Boosting Reversibility of Mn-Based Tunnel-Structured Cathode Materials for Sodium-Ion Batteries by Magnesium Substitution
Explore the source record for details and available documents.
Engineering topics
Publications and source records attributed to Wang, Qin‐Chao.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Oxygen-redox of layer-structured metal-oxide cathodes has drawn great attention as an effective approach to break through the bottleneck of their capacity limit. However, reversible oxygen-redox can only be obtained in the high-voltage region (usually over 3.5 V) in current metal-oxide cathodes. Here, we realize reversible oxygen-redox in a wide voltage range of 1.5-4.5 V in a P2-layered Na 0.7 Mg 0.2 [Fe 0.2 Mn 0.6 $\square$0.2]O 2 cathode material, where intrinsic vacancies are located in transition-metal (TM) sites and Mg-ions are located in Na sites. Mg-ions in the Na layer serve as "pillars" to stabilize the layered structure during electrochemical cycling, especially in the high-voltage region. Intrinsic vacancies in the TM layer create the local configurations of "$\square$-O-$\square$", "Na-O-$\square$" and "Mg-O-$\square$" to trigger oxygen-redox in the whole voltage range of charge-discharge. Additionally, time-resolved techniques demonstrate that the P2 phase is well maintained in a wide potential window range of 1.5-4.5 V even at 10 C. It is revealed that charge compensation from Mn- and O-ions contributes to the whole voltage range of 1.5-4.5 V, while the redox of Fe-ions only contributes to the high-voltage region of 3.0-4.5 V. The orphaned electrons in the nonbonding 2p orbitals of O that point toward TM-vacancy sites are responsible for reversible oxygen-redox, and Mg-ions in Na sites suppress oxygen release effectively.
P2-type layered oxides suffer from an ordered Na + /vacancy arrangement and P2→O2/OP4 phase transitions, leading them to exhibit multiple voltage plateaus upon Na + extraction/insertion. The deficient sodium in the P2-type cathode easily induces the bad structural stability at deep desodiation states and limited reversible capacity during Na + de/insertion. These drawbacks cause poor rate capability and fast capacity decay in most P2-type layered oxides. In this work, to address these challenges, a novel high sodium content (0.85) and plateau-free P2-type cathode-Na 0.85 Li 0.12 Ni 0.22 Mn 0.66 O 2 (P2-NLNMO) was developed. The complete solid-solution reaction over a wide voltage range ensures both fast Na + mobility (10 -11 to 10 -10 cm 2 s -1 ) and small volume variation (1.7%). Furthermore, the high sodium content P2-NLNMO exhibits a higher reversible capacity of 123.4 mAhg -1 , superior rate capability of 79.3 mAhg -1 at 20 C, and 85.4% capacity retention after 500 cycles at 5 C. The sufficient Na and complete solid-solution reaction are critical to realizing high-performance P2-type cathodes for sodium-ion batteries.