DOE OSTI2021

High-speed synchrotron X-ray phase-contrast imaging for evaluating microscale damage mechanisms and tracking cracking behaviors inside cross-ply GFRCs

In this study, we integrated the high-speed synchrotron X-ray phase-contrast imaging (PCI) with a modified Kolsky compression bar loading platform to visualize the dynamic failure processes of cross-ply glass fiber reinforced composites (GFRCs). Four S-2 glass/SC-15 composite specimens were prepared, having similar thicknesses but different stacking sequences, namely as [0 12 /90 12 ], [90 12 /0 12 ], [0 8 /90 8 /0 8 ], and [90 8 /0 8 /90 8 ]. Three-dimensional synchrotron X-ray computed tomography and scanning electron microscopy (SEM) were employed to examine the microstructures and quantify the fiber volume fractions. Each specimen was notched and subjected to a dynamic three-point flexural loading. The onset of cracking close to the notch tip, crack propagation in 0° or 90° plies and their interface, crack opening, and ultimately failure of the specimen were captured by high-speed synchrotron X-ray PCI. Additional dynamic experiments were performed to determine the average time when the stress wave propagated through the specimen and correlate the X-ray images with the specimen's force-deflection response. Finally, the surface morphology of each specimen after the dynamic loading was imaged by SEM. Comparison between real-time X-ray images and post-fracture SEM images demonstrated the capability of the X-ray method to record damage evolution inside composites. Furthermore, the high spatial and temporal resolutions of the X-ray setup and edge enhancement by PCI enabled the identification of microscale damage features within 1 μs. Two damaging processes were identified, crack growth was quantified, and fracture toughness of the composites was evaluated. The method is deemed useful to reveal microscale damage mechanisms and track cracking behaviors inside cross-ply GFRCs under dynamic loading in real time.

42 ENGINEERING↗

DOE OSTI2021

Transverse impact by RCCs on S-glass and Kevlar® FRC strips

This study aims to isolate interactions between plies and tows and reveal fundamental physics involved in transverse impact on fiber-reinforced composite (FRC) structures. Composite strips were sectioned from large panels and characterized by optical photography, three-dimensional synchrotron X-ray computed tomography, and scanning electron microscopy (SEM). Each strip was impacted perpendicularly by a right circular cylinder (RCC) projectile at a velocity ranging from ~ 150 to 600 m/s. The global strip behavior, as well as localized deformation and failure of the strip near the projectile corner, were both captured by high-speed optical imaging. S-Glass FRC strips were observed to fail in tension ahead of the RCC projectiles’ flat surfaces while Kevlar® FRC strips fractured at the projectile corners. The concept of critical velocity region previously used for impact on yarns was introduced to define different failure modes of each composite strip type. The strip damage extent was found to increase with the impact velocity and reach the maximum at the upper limit of the critical velocity region. Above the critical velocity region, the damage extent decreased with impact velocity. Wave propagations and load histories in the composite strips during impact were quantified and compared with Smith’s theory. Finally, critical velocities of single fibers, yarns, and composite strips and ballistic limits of single-ply and multi-ply composite panels were compared to provide insight into the design of impact-resistant fabrics and composites.

42 ENGINEERING↗

DOE OSTI2020

Real-time damage characterization for GFRCs using high-speed synchrotron X-ray phase contrast imaging

