Structural regulation-induced Li-electron disentanglement for stabilized oxygen redox of Li-excess disordered rock-salt cathode materials

Since the discovery of its electrochemical activity, Li-excess disordered rock-salt (DRX) cathode material has received worldwide attention as it sets up a new way to exploit oxygen redox beyond the conventional layered structure with late-3d transition metals. However, the intricate structure-function relationship in the disordered lattice of the DRX material fogs the researcher's lens on the underlying redox mechanisms. Here, in this study, we employ a synergistic approach combining neutron total scattering with reverse Monte Carlo modeling and density functional theory calculations to unravel the landscape of oxygen redox reactions in DRX. Redox activities are evaluated in diverse oxygen clusters (OLi x TM 6-x ) and the spatial distribution of these clusters in the model DRX structure (Li 1.16 Ti 0.37 Ni 0.37 Nb 0.1 O 2 and Li 1.2 Ti 0.35 Ni 0.35 Nb 0.1 O 1.8 F 0.2 ) is explicitly determined. The results unveil that by regulating the short-range ordering between cations, fluorine atoms can effectively decouple the location of Li extraction and electron depletion. Such disentanglement between the Li reservoir and electron reservoir in the DRX lattice could play a pivotal role in protecting the oxidized oxygen and preserving the lattice framework during cycling. Through a tentatively designed non-fluorinated DRX oxide realizing similar Li-electron decoupling, an obvious enhancement of the cycling capability can be achieved without compromising the capacity release.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Designing lithium halide solid electrolytes

All-solid-state lithium batteries have attracted widespread attention for next-generation energy storage, potentially providing enhanced safety and cycling stability. The performance of such batteries relies on solid electrolyte materials; hence many structures/phases are being investigated with increasing compositional complexity. Among the various solid electrolytes, lithium halides show promising ionic conductivity and cathode compatibility, however, there are no effective guidelines when moving toward complex compositions that go beyond ab -initio modeling. Here, we show that ionic potential, the ratio of charge number and ion radius, can effectively capture the key interactions within halide materials, making it possible to guide the design of the representative crystal structures. This is demonstrated by the preparation of a family of complex layered halides that combine an enhanced conductivity with a favorable isometric morphology, induced by the high configurational entropy. This work provides insights into the characteristics of complex halide phases and presents a methodology for designing solid materials.

25 ENERGY STORAGE↗
DOE OSTI2023

Stabilizing lattice oxygen redox in layered sodium transition metal oxide through spin singlet state

Abstract Reversible lattice oxygen redox reactions offer the potential to enhance energy density and lower battery cathode costs. However, their widespread adoption faces obstacles like substantial voltage hysteresis and poor stability. The current research addresses these challenges by achieving a non-hysteresis, long-term stable oxygen redox reaction in the P3-type Na 2/3 Cu 1/3 Mn 2/3 O 2 . Here we show this is accomplished by forming spin singlet states during charge and discharge. Detailed analysis, including in-situ X-ray diffraction, shows highly reversible structural changes during cycling. In addition, local CuO 6 Jahn-Teller distortions persist throughout, with dynamic Cu-O bond length variations. In-situ hard X-ray absorption and ex-situ soft X-ray absorption study, along with density function theory calculations, reveal two distinct charge compensation mechanisms at approximately 3.66 V and 3.99 V plateaus. Notably, we observe a Zhang-Rice-like singlet state during 3.99 V charging, offering an alternative charge compensation mechanism to stabilize the active oxygen redox reaction.

