DOE OSTI2022

Non‐Flammable Ester Electrolyte with Boosted Stability Against Li for High‐Performance Li Metal Batteries

Abstract In traditional non‐flammable electrolytes a trade‐off always exists between non‐flammability and battery performance. Previous research focused on reducing free solvents and forming anion‐derived solid‐electrolyte interphase. However, the contribution of solvated anions in boosting the stability of electrolyte has been overlooked. Here, we resolve this via introducing anions into Li + solvation sheaths using anions with similar Gutmann donor number (DN) to that of solvents. Taking trimethyl phosphate fire‐retardant (DN=23.0 kcal mol −1 ) and NO 3 − (DN=22.2 kcal mol −1 ) as an example, NO 3 − is readily involved in the Li + solvation sheath and reduces the polarity of solvent. This results in boosted stability of electrolyte against Li. The developed non‐flammable electrolyte has low viscosity, high ionic conductivity and is low cost. The reversibility of Li‐Cu cell was improved to 99.49 % and the lifespan of practical LMBs was extended by >100 %.

Wang, Zhijie↗
DOE OSTI2022

Non‐Flammable Ester Electrolyte with Boosted Stability Against Li for High‐Performance Li Metal Batteries

Abstract In traditional non‐flammable electrolytes a trade‐off always exists between non‐flammability and battery performance. Previous research focused on reducing free solvents and forming anion‐derived solid‐electrolyte interphase. However, the contribution of solvated anions in boosting the stability of electrolyte has been overlooked. Here, we resolve this via introducing anions into Li + solvation sheaths using anions with similar Gutmann donor number (DN) to that of solvents. Taking trimethyl phosphate fire‐retardant (DN=23.0 kcal mol −1 ) and NO 3 − (DN=22.2 kcal mol −1 ) as an example, NO 3 − is readily involved in the Li + solvation sheath and reduces the polarity of solvent. This results in boosted stability of electrolyte against Li. The developed non‐flammable electrolyte has low viscosity, high ionic conductivity and is low cost. The reversibility of Li‐Cu cell was improved to 99.49 % and the lifespan of practical LMBs was extended by >100 %.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Reducing sputter induced stress and damage for efficient perovskite/silicon tandem solar cells

Reducing damages caused by sputtering of transparent conductive oxide (TCO) electrodes is critical in achieving highly efficient and stable perovskite/silicon tandem solar cells. Here we study the sputter caused damage to bathocuproine (BCP), which is widely used in highly efficient p-i-n structure single junction perovskite solar cells. While BCP buffer layer protects the underneath layers from damage, itself can be damaged by sputtering of TCOs at a wide range of target-substrate distances, supported by molecular dynamic simulation. More intriguingly, it is observed that TCO easily peeled off after sputtering when the sputtering target is close to substrate. This is ascribed to formation of stress during cooling down process after sputtering due to different thermal expansion coefficients of the layers. Our studies explain why tin oxide (SnO2) made by atomic layer deposition can replace BCP for a much better tandem device performance. SnO2 has high affinity with sputtered TCO electrode to suppress peeling-off issue and has higher bond energy to resist sputter induced damage, thus it allows a wider window of target-substrate distances than BCP during TCO sputtering. Ultimately, we demonstrate an efficient perovskite/silicon monolithic tandem solar cell with efficiency of 26.0% to illustrate the beneficial effects of reduced stress and damage.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