NASA NTRS2009

Evaluation of Margins of Safety in Brazed Joints

One of the essential steps in assuring reliable performance of high cost critical brazed structures is the assessment of the Margin of Safety (MS) of the brazed joints. In many cases the experimental determination of the failure loads by destructive testing of the brazed assembly is not practical and cost prohibitive. In such cases the evaluation of the MS is performed analytically by comparing the maximum design loads with the allowable ones and incorporating various safety or knock down factors imposed by the customer. Unfortunately, an industry standard methodology for the design and analysis of brazed joints has not been developed. This paper provides an example of an approach that was used to analyze an AlBeMet 162 (38%Be-62%Al) structure brazed with the AWS BAlSi-4 (Al-12%Si) filler metal. A practical and conservative interaction equation combining shear and tensile allowables was developed and validated to evaluate an acceptable (safe) combination of tensile and shear stresses acting in the brazed joint. These allowables are obtained from testing of standard tensile and lap shear brazed specimens. The proposed equation enables the assessment of the load carrying capability of complex brazed joints subjected to multi-axial loading.

Flom, Yury↗

NASA NTRS2003

Flaw Tolerance In Lap Shear Brazed Joints

This paper presents results of the second part of an on-going effort to gain better understanding of defect tolerance in braze joints. In the first part of this three-part series, we mechanically tested and modeled the strength of the lap joints as a function of the overlap distance. A failure criterion was established based on the zone damage theory, which predicts the dependence of the lap joint shear strength on the overlap distance, based on the critical size of a finite damage zone or an overloaded region in the joint. In this second part of the study, we experimentally verified the applicability of the damage zone criterion on prediction of the shear strength of the lap joint and introduced controlled flaws into the lap joints. The purpose of the study was to evaluate the lap joint strength as a function of flaw size and its location through mechanical testing and nonlinear finite element analysis (FEA) employing damage zone criterion for definition of failure. The results obtained from the second part of the investigation confirmed that the failure of the ductile lap shear brazed joints occurs when the damage zone reaches approximately 10% of the overlap width. The same failure criterion was applicable to the lap joints containing flaws.

Wang, Len↗

NASA NTRS1999

Teflon FEP Analyzed After Retrieval From the Hubble Space Telescope

During the Hubble Space Telescope (HST) Second Servicing Mission, 6.8 years after the telescope was deployed in low Earth orbit, degradation of unsupported Teflon FEP (DuPont; fluorinated ethylene propylene), used as the outer layer of the multilayer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer (see the photograph) was retrieved during the second servicing mission and returned to Earth for ground testing and evaluation. Also retrieved was a Teflon FEP radiator surface from a cryogen vent cover that was exposed to the space environment on the aft bulkhead of the HST. NASA Goddard Space Flight Center directed the efforts of the Hubble Space Telescope MLI Failure Review Board, whose goals included determining the FEP degradation mechanisms. As part of the investigations into the degradation mechanisms, specimens retrieved from the first and second HST servicing missions, 3.6 and 6.8 years after launch, respectively, were characterized through exhaustive mechanical, optical, and chemical testing. Testing led by Goddard included scanning electron microscopy, optical microscopy, tensile testing, solar absorptance measurements, time-of-flight secondary ion mass spectroscopy (TOF-SIMS), Fourier transform infrared microscopy (m-FTIR), attenuated total reflectance infrared microscopy (ATR/FTIR), and x-ray diffraction (XRD). The NASA Lewis Research Center contributed significantly to the analysis of the retrieved HST materials by leading efforts and providing results of bend testing, surface microhardness measurements, x-ray photoelectron spectroscopy, solid-state nuclear magnetic resonance spectroscopy, and density measurements. Other testing was conducted by Nano Instruments, Inc., and the University of Akron.

Dever, Joyce A.↗