Wang, Y. Morris

Publications and source records attributed to Wang, Y. Morris.

12 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Additively manufactured β-Ti5553 with laser powder bed fusion: Microstructures and mechanical properties of bulk and lattice parts

Ti5553 (Ti-5Al-5Mo-5V-3Cr wt%) is a titanium alloy widely used for its high strength-to-weight ratio and good formability at elevated temperatures. Unlike Ti-6Al-4V, Ti5553 does not undergo martensitic transformation, preventing cracking of brittle martensite upon rapid cooling. This makes it a strong candidate for additive manufacturing (AM), particularly laser powder bed fusion (L-PBF). L-PBF offers the unique opportunity to make fine lattice structures to reduce component weight. Despite the growing field of AM, there have been limited studies on L-PBF Ti5553 lattices and how their properties differ from the bulk. Here the present work addresses this knowledge gap by investigating microstructures and properties of L-PBF bulk and lattice parts and the effect of post L-PBF heat treatments. Electron microscopy and mechanical testing show that the high dislocation density formed during L-PBF increases bulk part’s yield strength by approximately 100 MPa compared to the conventional alloy. Digital image correlation during compression testing of octet truss lattices reveals a layer-by-layer failure mode. Compared to the bulk, the lattice contains copious ω nanoprecipitation, weaker <001> texture, smaller average grain sizes, and larger content of high-angle grain boundaries. These features elicit differences in Taylor factor distributions for the lattice depending on load direction, underlining challenges in predicting lattice mechanical response based on bulk properties. By examining the processing-structure-property relationships in the bulk and lattice, the present results delineate their microstructural and mechanical differences and establish a benchmark for the future design applications of L-PBF Ti5553.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Discovering the nanoscale origins of localized corrosion in additive manufactured stainless steel 316L by liquid cell transmission electron microscopy

Here, we use liquid cell scanning transmission electron microscopy (STEM) to directly characterize the nanoscale origins of corrosion initiation in Additive manufacturing (AM) 316 L stainless steel. Under applied anodic potentials, we found that the dislocation cellular boundaries were preferentially corroded and that regions of localize corrosion occurred along the cellular boundaries. We directly observed the earliest stages of corrosion by controlling the biasing parameters to decelerate the corrosion processes. The results show that highly localized corrosion occurs via inclusion dissolution along dislocation cell boundaries. More widespread corrosion initiates at the dislocation cell boundaries and spreads throughout the dislocation networks.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Strong yet ductile nanolamellar high-entropy alloys by additive manufacturing

Additive manufacturing produces net-shaped components layer by layer for engineering applications. The additive manufacture of metal alloys by laser powder bed fusion (L-PBF) involves large temperature gradients and rapid cooling, which enables microstructural refinement at the nanoscale to achieve high strength. However, high-strength nanostructured alloys produced by laser additive manufacturing often have limited ductility. In this work, we use L-PBF to print dual-phase nanolamellar high-entropy alloys (HEAs) of AlCoCrFeNi 2.1 that exhibit a combination of a high yield strength of about 1.3 gigapascals and a large uniform elongation of about 14 percent, which surpasses those of other state-of-the-art additively manufactured metal alloys. The high yield strength stems from the strong strengthening effects of the dual-phase structures that consist of alternating face-centred cubic and body-centred cubic nanolamellae; the body-centred cubic nanolamellae exhibit higher strengths and higher hardening rates than the face-centred cubic nanolamellae. The large tensile ductility arises owing to the high work-hardening capability of the as-printed hierarchical microstructures in the form of dual-phase nanolamellae embedded in microscale eutectic colonies, which have nearly random orientations to promote isotropic mechanical properties. The mechanistic insights into the deformation behaviour of additively manufactured HEAs have broad implications for the development of hierarchical, dual- and multi-phase, nanostructured alloys with exceptional mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Visualization and validation of twin nucleation and early-stage growth in magnesium

The abrupt occurrence of twinning when Mg is deformed leads to a highly anisotropic response, making it too unreliable for structural use and too unpredictable for observation. Here, we describe an in-situ transmission electron microscopy experiment on Mg crystals with strategically designed geometries for visualization of a long-proposed but unverified twinning mechanism. Combining with atomistic simulations and topological analysis, we conclude that twin nucleation occurs through a pure-shuffle mechanism that requires prismatic-basal transformations. Also, we verified a crystal geometry dependent twin growth mechanism, that is the early-stage growth associated with instability of plasticity flow, which can be dominated either by slower movement of prismatic-basal boundary steps, or by faster glide-shuffle along the twinning plane. The fundamental understanding of twinning provides a pathway to understand deformation from a scientific standpoint and the microstructure design principles to engineer metals with enhanced behavior from a technological standpoint.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Ultra-low-density digitally architected carbon with a strutted tube-in-tube structure

