Publications and source records attributed to Wang, Yanli.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Experimental and Analytical Verification of ASME Section IiII Division 5 Creep-Fatigue Design Rules

The continuous advancement of structural materials and the growing demands for more reliable and economical structural components in high-temperature reactor applications have necessitated the development of comprehensive design methodologies and design rules. Mechanical degradation of structural components at elevated temperatures subjected to cyclic deformation is controlled by the creep-fatigue damage. Over the past few decades, diligent research efforts have been dedicated to refining the development of elevated temperature design rules in the American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code (BPVC), Section III, Division 5 and to develop conservative design rules that can effectively guard against the risk of creep-fatigue failure. In ASME Section III, Division 5, for a design to pass the creep-fatigue acceptance criteria, creep damage and fatigue damage are evaluated separately, and these damages must not violate the bi-linear creep-fatigue interaction diagram, i.e., the so-called D-diagram. The creep-fatigue damage evaluation procedure assumes that the effects of the actual cyclic loading sequence can be bounded by assuming that the individual loading cycles are uniformly distributed throughout the component design life. In this study, creep-fatigue experiments with variable amplitudes and loading sequencies were designed and performed on Alloy 617 at high temperatures. The results were analyzed to evaluate the loading history effect on creep-fatigue damage accumulation and to verify the assumptions for the creep-fatigue evaluation design rules.

36 - MATERIALS SCIENCE↗
DOE OSTI2024

Mitigation of distortion of Al/steel part under simulated paint baking condition: Experiment and numerical model studies

Multi-material joining of lightweight structures is essential to reduce vehicle weight for more energy savings and less greenhouse gas emission. However, mismatch of thermal expansion coefficient for dissimilar materials during the paint baking process can induce part distortion and joint failure for adhesive bonding. Here, in the present work, a thermomechanical model based on contact mechanics and large deformation theory was developed for dissimilar high-strength Al alloy and steel components to study the distortion mechanism and influential factors of the residual gap. The established model was used to optimize joint conditions, such as pitch distance and part geometry. When a weld pitch is shorter than 100 mm, the maximum gap between Al and steel part can be greatly reduced to 0.1 mm, and the local stress and plastic strain around the joint during the oven heating and cooling cycle are also substantially reduced compared with the long pitch case (900 mm). The numerical modeling results revealed that a comparable bending stiffness ratio between the steel and Al cross sections is critical to the minimization of gap and distortion under paint baking condition. Digital image correlation technique was used to measure the overall part distortion and local strain distribution that were used to validate the model prediction. Weld bonding (adhesive bonding with friction bit joining) process was successfully employed to join Al to steel component without gap opening in adhesive after the paint baking and cooling.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Irradiation And Post-Irradiation Examination Plan For A709

The Advanced Materials and Manufacturing Technologies program is proposing a neutron irradiation campaign for alloy 709 (A709) plate product developed by the Advanced Reactor Technologies program. This irradiation campaign will support the deployment of A709 (included welded components) by providing data of engineering importance, such as data that can be used for establishing end-of-life design parameters and knockdown factors for irradiated materials properties versus properties for non-irradiated material. It will also advance the scientific understanding of A709 irradiation behaviors and material property evolution, which is vital for deploying A709 components into reactors with different neutron spectra, neutron fluxes, and irradiation temperatures as well as accelerating the deployment of new product forms and weld procedures. This document presents the plan for the neutron irradiation and post-irradiation examination for A709 and the scientific and technical basis for the plan.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2024

New ASME Section III, Division 5 Creep-Fatigue Design Rules Based on EPP and SMT Approaches

The integrated elastic-perfectly plastic (EPP) and simplified model test (SMT) creep-fatigue (CF) design methodology, referred to as the EPP-SMT method, is being developed as an alternative for CF evaluation in the design of pressure boundary components for high-temperature reactors. This report reviews the conceptual basis of the EPP-SMT methodology, summarizes the SMT experimental development efforts and results, and provides the technical basis for finalizing the EPP-SMT CF design curves for Alloy 617, based on a combined experimental and numerical approach conducted in FY 2024. This report presents the effect of hold time on the CF design curves for Alloy 617 at elevated temperatures. It includes proposed EPP-SMT CF design curves and tabulated values for continuous cycling, along with the effects of maximum hold time, for the use of this EPP-SMT CF evaluation method.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Fatigue and Creep-Fatigue Evaluation of Alloy 709 at 760 and 816°C

