Characterizing Face Sheet/Core Disbonding Using the Single Cantilever Beam Test: Results from an International Round Robin

Test results from an international round robin are presented. The single cantilever beam (SCB) test was used to characterize face sheet/core disbonding in sandwich components in an effort to help standardization. Each of the seven participating laboratories performed a set of five baseline tests using the same protocol, however, using their own specific equipment. In addition, each laboratory performed two sets of tests with altered tests conditions which included using a test fixture with a translating carriage and performing the tests with different loading and unloading speeds. The orientation of the disbond front with respect to the honeycomb core cells was varied and the effect on the fracture toughness was also studied. Additional factors that could influence test results were investigated, such as the use of a saw cut starter disbond as an alternative to Teflon® release film, and the effects of using a face sheet doubler to increase the bending stiffness. For each set of tests, summary results such as load/displacements plots, observed disbond growth location and calculated energy release rates are reported and a comparison of results between labs is presented. Critical strain energy release rate measurements from SCB tests are also compared with measurements made from an alternative test, namely the double cantilever beam with uneven bending moments (DCB-UBM) test, which has been studied extensively at the Technical University of Denmark and proposed as a mixed-mode test standard. A set of recommendations are made with respect to improving the SCB test and a path to standardization is presented.

Ronald Krueger↗
NASA NTRSDate not supplied

An Engineering Approach to Analyze Damage Initiation Modes in Tapered Composite Structures

In this work an engineering approach is demonstrated for analyzing damage initiation modes in tapered composite structures. The analysis methodology includes simulation of the non-linear static response of tapered composite structures under static tension loads to predict the location of interfacial delamination initiation. Furthermore, the developed methodology provides a strength-based criterion to assess whether damage initiation will occur in the inter-laminar delamination or intra-laminar matrix cracking mode. Based on the results of the analysis, a tapered composite structure is fabricated and tested under displacement-controlled quasi-static tension loading. The damage initiation location captured experimentally is compared with the analysis towards achieving preliminary qualitative validation. The linear stiffness of the tapered composite structure is predicted within 15% of the experimental average thereby achieving preliminary quantitative validation.

Prabhakar M Rao↗
NASA NTRSDate not supplied

Progressive Damage Mechanisms in Thick 3D Composite Structures under Static and Fatigue Loading

The objective of this work is to demonstrate validation of predictive capabilities capturing both damage initiation and growth under static and fatigue loading in geometrically complex three-dimensional (3D) composite structures. The composite structure of interest in the present study resembles a 3D blade spar used in rotorcraft applications. Under both static and fatigue testing, it was shown that damage initiated at the same ply-drop location(s) and grew in the axial as well as hoop directions. CompDam – a state-of-the-art Progressive Damage Analysis (PDA) tool was used to achieve successful correlations of metrics including load-displacement responses and damage modes.

progressive damage analysis↗
NASA NTRSDate not supplied

Open-Hole Testing of Resin Infused Carbon Composite Laminates to Facilitate Damage Growth and Failure Analysis Tools for Structural Design

In manufacturing of carbon-fiber reinforced composite aircraft structures, resin infusion offers a highly repeatable process for manufacturing structural components with resin content control, low labor requirements, and complex curvatures. To further understand the structural capabilities of res-in infused composites (RIC), this study – as part of the NASA-led Hi-Rate Composite Aircraft Manufacturing project efforts – performed open hole tension (OHT) and open hole compression (OHC) testing on RIC laminates. This testing provides information on the damage morphology and growth characteristics of RICs, which fuels the development and evaluation of analysis tools for progressive damage growth and failure responses. X-ray computed tomography (XCT) was implemented on each OHC and OHT specimen prior to mechanical testing to identify preexisting damage and/or defects. Two OHT and OHC specimens were loaded monotonically to failure and an additional OHT and OHC specimen were loaded intermittently at defined conditions and XCT scanned after each run. From the data obtained in this study, damage mechanisms leading to failure were identified, damage morphology and size were assessed, and damage initiation and failure loads were measured.

HiCAM↗