DOE OSTI2023

Cu-Doped Iron Oxide for the Efficient Electrocatalytic Nitrate Reduction Reaction

The electrochemical nitrate reduction reaction (NO 3 RR) is a promising alternative synthetic route for sustainable ammonia (NH 3 ) production, because it not only eliminates nitrate (NO 3 – ) from water but also produces NH 3 under mild operating conditions. However, owing to the complicated eight-electron reaction and the competition from the hydrogen evolution reaction, developing catalysts with high activities and Faradaic efficiencies (FEs) is highly imperative to improve the reaction performance. In this study, Cu-doped Fe 3 O 4 flakes are fabricated and demonstrated to be excellent catalysts for electrochemical conversion of NO 3 – to NH 3 , with a maximum FE of ~100% and an NH 3 yield of 179.55 ± 16.37 mg h –1 mg cat –1 at –0.6 V vs RHE. Here, theoretical calculations reveal that doping the catalyst surface with Cu results in a more thermodynamically facile reaction. These results highlight the feasibility of promoting the NO 3 RR activity using heteroatom doping strategies.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Fe–N–C Boosts the Stability of Supported Platinum Nanoparticles for Fuel Cells

The poor durability of Pt-based nanoparticles dispersed on carbon black is the challenge for the application of long-life polymer electrolyte fuel cells. Recent work suggests that Fe- and N-codoped carbon (Fe-N-C) might be a better support than conventional high-surface-area carbon. In this work, we find that the electrochemical surface area retention of Pt/Fe-N-C is much better than that of commercial Pt/C during potential cycling in both acidic and basic media. In situ inductively coupled plasma mass spectrometry studies indicate that the Pt dissolution rate of Pt/Fe-N-C is 3 times smaller than that of Pt/C during cycling. Density functional theory calculations further illustrate that the Fe-N-C substrate can provide strong and stable support to the Pt nanoparticles and alleviate the oxide formation by adjusting the electronic structure. The strong metal-substrate interaction, together with a lower metal dissolution rate and highly stable support, may be the reason for the significantly enhanced stability of Pt/Fe-N-C. In conclusion, this finding highlights the importance of carbon support selection to achieve a more durable Pt-based electrocatalyst for fuel cells.

25 ENERGY STORAGE↗

DOE OSTI2021

Electrolytes Polymerization‐Induced Cathode‐Electrolyte‐Interphase for High Voltage Lithium‐Ion Batteries

Abstract Lithium‐ion batteries (LIBs) based on LiNi x Co y Mn 1‐x‐y O 2 (NCM) cathode materials have been widely commercialized, because of their high energy density, favorable rate performance, and relatively low cost. However, with increased Ni content to further increase their energy density, their cycling stability deteriorates dramatically and thus fails to meet the commercial application requirements. The artificial cathode‐electrolyte‐interphase (CEI) is a promising approach to solve this problem. Here, a robust CEI is fabricated through in situ polymerization of ethylene carbonate induced by aluminum isopropoxide (AIP). By adding 1 wt.% AIP in a commercial electrolyte, the capacity retention of LiNi 0.8 Co 0.1 Mn 0.1 O 2 ||Li cell at 1 C rate has been significantly increased from 80.8% to 97.8% with a highly reversible capacity of 176 mA h g −1 after 200 cycles. AIP can be also used as an additive during the slurry‐making process, enabling a reversible capacity of 170 mA h g −1 for LiCoO 2 after 200 cycles even at a high charge cut‐off voltage of 4.6 V. It is confirmed that the in situ formed CEI layer can prevent the cathodes from cracking and reduce the irreversible phase transformation.

Yang, Jixiang↗

DOE OSTI2021

Solid-State Synthesis of Highly Dispersed Nitrogen-Coordinated Single Iron Atom Electrocatalysts for Proton Exchange Membrane Fuel Cells

Fe–N–C with atomically dispersed Fe single atoms is the most promising candidate to replace platinum for the oxygen reduction reaction (ORR) in fuel cells. However, the conventional synthesis procedures require quantities solvents and metal precursors, sluggish adsorption process, and tedious washing, resulting in limited metal doping and uneconomical for large-scale production. Here, for the first time, Fe 2 O 3 is adopted as the Fe precursor to derive abundant single Fe atoms dispersed on carbon surfaces. The Fe–N–C catalyst synthesized by this simple method shows an excellent ORR activity with half-wave potentials of 0.82 and 0.90 V in acidic and alkaline solutions, respectively. A single fuel cell with an optimized Fe–N–C cathode shows a high peak power density of 0.84 W cm –2 . The solid-state transformation synthesis method developed in this study may shed light on mass production of single-atom-based catalysts.

25 ENERGY STORAGE↗