A significant research and development effort is underway to support the qualification of Alloy 709 as a Class A construction material in the American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code, Section III, Division 5, High Temperature Reactors. This initiative includes a comprehensive Alloy 709 code qualification plan aimed at generating extensive material testing data crucial for compiling the code case data package. The data package is essential in establishing material-specific design parameters for Alloy 709 to be used as Section III, Division 5 Class A construction material for fast reactors, molten salt reactors and gas-cooled reactors. An ASME Section III, Division 5 material code case requires the evaluation of mechanical properties from a minimum of three commercial heats, covering anticipated compositional ranges. A key part of the data package involves fatigue and creep-fatigue testing at elevated temperatures, needed for developing the fatigue design curves and the damage envelope of the creep-fatigue interaction diagram (D-diagram). This paper summarizes the strain-controlled fatigue testing on three commercial heats of Alloy 709 at 760 and 816°C with strain ranges between 0.25% and 3%. The fatigue failure data are used to generate a preliminary fatigue design curve. Additionally, the creep-fatigue testing results at 816°C with tensile hold times of 10, 30, and 60 minutes are presented in support of developing the D-diagram for Alloy 709.

Wang, Yanli↗
DOE OSTI2024

Assessment of a Grade 91 Steel Forging and Seamless Pipe Section After 141,000-Hours of Operation in a Superheat Outlet Header

In this work, two unique heats of 9Cr creep strength enhanced ferritic (CSEF) steels extracted from a retired superheat outlet header after 141,000 hours of service were evaluated. These two CSEF steels were a forging manufactured to SA-182 F91 (F91) reducer and a seamless pipe produced to SA-335 P91 (P91) pipe. Their creep deformation and fracture behavior were assessed using a lever arm creep frame integrated with in-situ high-temperature digital image correlation (DIC) system. Critical metallurgical and microstructure factors, including composition, service damage, grain matrix degradation, precipitates, and inclusions were quantitatively characterized to link the performance of the two service aged F91 and P91 CSEF steels. The creep test results show the F91 and P91 steels exhibit a large variation in creep strength and creep ductility. The F91 steel fractured at 572 hours while P91 steel fractured at 1,901 hours when subjected to a test condition of 650 °C and 100 MPa. The nominal creep strains at fracture were 12.5% (F91) and 14.5% (P91), respectively. The high-resolution DIC strain measurements reveal the local creep strain in F91 was about 50% while the local creep strain in P91 was >80%. The characterization results show that the F91 steel possessed pre-existing creep damage from its time in service, a higher fraction of inclusions, and a faster matrix grain coarsening rate. These features contribute to the observed reduction in performance for the F91 steel. The context for these findings, and the importance of metallurgical risk in an integrated life management approach will be emphasized.

Wang, Yiyu↗
DOE OSTI2024

Modeling-Based Design and Optimization of a Gradient Composite Transition Joint

An innovative additively manufactured gradient composite transition joint (AM-GCTJ) has been designed to join dissimilar metals, to address the pressing issue of premature failure observed in conventional dissimilar metal welds (DMWs) when subjected to increased cyclic operating conditions of fossil fuel power plants. The transition design, guided by computational modeling, developed a gradient composite material distribution, facilitating a smooth transition in material volume fraction and physical properties between different alloys. This innovative design seeks to alleviate structural challenges arising from distinct material properties, including high thermal stress and potential cracking issues resulting from the thermal expansion mismatch typically observed in conventional DMWs. In this study, we investigated the creep properties of transition joints comprising Grade 91 steel and 304 stainless steel through a combination of simulations and creep testing experiments. The implementation of a gradient composite design in the plate transition joint resulted in a significant enhancement of creep resistance when compared to the baseline conventional DMW. For instance, the creep rupture life of the transition joint was improved by > 400% in a wide range of temperature and stress testing conditions. Meanwhile, the failure location shifted to the base material of Grade 91 steel. Such enhancement can be primarily attributed to the strong mechanical constraint facilitated by the gradient composite design, which effectively reduced the stresses on the less creep-resistant alloy in the transition zone. Beyond examining plate joints, it is crucial to assess the deformation response of tubular transition joints under pressure loading and transient temperature conditions to substantiate and demonstrate the effectiveness of the design. The simulation results affirm that the tubular transition joint demonstrates superior resistance compared to its counterpart DMW when subjected to multiaxial stresses in tubular structures. In addition, optimization of the transition joint’s geometry dimensions has been conducted to diminish the accumulated deformation and enhance the service life. Lastly, the scalability and potential of the innovative transition joints for large-diameter pipe applications are addressed.