25 ENERGY STORAGE↗
DOE OSTI2023

Direct Observation of Twin van der Waals Molecular Chains

The van der Waals (vdW) assemblies are the most common structures of materials. However, directly mapping intermolecular electron clouds of a vdW assembly has never been obtained, even though the intramolecular electron clouds were visualized by atomic-resolution techniques. In this report, we unprecedently mapped the intermolecular electron cloud of the assembles of ethanol molecules via ethyl groups with noncontact atomic force microscopy at 5 K, leading to the first visualization of vdW molecular chains, in which ethanol molecules assemble into twin vdW molecular chains in a reverse parallel configuration on Ag(111) plane. Furthermore, spontaneous order-disorder transitions in the chain were dynamically observed, suggesting its unusual properties different from 2D vdW materials. In conclusion, these findings provide an "eye" to see the atomic world of vdW materials.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Revealing Intermetallic Active Sites of PtNi Nanocatalysts for Reverse Water Gas Shift Reaction

Bimetallic nanoparticles have gained great interest due to their potential applications in catalysis. By combining Lattice Boltzmann Modeling (LBM), Density Functional Theory (DFT) calculations, and kinetic Monte Carlo (KMC) simulation, here we rationalize the superior performance of supported Pt-Ni alloy nanostructures over Pt and Ni alone during the reverse Water Gas Shift (rWGS) reaction, which was observed previously. The LBM simulation including the diffusion and flow of the reacting gas molecules within the supporting nanoporous channels in SBA-15 indicates that the simple combination of contributions from Ni and Pt alone is not enough to result in the observed promotion in rWGS activity and selectivity of the Pt-Ni alloy. Instead, the synergy between Pt and Ni via a unique intermetallic motif is responsible according to the DFT and KMC simulation. In conclusion, compared to the monometallic counterparts, the intermetallic-introduced ensemble effect at the low-coordinated Pt-Ni hybrid site of Pt-Ni alloy nanocatalysts enables the enhanced activation of CO 2 and promoted removal of CO/H 2 O as gas phase product.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

The Mechanism of Fluorine Doping for the Enhanced Lithium Storage Behavior in Cation-Disordered Cathode Oxide

Li-rich cation-disordered rock-salt (DRX) materials have emerged as promising candidates for high-capacity oxide cathodes. Their fluorinated variants have shown improved cycling stability with effectively suppressed oxygen loss. However, a comprehensive understanding of how fluorination impacts the multiscale structure and lithium transportation in DRX remains elusive in experiments. In this study, the neutron total scattering technique in conjunction with the advanced reverse Monte Carlo (RMC) fitting method is employed to characterize the intricate structure of Li 1.16 Ti 0.37 Ni 0.37 Nb 0.1 O 2 (LTNNO) and the fluorinated Li 1.2 Ti 0.35 Ni 0.35 Nb 0.1 O 1.8 F 0.2 (LTNNOF). Through rigorous statistical analysis, the multiscale structural evolution upon fluorination is quantified from atomic (≤5 Å) to long-range scale (≈100 Å). The local Li-rich environments around F induce a modest 2.4% increment in the number of fast Li 0TM (transition metal) channels. Crucially, at a broader scale, the proportion of 0TM channels participating in percolation increases significantly from 2.9% in LTNNO to 8.7% in LTNNOF. Fluorination improves the capacity release mainly through merging isolated fast Li channels into the percolation network. This work experimentally unravels the multiscale mechanism of fluorination-induced performance improvement in DRX materials and highlights the necessity of adopting an advanced RMC fitting method to obtain a full view of the complex structural features in developing high-capacity DRX cathodes.

25 ENERGY STORAGE↗
DOE OSTI2023

Determination of the Interfacial Energy between Graphene Nanoplatelets and Deuterated or Hydrogenated Polystyrene

