Publications and source records attributed to Was, Gary S..

14 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

How irradiation promotes intergranular stress corrosion crack initiation

Irradiation assisted stress corrosion cracking (IASCC) is a form of intergranular stress corrosion cracking that occurs in irradiated austenitic alloys. It requires an irradiated microstructure along with high temperature water and stress. The process is ubiquitous in that it occurs in a wide range of austenitic alloys and water chemistries, but only when the alloy is irradiated. Despite evidence of this degradation mode that dates back to the 1960s, the mechanism by which it occurs has remained elusive. Here, using high resolution electron backscattering detection to analyze local stress-strain states, high resolution transmission electron microscopy to identify grain boundary phases at crack tips, and decoupling the roles of stress and grain boundary oxidation, we are able to unfold the complexities of the phenomenon to reveal the mechanism by which IASCC occurs. The significance of the findings impacts the mechanical integrity of core components of both current and advanced nuclear reactor designs worldwide.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Experimental and Computational Studies of Stress Corrosion Cracking of Alloys 308/309 and 82/182 Weldments in Corrosive and Radiation Environment

The goal of the project was to determine factors that influence SCC and IASCC in weldments found in LWR nuclear power plants. We focused on a SA508-304L SS weldment fabricated by EPRI using gas tungsten arc welding and used an aggressive BWR normal water chemistry (NWC) immersion environment. This weldment used 309L butter and 308L groove filler material. The microstructure of the 309L butter was non-uniform, exhibiting a 20–30μm thick martensitic layer closest to the SA508 interface, a 1–4 mm thick single γ austenite phase dilution zone, and a γ–δ duplex region extending to the 308L groove filler. The 308L groove filler had an entirely γ–δ duplex microstructure. Two approximately 1-inch thick 304L and SA508 plates approximately 12 by 6 square inches were joined using standard nuclear grade welding techniques. This included a post weld heat treatment of the 309L butter after application, a 0.32 cm fit-up root opening, and 57 bead lines of 308L groove filler applied in 18 layers. A 60 degree weld bevel angle was used and the 309L butter was 1.5 cm thick. Displacement cascade damage was induced using proton irradiation at the Michigan Ion Beam Laboratory. The incident proton energy was 2 MeV, the sample temperature was 360 ºC, and the calculated dpa value at 10 μm (60% of the Bragg peak depth of ~18 μm) was 5 dpa using the quick Kinchin-Pease model. Proton irradiation to this damage level required approximately 125 hours of beam time. Two types of samples were irradiated, tensile specimens and TEM bars. Samples were selected from all regions of the weldment, including the SA508-309L butter interface, the 309L-308L interface, and 308L-304L interface. The stainless steel alloys (304L, 308L, and 309L) within the heat affected zone are characterized by a duplex skeletal morphology of δ-ferrite and γ-austenite resulting from the recrystallization associated with weld fabrication. Approximately 7 to 8 mm of length along the specimen was irradiated. The gauge volume surfaces were mechanically polished and then electro-polished to remove mechanical damage from the mechanical polishing step prior to irradiation. Immersion tests were performed in a recirculating autoclave under BWR NWC conditions (2000 ppb wt. dissolved oxygen, neutral pH, 288 ºC, 10 MPa, and inlet water conductivity <100 nS/cm) to accelerate corrosion. Constant strain rate tests were performed either to failure or to approximately 5% strain. Strain rates of 10 -7 to 10 -6 mm/mm/s were used and typical immersion testing required four to six weeks to achieve failure or strains near 5%. Analysis primarily used advanced electron microscopy techniques of FIB lift out specimens.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Irradiation-assisted Stress Corrosion Cracking of PWRirradiated Type 347 Stainless Steel (NSUF CINR 19-16567)

This document serves as the final report for NSUF Project 19-16567 (Reference 1) and its supporting contracts (References 2 and 3). It documents completion of testing of specimens fabricated as previously described in Reference 4. At a high level, the purpose of the testing is to generate data to support continued operation of light water reactors (LWR) and provide further understanding of irradiation-assisted stress corrosion crack (IASCC) initiation in baffle-former bolt materials. Baffle-former bolts that had been extracted from commercial pressurized water reactors (PWRs) were machined into miniature 4-point bend specimens and TEM samples at the Westinghouse Churchill Site hot cell facility. These samples were then shipped to the University of Michigan to undergo IASCC initiation testing in simulated PWR primary coolant containing either LiOH or KOH additions. Overall, 15 samples were tested, 8 in water with KOH additions and 7 in water with LiOH additions, until indications of cracking were observed. Crack initiation stress was similar in both water environments at 50-60% of the irradiated yield stress. Post-test examination of the cracking sites, including scanning electron microscopy and transmission electron microscopy, demonstrated that the crack initiation mechanism and crack initiation rates were similar between the two different water chemistries. A grain boundary oxidation and oxide fracture mechanism was observed to be responsible for crack initiation.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2022