Zhang, Wei↗
DOE OSTI2024

An Engineering Approach for Weld Creep Lifetime Assessment Based on Local Property Measurement

The localized creep failure in the heat-affected zone (HAZ) of Grade 91 steel weldments has been identified as one of the most important factors causing significantly shortened service lifetime and structural integrity issues of welded components in advanced fossil and nuclear power plants. To conduct a reliable creep lifetime assessment, a new engineering assessment approach has been developed by incorporating the experimentally determined local properties of the heterogeneous HAZ. By creep testing a purposely simulated HAZ specimen with in situ digital image correlation (DIC) technique, the highly gradient creep properties across the HAZ of Grade 91 steel was quantitatively measured. A physical creep cavitation constitutive model was proposed to investigate the local creep deformation and damage accumulation within the heterogeneous HAZ, which takes into account the nucleation of creep cavities and their growth by both grain boundary diffusion and creep deformation. The relationship among the local material property, creep strain accumulation, and evolution characteristic of creep cavities was established. The approach was then utilized to investigate the creep response and subsequent life for an ex-service 9% Cr steel weldment by incorporating the effects of pre-existing damages which developed and accumulated during long-term services. The predicted results exhibited quantitative agreement with the DIC measurement in terms of both nominal/local creep deformation as well as the subsequent life under the test conditions at 650 and 80 MPa.

Zhang, Wei↗
DOE OSTI2024

Creep-Fatigue Properties of Additional 316H PM-HIP Materials Fabricated from Different Powder Compositions and Processing Routes

The process of powder metallurgy (PM) hot isostatic pressing (HIP) works by consolidating powdered materials at relatively high temperature and pressure to form near-net-shaped components. Ideally, PM-HIP production methods can reduce component lead time and improve designs for high-temperature reactors and/or microreactors. To introduce PM-HIP into Section III, Division 5 of the American Society of Mechanical Engineers Boiler and Pressure Vessel Code, it is necessary to show adequate material properties regarding creep, high-temperature low-cycle fatigue, and creep fatigue. However, prior work has shown that the creep-fatigue cycles to failure for PM-HIP 316H stainless steel are greatly reduced compared to the conventional, wrought product. This work continued creep-fatigue analysis on a 316H stainless steel with lower oxygen and nitrogen contents and at different HIP parameters than previously analyzed. The objective was to better understand what is causing the reduced PM-HIP 316H performance so improvements can be made PM-HIP 316H creep-fatigue lifetimes.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Interim Development of new Class B Code Case with Variable Design Lifetime and enhanced design rules to guard against cyclic structural failure mode

This report summarizes updates on the ongoing development of the new American Society of Mechanical Engineers Section III, Division 5, Class B rules to address the potential failure modes of Class B components. An initial design-by-analysis approach and supporting design rules are presented. The elastic-perfectly plastic (EPP) analysis approach has been adopted for primary stress limit and ratcheting check to prevent the component failure against the structural failure mode against primary load and strain accumulation due to cyclic loads. The creep-fatigue damage assessment uses explicitly defined elastic follow-up calculated from the stress concentration region of given component. Damage fraction calculation uses a novel coupled approach to capture the influence of the elastic follow-up and provide adequate conservatism for Class B components. The proposed Class B rules does not use the stress classification approach and uses the combined loads to assess component.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Summary of FY 2024 A709 Code Case testing at ANL, INL and ORNL

