wang, Haotian — Page 2

DOE OSTI2020

Can N95 Respirators Be Reused after Disinfection? How Many Times?

The coronavirus disease 2019 (COVID-19) pandemic has led to a major shortage of N95 respirators, which are essential for protecting healthcare professionals and the general public who may come into contact with the virus. Thus, it is essential to determine how we can reuse respirators and other personal protective equipment in these urgent times. We investigated multiple commonly used disinfection schemes on media with particle filtration efficiency of 95%. Heating was recently found to inactivate the virus in solution within 5 min at 70 °C and is among the most scalable, user-friendly methods for viral disinfection. We found that heat (≤85 °C) under various humidities (≤100% relative humidity, RH) was the most promising, nondestructive method for the preservation of filtration properties in meltblown fabrics as well as N95-grade respirators. At 85 °C, 30% RH, we were able to perform 50 cycles of heat treatment without significant changes in the filtration efficiency. At low humidity or dry conditions, temperatures up to 100 °C were not found to alter the filtration efficiency significantly within 20 cycles of treatment. Ultraviolet (UV) irradiation was a secondary choice, which was able to withstand 10 cycles of treatment and showed small degradation by 20 cycles. However, UV can potentially impact the material strength and subsequent sealing of respirators. Finally, treatments involving liquids and vapors require caution, as steam, alcohol, and household bleach all may lead to degradation of the filtration efficiency, leaving the user vulnerable to the viral aerosols.

60 APPLIED LIFE SCIENCES↗

DOE OSTI2020

Organic-Inorganic Reaction of Li-Containing thin film: Structure of Lithium Propane Dioxide via MLD

In combining organometallic with organic precursors, molecular layer deposition (MLD) offers not only an expanded portfolio of molecular combinations but specifically the possibility of tuning mechanical properties for more robust functionality. This is appealing for applications in energy storage, where ion transport in and out of electrodes causes significant stress/strain cycling. It is particularly opportune for Li-ion solid state batteries (LISSBs), where electrode and solid electrolyte structures are usually arranged densely for high power and energy. Despite diverse MLD applications to date, little prior research has been aimed at Li-containing MLD materials and processes. Here, we report the MLD growth and process for a lithium-containing organic thin film using lithium tert-butoxide (LiO t Bu) and 1,3-propanediol, leading to an MLD film of lithium propane dioxide, Li 2 O 2 C 3 H 6 (LPDO), identified through X-ray photoelectron spectroscopy (XPS) and ab initio calculations. The growth showed self-limiting behavior for both precursors, with significant nucleation delay before linear growth at 0.23 Å/cycle at 150 °C, and 0.15 Å/cycle at 200 °C. XPS-determined stoichiometry was Li 1.6 O 2.2 C 3 H 6 at both 150 and 200 °C, while additional species, presumably from incomplete reaction, were found at 100 °C, leading to a notably higher (0.84 Å/cycle) growth rate. The LPDO film showed crystallinity and high surface roughness when grown on the crystalline substrate, while on the amorphous substrate, an amorphous LPDO film with low surface roughness was observed. In addition, high air sensitivity of LPDO film was observed, with Li propyl carbonate and Li carbonate formation under air exposure. Further modification strategies were proposed in order to achieve a MLD or atomic layer deposition-/MLD-based solid electrolyte material.

25 ENERGY STORAGE↗