The tracer diffusion coefficients of various graphene nanoplatelet-polystyrene (GNP-PS) systems were determined by using dynamic secondary ion mass spectrometry, which provided insights into the interactions within the polymer nanocomposite system. Bilayer films, where one contained trace amounts of deuterated polystyrene (dPS), were produced, and the interdiffusion was measured by detecting the position of the dPS interface. GNPs were placed in both or only one of the two layers. The diffusion coefficient was decreased when GNPs were present in both layers as compared to the samples without GNP, indicating an attractive interaction between GNP and polystyrene. Surprisingly, the coefficient increased relative to the control when GNPs were present only in the PS containing layer, whereas it decreased most strongly when GNP and dPS were present only in the same layer, indicating that an additional preference existed for GNPs and dPS. A significant difference in interfacial energies was measured using contact angle goniometry of PS or dPS droplets on flat GNP layers, confirming the preferential interaction. DFT calculations were used to calculate the interfacial interaction between GNP and dPS or PS, and they showed an attractive potential which was maximal when the PS rings were conformal with the GNP structure. Furthermore, the differential energy between PS and dPS at the GNP interface was in excellent agreement with the measured value. In contrast, contact angle goniometry indicated that the interaction between GNP and poly(methyl methacrylate) (PMMA) was unfavorable, and no difference in interfacial energy between dPMMA and PMMA was observed. Therefore, these techniques can provide a means for determining the relative affinity between GNP and different polymer hosts, which can be an important consideration in the mechanics and adhesion properties of the compounds.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Expandable Li Percolation Network: The Effects of Site Distortion in Cation-Disordered Rock-Salt Cathode Material

Cation-disordered rock-salt (DRX) materials receive intensive attention as a new class of cathode candidates for high-capacity lithium-ion batteries (LIBs). Unlike traditional layered cathode materials, DRX materials have a three-dimensional (3D) percolation network for Li + transportation. The disordered structure poses a grand challenge to a thorough understanding of the percolation network due to its multiscale complexity. In this work, we introduce the large supercell modeling for DRX material Li 1.16 Ti 0.37 Ni 0.37 Nb 0.10 O 2 (LTNNO) via the reverse Monte Carlo (RMC) method combined with neutron total scattering. Here, through a quantitative statistical analysis of the material’s local atomic environment, we experimentally verified the existence of short-range ordering (SRO) and uncovered an element-dependent behavior of transition metal (TM) site distortion. A displacement from the original octahedral site for Ti 4+ cations is pervasive throughout the DRX lattice. Density functional theory (DFT) calculations revealed that site distortions quantified by the centroid offsets could alter the migration barrier for Li + diffusion through the tetrahedral channels, which can expand the previously proposed theoretical percolating network of Li. The estimated accessible Li content is highly consistent with the observed charging capacity. The newly developed characterization method here uncovers the expandable nature of the Li percolation network in DRX materials, which may provide valuable guidelines for the design of superior DRX materials.

25 ENERGY STORAGE↗
DOE OSTI2023

Unraveling the convoluted and dynamic interphasial mechanisms on Li metal anode

Accurate understanding of the chemistry of solid-electrolyte interphase (SEI) is key to developing new electrolytes for high-energy batteries using lithium metal (Li-0) anodes(1). SEI is generally believed to be formed by the reactions between Li-0 and electrolyte(2,3). However, our new study shows this is not the whole story. Through synchrotron-based X-ray diffraction and pair distribution function analysis, we reveal a much more convoluted formation mechanism of SEI, which receives considerable contributions from electrolyte, cathode, moisture and native surface species on Li-0, with highly dynamic nature during cycling. Using isotope labelling, we traced the origin of LiH to electrolyte solvent, moisture and a new source: the native surface species (LiOH) on pristine Li-0. When lithium accessibility is very limited as in the case of anode-free cells, LiOH develops into plate-shaped large crystals during cycling. Alternatively, when the lithium source is abundant, as in the case of Li||NMC811 cells, LiOH reacts with Li-0 to form LiH and Li2O. While the desired anion-derived LiF-rich SEI is typically found in the concentrated electrolytes or their derivatives, we found it can also be formed in low-concentration electrolyte via the crosstalk effect, emphasizing the importance of formation cycle protocol and opening up opportunities for low-cost electrolyte development.

