DOE OSTI2024

Sister Rod Destructive Examinations (FY23) Appendix F: Cyclic Integrated Reversible-Bending Fatigue Tests

Spent nuclear fuel (SNF) assemblies must be shipped to other sites for processing and disposal. During shipment, the fuel is typically oriented horizontally, and the fuel rods are subject to periodic alternating loads related to the movement of the vehicle that results in alternating bending of the SNF fuel rods. The number of bending cycles is related to the length of the shipping route, with longer routes producing more cycles. Because it is well-known that cyclic loads can produce failures, even when the stress and strain imposed are below the material’s yield point, investigation of the SNF’s fatigue behavior is prudent. This report discusses the results of fatigue testing conducted at Oak Ridge National Laboratory (ORNL) using the Cyclic Integrated Reversible-Bending Fatigue Tester (CIRFT) created by the US Department of Energy Office of Nuclear Energy for the High Burnup Spent Fuel Data Project and its sister rods. The results of the tests are compared with results obtained over the last decade using the same CIRFT for the US Nuclear Regulatory Commission (NRC).

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Foam Fracturing Study for Stimulation Development of Enhanced Geothermal Systems

The large thermal gradients and high subsurface temperatures of the western region of the U.S. hold great potential for the implementation of enhanced geothermal systems (EGS). The development of these potential EGS resources requires stimulation of the reservoir to enhance permeability and it has been widely reported that a substantial amount of water will be required should conventional hydraulic stimulation be used. This presents a huge challenge and a high risk to the geothermal development because the water stress1 in these areas is already high or extremely high. The use of foam, a gas/liquid mixture predominantly composed of gas, in fracturing is considered and explored in this project as a potential approach to address water concerns with hydraulic stimulation in the development of EGS. This project, led by Oak Ridge National Laboratory (ORNL) in collaboration with Temple University, was awarded in an open lab call in 2018, and was part of the DOE GTO waterless stimulation initiative. The goal of the project was to demonstrate the feasibility of foam fracturing for EGS development through two primary tasks: Task 1: Laboratory study of the effectiveness of foam fracturing for representative geological materials, including cyclic pressurization using foam (led by ORNL) and Task 2: High temperature foam material selection and characterization (led by Temple University). In FY19, ORNL finished the critical review on serval issues associated with foam fracturing and the implementation of the proposed tasks in a lab study (Wang, et al., 2019), and completed the foam fracturing testing using cement as a model material (Wang, et al, 2020a). The work at ORNL was geared up to develop a brand-new foam testing system in FY20. The purchase of main components for the new system was finished in the first half of the FY20. The assembly of the foam testing system and foam fracturing testing were completed in the second half of the FY20 (Wang, et al., 2021a). Task 1 required the development of a test system which can be used to perform hydraulic fracturing of geological specimens with both water and foamed liquids at pressure up to 6,000 psi (41.4 MPa). The system possesses several capabilities that conventional injection systems lack for hydraulic fracturing. In addition to its ability to generate foam with controlled quality, it is capable of cycling pressure levels between specified values up to frequencies of 50 Hz. The latter capability was developed to evaluate the hypothesis that cyclic loading of samples would produce enhanced fracturing. The system consists of two sections: one for foam generation and another for foam injection. The foam is generated through separate control and pressurization of liquid and gas phases with controlled flow rates. The injection section is equipped with a low-flow Coriolis flow that monitors the density of foam to ensure the injection is in the range of target foam quality2. Experimental results of foam fracturing are reported for cylindrical granite specimens using water and aqueous N2 foam as the fracturing fluids. All experiments were performed for unconfined conditions. The effects of injection mode (i.e., monotonic vs cyclic pressurization) on breakdown pressure and failure response sample were investigated using water alone as a fracturing fluid and foams with a range of compositions. It was found that in the case of monotonic injection, the breakdown pressure of granite specimens tended to be slightly higher when fracturing with foam. Additionally, with a foam quality of 90%, the water use can be reduced by 50 to 84%, depending on hole size. On the other hand, it was observed that the breakdown pressure can be brought down to 70% of the monotonic breakdown pressure by using low cycle fatigue. Finally, discussions are presented regarding injectivity and water use reduction.