Porous materials with engineered stretching-dominated lattice designs, which offer attractive mechanical properties with ultra-light weight and large surface area for wide-ranging applications, have recently achieved near-ideal linear scaling between stiffness and density. Here, rather than optimizing the microlattice topology, we explore a different approach to strengthen low-density structural materials by designing tube-in-tube beam structures. We develop a process to transform fully dense, three-dimensional printed polymeric beams into graphitic carbon hollow tube-in-tube sandwich morphologies, where, similar to grass stems, the inner and outer tubes are connected through a network of struts. Compression tests and computational modelling show that this change in beam morphology dramatically slows down the decrease in stiffness with decreasing density. In situ pillar compression experiments further demonstrate large deformation recovery after 30–50% compression and high specific damping merit index. Lastly, our strutted tube-in-tube design opens up the space and realizes highly desirable high modulus–low density and high modulus–high damping material structures.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Confinement effects on the solvation structure of solvated alkaline metal cations in a single-digit 1T-MoS 2 nanochannel: A first-principles study

Confinement plays an important role in determining ion transport in porous materials, which, in turn, may influence the performance of many energy storage and desalination devices. In this work, we combined density functional theory (DFT) with an implicit solvation model and ab initio molecular dynamics (AIMD) to investigate the effects of nanoconfinement on several solvated alkaline metal cations in a single-digit 1T-MoS 2 nanochannel. Our DFT calculations with a solvation model indicated that cations with stronger hydration energy introduce a higher number of co-intercalated water molecules into the channel, consistent with early experimental observation obtained for MXene (2D transition metal carbide) channels. The predicted optimal water numbers for the cations were then used for AIMD simulations that explicitly include the effects of the solvent. When compared with the cations in bulk solution, our simulations showed that the hydration structure and coordination number (CN) of the solvated cations confined in the MoS 2 channel can be significantly altered. Further, we found that larger cations with weaker hydration energy (K + , Rb + , and Cs + ) exhibited a distinctive CN decrease under confinement, while smaller cations (Li + and Na + ) retained a similar hydration shell as in the bulk solution. More specifically, the hydration shell of large cations (K + , Rb + , and Cs + ) in MoS 2 showed similar features of the coordination angle to the bulk, which suggests the partially broken hydration shell with no geometry change under confinement. Our simulations provided insights into the change of the hydration structure of alkaline metal cations under confinement, which may have important implications on their transport in the 1T-MoS 2 channel.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Heavy ion irradiation response of an additively manufactured 316LN stainless steel

Additive manufacturing has become an appealing technique to fabricate three-dimensional metallic materials and components for nuclear reactors. However, response of additively manufactured alloys to high-dose heavy ion irradiations at elevated temperatures is still not well understood. Here, an additively manufactured 316LN austenitic stainless steel with high-density solidification cells was irradiated using 3.5 MeV Fe ion to a peak dose of 220 dpa at 450 °C. Microscopy studies show a lower Frank loop density and smaller size in the additively manufactured sample compared with its cold worked counterpart, and the cellular structures may largely suppress the formation of perfect loops and dislocation networks and reduce the magnitude of solute segregations comparing with high angle grain boundaries. In conclusion, the present work advances the understanding on the high-temperature irradiation response of additively manufactured steels for nuclear reactor applications.

36 MATERIALS SCIENCE↗
DOE OSTI2020

A 3D nm-thin biomimetic membrane for ultimate molecular separation

Multi-functional membranes with high permeance and selectivity that can mimic nature's designs have tremendous industrial and bio-medical applications. In this paper, we report a novel concept of a 3D nanometer (nm)-thin membrane that can overcome the shortcomings of conventional membrane structures. Our 3D membrane is composed of two three-dimensionally interwoven channels that are separated by a continuous nm-thin amorphous TiO 2 layer. This 3D architecture dramatically increases the surface area by 6000 times, coupled with an ultra-short diffusion distance through the 2–4 nm-thin selective layer that allows for ultrafast gas and water transport, ~900 l m –2 h –1 bar –1 . The 3D membrane also exhibits a very high ion rejection (R ~ 100% for potassium ferricyanide) due to the combined size- and charge-based exclusion mechanisms. The combination of high ion rejection and ultrafast permeation makes our 3DM superior to the state-of-the-art high-flux membranes whose performances are limited by the flux-rejection tradeoff. Furthermore, its ultimate Li+ selectivity over polysulfide or gas can potentially solve major technical challenges in energy storage applications, such as lithium–sulfur or lithium–O 2 batteries.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Lattice strains and diffraction elastic constants of cubic polycrystals

In situ synchrotron X-ray and neutron diffraction experiments provide a powerful approach to measure lattice strains in bulk polycrystalline materials. They are being increasingly used for quantitative characterization of microscale deformation within and between grains and phases. Here we use a self-consistent micromechanics model to obtain a general analytic solution of the grain-level lattice strains and diffraction elastic constants for a broad class of elastically isotropic polycrystals with cubic crystal symmetry. This analytic solution reveals a direct linear relationship between the reciprocal of the elastic diffraction constant and the orientation index parameter along the direction of any diffraction vector, including tensile loading and transverse directions. The straightforward numerical implementation of this solution provides diffraction elastic constants for 26 representative cubic polycrystals. Finally, analytic solutions of this kind can serve to benchmark in situ diffraction measurements of lattice strains and also facilitate high-throughput studies of microscale stresses and diffraction elastic constants in polycrystalline materials.

36 MATERIALS SCIENCE↗