Polzin, Bryant J.↗
DOE OSTI2023

Atomic Structural Origin of the High Methanol Selectivity over In 2 O 3 –Metal Interfaces: Metal–Support Interactions and the Formation of a InO x Overlayer in Ru/In 2 O 3 Catalysts during CO 2 Hydrogenation

CO 2 hydrogenation to methanol is of great environmental and economic interest due to its potential to reduce carbon emissions and produce valuable chemicals in one single reaction. Compared with the unmodified traditional Cu/ZnO/Al 2 O 3 catalyst, an indium oxide (In 2 O 3 )-based catalyst can double the methanol selectivity from 30–50 to 60–100%. It is worth noting that over catalysts involving various active metals dispersed on indium oxide (M/In 2 O 3 , M = Pd, Ni, Au, etc.), although the methanol yield is boosted, the selectivity remains similar to that of plain In 2 O 3 despite the distinct chemical properties of the added metals. Here, to investigate the phenomena behind this behavior, we used RuO 2 /In 2 O 3 as a test catalyst. The results of ambient pressure photoelectron spectroscopy, in situ X-ray absorption fine structure, and time-resolved X-ray diffraction indicate that the structure of the RuO 2 /In 2 O 3 catalyst is highly dynamic in the presence of a reactive environment. Specifically, under CO 2 hydrogenation conditions, Ru clusters facilitate the reduction of In 2 O 3 to generate In 2 O 3–x aggregates, which encapsulate the Ru systems in a migration driven by thermodynamics. In this way, the Ru O sites for CH 4 production are blocked while creating RuO x –In 2 O 3–x interfacial sites with tunable metal–oxide interactions for selective methanol production. In an inverse oxide/metal configuration, indium oxide has properties not seen in its bulk phase that are useful for the binding and conversion of CO 2 . This work reveals the dynamic nature of In 2 O 3 -based catalysts, providing insights for a rational design of materials for the selective synthesis of methanol.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Resolving complex intralayer transition motifs in high-Ni-content layered cathode materials for lithium-ion batteries

High-Ni-content layered materials are promising cathodes for next-generation lithium-ion batteries. However, investigating the atomic configurations of the delithiation-induced complex phase boundaries and their transitions remains challenging. Here, in this study, by using deep-learning-aided super-resolution electron microscopy, we resolve the intralayer transition motifs at complex phase boundaries in high-Ni cathodes. We reveal that an O3 → O1 transformation driven by delithiation leads to the formation of two types of O1–O3 interface, the continuous- and abrupt-transition interfaces. The interfacial misfit is accommodated by a continuous shear-transition zone and an abrupt structural unit, respectively. Atomic-scale simulations show that uneven in-plane Li+ distribution contributes to the formation of both types of interface, and the abrupt transition is energetically more favourable in a delithiated state where O1 is dominant, or when there is an uneven in-plane Li + distribution in a delithiated O3 lattice. Moreover, a twin-like motif that introduces structural units analogous to the abrupt-type O1–O3 interface is also uncovered. The structural transition motifs resolved in this study provide further understanding of shear-induced phase transformations and phase boundaries in high-Ni layered cathodes.

77 NANOSCIENCE AND NANOTECHNOLOGY↗
DOE OSTI2022

Additive engineering for robust interphases to stabilize high-Ni layered structures at ultra-high voltage of 4.8 V

Nickel-rich layered cathode materials promise high energy density for next-generation batteries when coupled with lithium metal anodes. However, the practical capacities accessible are far less than the theoretical values due to their structural instability during cycling, especially when charged at high voltages. Here we demonstrate that stable cycling with an ultra-high cut-off voltage of 4.8 V can be realized by using an appropriate amount of lithium difluorophosphate in a common commercial electrolyte. The Li||LiNi 0.76 Mn 0.14 Co 0.10 O 2 cell retains 97% of the initial capacity (235 mAh g -1 ) after 200 cycles. The cycling stability is ascribed to the robust interphase on the cathode. It is formed by lithium difluorophosphate decomposition, which is facilitated by the catalytic effect of transition metals. The decomposition products (Li 3 PO 4 and LiF) form a protective interphase. This suppresses transition metal dissolution and cathode surface reconstruction. It also facilitates uniform Li distribution within the cathode, effectively mitigating the strain and crack formation.