Here, we report the application of high-speed synchrotron X-ray phase contrast imaging (PCI) in real-time damage characterization for glass fiber reinforced composites (GFRCs) subjected to dynamic loading. Dynamic single-edge notched bending (DSENB) experiments on pre-notched S-2 GFRCs were performed on a modified Kolsky compression bar. During loading, the synchrotron X-ray beam penetrated through the composite specimen from the side to detect damage evolution inside the material. Entire dynamic events were recorded by a high-speed camera as image sequences.0° and 90° unidirectional and cross-ply composites were investigated. An optical imaging technique was also employed to capture similar dynamic events in comparison with the radiographic imaging. It is demonstrated that high-speed X-ray PCI had sufficient phase contrast to characterize a crack initiation at a 20-μm spatial resolution within 920 ns and track the crack geometry during propagation, thereby providing reliable data to quantify the dynamic damage resistance of GFRCs. Furthermore, being capable of recognizing microscopic damage-related features at a sub-10-μm resolution, high-speed X-ray PCI provided fundamental material failure mechanisms to reveal the essential of macroscale structural failure of composites. It can also track the damage evolution inside and between individual plies of laminated composites. However, current high-speed X-ray PCI technique only supports in-situ observation and the high timing and spatial resolutions are limited within a field of view of ~2.5 mm in square, preventing its application in the three-dimensional and larger-area damage detection for GFRC structures.

42 ENGINEERING↗

DOE OSTI2020

A method for characterization of multiple dynamic constitutive parameters of FRCs

We propose a method to measure multiple dynamic material constitutive parameters of unidirectional fiber reinforced composites (FRCs) in a single experiment. Dynamic short-beam shear (DSBS) experiments were performed on a modified Kolsky compression bar, with integration of high-speed imaging and digital image correlation (DIC). The unidirectional FRCs investigated were S-2 glass fiber reinforced matrix of TGDDM-Jeffamine® D230 with monoamine functionalized partially reacted substructures (mPRS) and commercially available SC-15. Analytical solutions of normal and shear strains of a composite beam were derived based on Timoshenko beam theory, assuming material to be transversely isotropic and have different moduli in tension and compression in each principle material orientation. Tensile and compressive moduli were inversely computed through monitoring normal strain slope when specimen was constantly loaded at a speed of ~7.3 m/s within a small deflection. Non-linear shear stress-strain behavior of the composite was described via Ramberg–Osgood equation. Finite element (FE) analysis was conducted in ABAQUS, simultaneously defining via user subroutine UMAT the transverse isotropy of material, bi-modulus constitutive model, and non-linear shear stress-strain relation. The method proposed in this work was validated by comparing strain distributions computed by FE model and DIC measurements. Comparing with traditional dynamic tensile, compressive, and shear experiments on FRCs, this method significantly simplifies the specimen preparation and design of complicated gripping fixtures for multiple experiments. Here, systematic errors resulting from variations of specimen geometry and dimension, loading direction, and instrumentation are reduced, thereby providing compatible data for numerical studies on impact behavior of composites.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Lead-Free Cs 4 CuSb 2 Cl 12 Layered Double Perovskite Nanocrystals

Concerns about the toxicity of lead-based perovskites have aroused great interest for the development of alternative lead-free perovskite-type materials. Recently, theoretical calculations predict that Pb 2+ cations can be substituted by a combination of Cu 2+ and Sb 3+ cations to form a vacancy-ordered layered double perovskite structure with superior optoelectronic properties. However, accessibilities to this class of perovskite-type materials remain inadequate, hindering their practical implementations in various applications. Here, we report the first colloidal synthesis of Cs 4 CuSb 2 Cl 12 perovskite-type nanocrystals (NCs). The resulting NCs exhibit a layered double perovskite structure with ordered vacancies and a direct bandgap of 1.79 eV. A composition-structure-property relationship has been established by investigating a series of Cs 4 Cu x Ag 2-2x Sb 2 Cl 12 perovskite-type NCs (0 ≤ x ≤ 1). The composition-induced crystal structure transformation, thus the electronic bandgap evolution has been explored by experimental observations and further confirmed by theoretical calculations. Taking advantages of both the unique electronic structure and solution processability, we demonstrate that the Cs 4 CuSb 2 Cl 12 NCs can be solution-processed as high-speed photodetectors with ultrafast photo-response and narrow bandwidth. We anticipate that our study will prompt future research to design and fabricate novel and high-performance lead-free perovskite-type NCs for a range of applications.

25 ENERGY STORAGE↗