Mechanical response of HFIR-irradiated M5FRAMATOME cladding under simple and complex loading conditions

This study investigates the mechanical behavior of High Flux Isotope Reactor (HFIR) irradiated M5FRAMATOME cladding under simple and complex loading conditions through axial tensile and reversible cyclic bending. Axial tension specimens were pre-machined prior to HFIR irradiation while cyclic bend specimens were inserted as intact tubes. Tests articles were neutron-irradiated to 4 and 16 dpa, and specimens were tested at ORNL's hotcell facilities. The axial tension tests were conducted under constant displacement control, and the reversible cyclic bend tests were performed using ORNL's Cyclic Integrated Reversible-Bending Fatigue Tester (CIRFT) apparatus. Results showed that mechanical response of Cr-coated and uncoated M5FRAMATOME cladding were similar and independent of irradiation dose for axial tension tests, while Cr-coated specimens’ reversible cyclic bend behavior differed from uncoated counterparts. For all tests, irradiation temperature showed a significant impact on the mechanical behavior. Below 280°C, all axial tensile specimens whether coated or not behaved similarly. Above 280°C, YS and UTS showed decrease with increasing irradiation temperature. A similar behavior was also observed in cyclic bend tests as well. The mechanical damage during cyclic bend tests was linked to damage accumulation in unirradiated Cr-coated zircaloy-4 specimens, and the effect of irradiation temperature was related to changing characteristics of defect mobility during high temperature irradiation.

Cinbiz, Nedim [ORNL] (ORCID:0000000346268515)↗
DOE OSTI2025

Effect of Transverse Compression on the Dielectric Breakdown of Power Cable with Ethylene Propylene Rubber Insulation

Understanding of the failure mechanisms of submarine dynamic power cables (SDPC) is critical for innovative design to meet the 2035 cost reduction target of U.S. DOE Floating Offshore Wind Shot. This is important because the current design suffers a significant failure rate in the field. This project explored a multiphysics approach and conducted systematic electro-thermo-mechanical (ETM) experimental study on the power cores extracted from a 15 kV power cable. The power cable had three cores of copper conductor and ethylene propylene rubber (EPR) insulation. An ETM testing system with transverse compression capability was developed. Mechanical loading induced dielectric breakdown. Increasing temperature from room temperature (RT, 22 degrees Celsius) to 90 degrees Celsius resulted in the 67% decrease in the failure mechanical load as defined by the dielectric breakdown. With the same temperature rise, the creep mechanical load was reduced by 70% at a given dielectric breakdown time. The post-test measurement revealed an impressive recovery of electrical resistance, although the dielectric breakdown occurred in the ETM test that would not be captured without the use of ETM testing.