15 GEOTHERMAL ENERGY↗

DOE OSTI2022

Sister Rod Destructive Examinations (FY2021) Appendix F: Cyclic Integrated Reversible-Bending Fatigue Tests

As a part of DOE NE High Burnup Spent Fuel Data Project, Oak Ridge National Laboratory (ORNL) is performing destructive examinations (DEs) of high burnup (HBU) (>45 GWd/MTU) spent nuclear fuel (SNF) rods from the North Anna Nuclear Power Station operated by Dominion Energy. The SNF rods, called sister rods or sibling rods, are all HBU and include four different kinds of fuel rod cladding: standard Zircaloy-4 (Zirc-4), low-tin (LT) Zirc-4, ZIRLO, and M5. This appendix documents the status of the ORNL Phase 1 DE activities related to tests of the sister rods using the Cyclic Integrated Reversible-Bending Fatigue Tester (CIRFT) in Phase 1 of the sister rod test program.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

High Temperature, High Pressure Stability of Aqueous Foams for Potential Application in Enhanced Geothermal System (EGS)

Enhanced Geothermal Systems (EGS) are typically constructed by injecting high-pressure water into deep hot dry rocks (HDR) under carefully controlled conditions to create new or re-open existing fractures, which usually uses an immense quantity of water. In lieu, a more sustainable technique is to utilize aqueous foams as fracturing fluid to reduce water consumption and waste-water treatments of conventional hydraulic fracturing. Although foam-based fracturing has shown promising results in oil and gas industries, its feasibility is not demonstrated in EGS conditions that usually involve high temperature and high pressures. One potential barrier of utilizing foams in EGS applications is that foams are thermodynamically unstable and will become more unstable with increasing temperature due to liquid drainage, bubble coarsening, and coalescence. This work focuses on evaluation of the stability of selected aqueous foams under high-temperature and high-pressure conditions. Specifically, foams generated with surfactant alfa olefin sulfonate (AOS) were studied at temperature up to 200oC, while the pressure ranged between 100 psi and 1000 psi. The effect of additional stabilizing agents was also examined, including guar gum, bentonite clay, borate salt crosslinker, silicon dioxide nanoparticles (SiO2), and graphene oxide (GO) dispersion. Results showed that the stabilizing agents can enhance the foam thermal stability. Foams made with AOS and the borate salt crosslinker exhibited the longest half-life of 20 min at 200°C when the pressure was at 1000 psi. Data fitting showed that foam stability decreased exponentially as temperature increased. On the other hand, pressure increased the foam half-life which followed a power model. This study indicates that it may be possible to obtain highly stable foams at high-temperature and high-pressure conditions with appropriate stabilizing agents.

Thakore, Viren↗

DOE OSTI2021

Data Processing Package for Cyclic Integrated Reversible Bending Fatigue Testing

A data processing software package has been introduced. The package was developed using MATLAB with the aid of the Curve Fitting Toolbox. The package is made up of four modules: pre-processing, data processing for static testing, data processing for monitoring, and data processing for measurements. CIRFT data are structured with multiple levels of architecture involving group, specimen, session, and scan/block. The degree of complexity of the data structure depends on whether a test is static or cyclic.The test results are presented in figures, scatter plots, and tables. For static testing, the output in tables provides bending mechanical properties and characteristic points of moment–curvature relation: flexural rigidities in linear segments of loading and unloading stages, intersection points between characteristic segments of the curve, and equivalent stress and strain quantities. For cyclic testing, the table output lists control and fatigue life and responsive/dependent quantities including moment, curvature, flexural rigidity, flexural hysteresis, rigidity phase angle, and equivalent stresses and strains. In addition, derivatives such as half-gage length and sensor spacing correction are included. The output also provides standard deviations of the reported quantities when they are applicable or available. The data processing package can serve as a fundamental characterization tool in mechanical study of materials. The package is intended primarily for data processing for the CIRFT process and can also be used in applications for which similar testing requirements exist.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Neutron diffraction illustrates residual stress behavior of welded alloys used as radioactive confinement boundary

Corrosion-resistant welded alloys are frequently used as a leak-tight boundary in critical applications that require confinement of hazardous and/or radioactive substances, including an increasing population of spent nuclear fuel (SNF) canisters. The behavior of residual stresses generated as a result of irregular elastic–plastic deformation during processes such as welding is one of today's key issues to a full understanding of the aging mechanisms that may compromise the confinement boundary. Whether such processes and any subsequent weld repairs, not subjected to post-weld heat treatment, would negatively affect the initial material by introducing through-thickness tensile stresses remains an open question. Here we report the first residual stress measurements using neutron diffraction on the welded joints of a SNF canister. We found significant tensile residual stresses in the as welded sample, indicating that initiation and through-thickness growth of cracks may be possible. Following repair, we observed a stress redistribution and introduction of beneficial compressive stresses. We anticipate our results will improve understanding of confinement susceptibility to aging and guide improvements in repair techniques.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Fatigue Test Result for High Burnup Pressurized Water Reactor Rods

