1.7-kV vertical GaN p-n diode with triple-zone graded junction termination extension formed by ion-implantation
Not Available
Duan, Yu (ORCID:0000000299333141)↗
Engineering topics
Wang, Jingshan
Publications and source records attributed to Wang, Jingshan.
Edge termination in vertical GaN diodes: Electric field distribution probed by second harmonic generation
We characterized the electric field distribution of GaN-on-GaN p–n diodes with partially compensated ion-implanted edge termination (ET) using an electric field induced second harmonic generation technique (EFISHG). The distributed electric field from the anode to the outer edge of the ET demonstrates the effectiveness of the ET structure. However, EFISHG also shows that its effectiveness is strongly dependent on the acceptor charge distribution in the ET's partially compensated layer (PC). A generally lower amount of acceptor charge can be inferred from the measured electric field distribution resulting from excessive ion implantation energy or dose during ET fabrication and causing lower than optimal breakdown voltage. Localized field crowding can be observed when the remaining acceptors uncompensated by the implant in the PC layer are nonuniformly distributed around the periphery of the devices. Important information can be obtained from these direct electric field measurements and used for optimizing the device design and fabrication process.
Cao, Yuke↗
Connection between Carbon Incorporation and Growth Rate for GaN Epitaxial Layers Prepared by OMVPE
Carbon, a compensator in GaN, is an inherent part of the organometallic vapor phase epitaxy (OMVPE) environment due to the use of organometallic sources. In this study, the impact of growth conditions are explored on the incorporation of carbon in GaN prepared via OMVPE on pseudo-bulk GaN wafers (in several cases, identical growths were performed on GaN-on-Al2O3 templates for comparison purposes). Growth conditions with different growth efficiencies but identical ammonia molar flows, when normalized for growth rate, resulted in identical carbon incorporation. It is concluded that only trimethylgallium which contributes to growth of the GaN layer contributes to carbon incorporation. Carbon incorporation was found to decrease proportionally with increasing ammonia molar flow, when normalized for growth rate. Ammonia molar flow divided by growth rate is proposed as a reactor independent predictor of carbon incorporation as opposed to the often-reported input V/III ratio. A low carbon concentration of 7.3 × 1014 atoms/cm3 (prepared at a growth rate of 0.57 µm/h) was obtained by optimizing growth conditions for GaN grown on pseudo-bulk GaN substrates.
Ciarkowski, Timothy (ORCID:0000000309896053)↗