A collaborative research and development effort in support of the Alloy 709 Code Case qualification in the American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code, Section III, Division 5, High Temperature Reactors is being carried out at Oak Ridge National Laboratory (ORNL), Idaho National Laboratory (INL), and Argonne National Laboratory (ANL). Key testing data for the Alloy 709 100,000-hr near-term Code Case submittal to ASME is expected to be completed by the end of 2024, with design parameters anticipated to be finalized in FY 2025. This report summarizes the testing results for three commercial heats of Alloy 709 conducted across three laboratories, reviews the current testing status, and outlines the remaining data needed to support the first Alloy 709 Code Case submittal to ASME. The Alloy 709 Code Case plan remains on schedule.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2024

Design by analysis rules for ASME Section III, Division 5, Class B components

The current rules for elevated temperature ASME Section III, Division 5, Class B components, other than piping, were basically adapted from the Design-by-Rule approach for Section VIII, Division 1 vessels. A goal of the proposed new rules is to explicitly account for the design life and cyclic service while recognizing the less-rigorous requirements commensurate with lesser safety consideration. Further goals are to maximize the use of modern computational technology, for example finite element analysis in conjunction with reference stress concepts, and to avoid the need for stress classification. This paper summarizes the work done to address these issues. A summary of the design-by-analysis for primary loads, strain limit evaluation, and creep-fatigue damage assessment is presented. The proposed design-by-analysis creep-fatigue damage calculation approach uses a new elastic follow-up-based Isochronous Stress Strain Curve stress relaxation procedure. A set of sample problems are selected to validate the proposed design-by-analysis rules for creep-fatigue damage assessment. The proposed Class B rules are evaluated against the Class A elastic design rules and the experimental data obtained from a family of a simplified model test-based key-feature test results. The proposed Class B creep-fatigue damage assessment methodology yields conservative design cycles estimates compared to the experimental results.

36 MATERIALS SCIENCE↗
DOE OSTI2024

High Temperature Materials

Overview of high temperature metals, including component construction rules for advanced reactor designs, assessment of filler metal for Alloy 800H weldments, high-temperature crack growth rate testing, work packages and contributors for FY24, creep-fatigue damage summation evaluation, GCR metal needs, and high temperature metals from other programs.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Preliminary Experimental Results in Support of the Development of EPP and SMT Design Methods and Viscoplastic Model for A709

The ASME code qualification effort for Alloy 709 (A709) is currently underway to qualify it for Class A construction in the American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code, Section III, Division 5. The United States (U.S.) Department of Energy (DOE) national laboratories are collaborating in the advanced materials development initiative to investigate the mechanical performance of A709 in support of its code qualification. As part of the A709 code qualification effort, this report summarizes ORNL’s initial experimental findings that support the integration of A709 into the elastic-perfectly plastic (EPP) strain limits code case. It also covers thermomechanical fatigue testing conducted to develop viscoelastic material models, along with the preliminary results of creep-fatigue experiments at 816°C using the Simplified Model Test (SMT) method.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Summary of FY2024 Experimental Results to Support Development of New Inelastic Material Models and Validation of Section III, Division 5, Class A Design Rules

To address the data gap crucial for updating existing viscoplastic constitutive material models for the Class A materials in the American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code, Section III, Division 5, High Temperature Reactors (ASME, 2023) for inelastic design analysis, Oak Ridge National Laboratory (ORNL) conducted experimental studies on Alloy 800H and Alloy 617 across a range of temperatures up to their maximum temperature limits in Section III, Division 5. The studies aim to characterize the materials' deformation behavior under both strain-controlled mechanical cyclic loading and thermal cycling conditions. This report summarizes ORNL's FY 2024 experimental findings on Alloy 800H and Alloy 617, focusing on pure fatigue tests, cyclic stress-strain curves, thermomechanical fatigue experiments, and verification of the high temperature cyclic damage summation design rules.

36 MATERIALS SCIENCE↗