The High Burnup Spent Fuel Data Project, sponsored by DOE-NE, is focused on understanding the effects of long-term storage and transportation on high burnup (HBU) (>45 gigawatt days per metric ton uranium) light water reactor fuel. The experiment includes 32 HBU spent nuclear fuel (SNF) assemblies that will be stored in a typical Independent Spent Fuel Storage Installation (ISFSI) and 25 sister rods - nine SNF rods that were removed from the fuel assemblies prior to insertion to the ISFSI and 16 SNF rods removed from similar HBU assemblies. The sister rods provide a baseline of the condition of the HBU rods prior to loading, drying, and long-term dry storage. Destructive examinations of the sister rods are focused on understanding overall SNF rod strength and durability. Both composite fuel and empty cladding will be tested to derive material properties. While the data generated can be used for multiple purposes, a primary goal of the sister rod PIE data and associated measured mechanical properties is to support existing fuel storage licensing and relicensing activities by addressing identified knowledge gaps, and enhance the technical basis for post-storage transportation, handling, and consolidation activities. Fatigue tests of HBU M5-clad, ZIRLO-clad, Zircaloy-4, and low tin Zircaloy-4 segments have been completed using ORNL’s Cyclic Integral Reversible Fatigue Tester (CIRFT). This is the first time ZIRLO-clad rods have been tested. Some of the segments were heat-treated to understand the effects of thermal transients such as those encountered during dry storage vacuum drying on the fatigue lifetime. This paper presents results of the fatigue tests obtained to date and discusses planned future tests.

Montgomery, Rose↗

DOE OSTI2021

Drop impact tester development for spent nuclear fuel vibration integrity study

The accumulated damage of SNF rod is defined as the integrated damage induced by the SNF assembly harmonic vibrations and SNF assembly & cask system contact interactions induced transient shocks, experienced by SNF rods during normal conditions of transportation (NCT). The CIRFT technology has provided means to resolve/understand the SNF rod harmonic vibration reliability issues associated with maximum axial clad tubing stress induced by SNF inertia related dynamic bending loading. However, the SNF rod integrity in association with the transient shock loads during NCT through dynamic contact interactions among SNF assembly cannot be investigated systematically through CIRFT technology alone. Thus, the proposed drop impact tester development become a viable tool for SNF system transient shock effect investigation. Furthermore, the transient shocks induced loading mode is normally perpendicular to the SNF rod axial orientation, i.e., in a transverse orientation to the SNF rod. To proceed with such loading mode investigation, a new device, “SNF Drop Impact Tester” that provides the transverse impact shock load onto a SNF rod through a free-drop projectile was developed in FY20 for SNF System Vibration Reliability Investigation; where the SNF system contact impact intensity can be calibrated accordingly with projectile weight and projectile head geometry. This newly developed research tool can further provide a detailed understanding about the effect of dynamic contact-interaction loadings; and combined harmonic vibration and transient shock loading modes on the fatigue damage evolution of the HBU SNF under NCT.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Fracture toughness evaluations for spent nuclear fuel dry storage canister welds and spent nuclear fuel clad-pellet structures

Integrity of spent nuclear fuel (SNF) interim storage canisters is very important to the safety of the back-end nuclear fuel cycle. Stress corrosion cracking (SCC) potential of interim storage canister has been considered as a high priority. Because no post-weld heat treatment was required for forming these canisters, the high tensile residual stress existed within these canister welds. This can change the fracture resistance capacity significantly as well as increase SCC potential. Due to relative thin shell thickness of a canister weldment, the spiral notch torsion test (SNTT) method was used to estimate the canister weldment fracture toughness. SNTT was developed to measure the intrinsic fracture toughness of structural materials using small specimens. The SNTT method has been applied to a wide variety of structural materials, such as low-alloy steels, stainless steel, aluminum alloy, ceramics, concrete, and composites. The SNTT system operates by applying pure torsion to cylindrical specimens with a notch line that spirals around the specimen at a 45° pitch. In order to carry out pure torsion load mode, biaxial tension/torsion tester was developed accordingly to perform SNTT protocol. Moreover, applying fracture mechanics approach to SNF system reliability investigation is warranted due to the inherent flaws and hydride structures existed in a SNF system after nuclear reactor operation. However, none of the existing fracture toughness data deal with fuel cladding specific geometry or spent fuel material conditions, such as cladding structure with the pellet-inserts and the associated pellet clad mechanical interactions induced mixed-mode damage mechanisms. Thus, the development of an intrinsic fracture mechanics approach that is suitable for SNF materials is needed. Furthermore, due to thin wall and small dimension of clad tubing structure, the SNTT method was used to estimate the clad tubing structure fracture toughness. Fracture testing were performed on the received stainless steel canister weldment, most SNTT weld samples fracture initiation sites are at heat-affected zone (HAZ) regions. The estimated fracture toughness J Q ’ for the baseline SS304 steel is at 283 kJ/m². The estimated JQ’ for the SS304/308 weld and baseline metals are 148 kJ/m 2 and 459 kJ/m 2 , respectively. Out of cell fracture testing for spent fuel structure were carried out on the surrogate rods made of Zr-4 clad and alumina inserts, the estimated fracture toughness values for baseline Zr-4 cladding with alumina-pellet inserts are: (1) For SNTT samples with a short or medium crack length, between 5.4-mm and 8-mm, the estimate J IQ upon fracture initiation for the baseline Zr-4 cladding is at 50 kJ/m 2 with 2-sigma uncertainty of 3.26 kJ/m 2 , and the associated K IQ is at 67.46 MPa$\sqrt{m}$; and (2) For SNTT samples with a long crack length, around 13-mm, the crack initialization is deviated from that of the Mode-I tensile fracture and appears to be a mixed-mode fracture of Mode I - tensile stress and Mode III - out of plane shear stress; the estimated J MQ is at 18.9 kJ/m 2 , the associated K MQ is at 41.4 MPa$\sqrt{m}$.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

High Temperature Stability of Aqueous Foams for Potential Application in Enhanced Geothermal System (EGS)

Enhanced Geothermal Systems (EGS) are typically constructed by injecting high-pressure water into the deep hot dry rocks (HDR) under carefully controlled conditions to create new or re-open existing fractures, which usually utilizes an immense quantity of water. Alternatively, aqueous foam-based fracturing fluids may offer potential advantages over conventional water-based fracturing fluid, including reduced consumption of water and environmental impact. Although foam-based fracturing has shown promising results in oil and gas industries, its applicability to EGS is unknown. Foams are complex mixtures of liquids with gaseous phases that are thermodynamically unstable. Their stability will decrease over time due to liquid drainage, bubble coarsening, and coalescence. Therefore, it is essential to stabilize foam fluids at high temperatures for EGS related applications such as fracking of HDRs.This paper is focused on investigating high-temperature stability of N2-in-water or N2 foams containing different surfactants and stabilizing agents. Foam stability was characterized by the half-life, which is defined as the time a foam decreases to 50% of its original height due to drainage. Surfactants with various concentrations dissolved in deionized water were investigated, including alfa olefin sulfonate (AOS), sodium dodecyl sulfonate (SDS), TergitolTM (NP – 40), and cetyltrimethylammonium chloride (CTAC). Also, the effects of other stabilizing agents, including guar gum, bentonite clay, crosslinker, graphene oxide (GO) dispersion on foam stability were tested. Initial results showed that foam stability decreased dramatically as temperature increased. On the other hand, foams became relatively more stable as pressure increased. Certain stabilizing agents, such as guar gum and crosslinker, can enhance foam stability at a wide range of temperatures. Our results indicate that it may be possible to obtain stable foams at high-temperature, high-pressure conditions with appropriate stabilizing agents.

Thakore, Virensinh↗

DOE OSTI2021

Study on Foam Fracturing of Granite for the Development of Enhanced Geothermal Systems

Foam fracturing has been considered as a potential technical approach to address water concerns with hydraulic stimulation in the development of enhanced geothermal systems (EGS). This paper reports the recent progress of a project sponsored by the U.S. DOE GTO Waterless Stimulation Initiative. The project investigates the foam fracturing as an alternative approach to the hydraulic fracturing. The paper describes the development of foam fracturing testing system at Oak Ridge National Laboratory (ORNL). The system can be used to perform the hydraulic fracturing of rock-like materials with both water and foamed fluids under pressure to 6,000 psi (41.4 MPa). The system features the sections of foam generation and foam injection and has the capability of testing materials in both monotonic and cyclic injection modes.Experimental results of foam fracturing on Charcoal Black granite will be reported. Cylindrical granite specimens with a blind hole were studied along with water and nitrogen-gas-in-water foam as the fracturing fluids. The effects of fracturing fluids and injection modes on the breakdown pressure and failure responses of the material were examined. The observations from the experimental work and the implications to the EGS application will be presented and discussed.

Wang, Hong↗