Data on Cu- and Ni-Si-Mn-rich solute clustering in a neutron irradiated austenitic stainless steel

The data presented in this article is supplementary to the research article “Phase instabilities in austenitic steels during particle bombardment at high and low dose rates” (Levine et al.). Needle-shaped samples were prepared with focused ion beam milling from a 304L stainless steel that was irradiated with fast neutrons (E 0.1 MeV) in the BOR-60 reactor at 318 °C to 47.5 dpa. Atom probe tomography (APT) experiments in voltage mode were then conducted on a Cameca LEAP 5000X HR. Atom position, range, and mass spectrum files after reconstruction with Cameca’s IVAS software are included. Cu- and Ni-Si-Mn-rich solute nanoclusters were identified and analyzed using the Open Source Characterization of APT Reconstructions (OSCAR) program. Python code for OSCAR, information on the program’s underlying algorithm, and sample output files are provided. A proximity histogram of a Ni-Si-Mn-rich cluster and a 1D density/solute concentration profile of a Cu-rich cluster are given to demonstrate OSCAR’s analytical functionalities. The provided APT dataset is valuable for benchmarking phase instabilities in neutron-irradiated austenitic stainless steels that occur at high doses. The OSCAR program can be reused to process other APT data sets where solute nanoclustering is of interest.

42 ENGINEERING↗
DOE OSTI2022

Synergies between H, He and radiation damage in dual and triple ion irradiation of candidate fusion blanket materials

Three ferritic/martensitic alloys were studied to understand the synergistic effect between single ion beam (Fe 2+ ), dual ion beam (Fe 2+ +He 2+ and Fe 2+ +H + ), and triple ion beam (Fe 2+ +He 2+ +H + ) irradiations on cavity evolution. A commercial alloy, F82H, a castable nanostructured alloy, CNA3, and a high purity model alloy, Fe8Cr2W, were irradiated at 400°C to 600°C to a damage level of 50 dpa at a damage rate of 1 × 10 –3 dpa/s with He and H injection rates of 10 and 40 appm/dpa, respectively. Post-irradiation characterization via bright field transmission electron microscopy and high-angle annular dark-field scanning transmission electron microscopy was performed on all irradiated conditions to characterize the cavity size distribution and determine the effects of H/He injection on cavity microstructure. In all three alloys, hydrogen co-injection with helium resulted in an increased cavity number density and maximum cavity size, producing an increase in swelling over that from helium injection alone. Swelling in F82H appears to peak between 450°C and 500°C. At 600°C, swelling was minimal and cavities of high density and small size were confined to grain boundaries and dislocations while at 400°C, swelling is also low with a nearly homogeneous, high density, distribution of very small cavities throughout. Swelling was least in the commercial alloy F82H due to the high sink strength. The CNA3 alloy underwent dissolution of precipitates that lowered the sink strength and resulted in higher swelling than F82H, but less than the model alloy. Electron energy loss spectroscopy (EELS) elemental mapping revealed hydrogen forming a halo-like structure about the periphery of the cavities and helium residing within the cavities themselves. Finally, this observation suggests that hydrogen reduces the surface energy of helium-filled cavities which results in both increased cavity number density and cavity size in triple beam irradiation over dual beam irradiation.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Solute segregation and precipitation across damage rates in dual-ion–irradiated T91 steel

We report that dual-ion irradiations using 5.0 MeV defocused Fe 2+ ions and co-injected energy degraded 2.00 to 2.85 MeV He 2+ ions were conducted on a Fe9CrMo ferritic-martensitic steel T91 to 17 dpa at a damage rate range of 5 × 10 -5 dpa/s to 3 × 10 -3 dpa/s at 445°C, followed by characterization of the microstructure using conventional and scanning transmission electron microscopy. Radiation induced Ni/Si clusters and radiation induced segregation were quantified using energy dispersive X-ray spectroscopy at each condition and were compared with the same material irradiated in the BOR-60 reactor and in the as-received condition. No significant Cr segregation was found at lath boundaries after dual-ion irradiation, while Ni and Si enrichments both decreased with increasing damage rate leading to a sharp decrease in the density of Ni/Si clusters with damage rate. Increased point defect recombination at higher ion damage rates likely reduced the Ni/Si cluster density compared with BOR-60. Although the overall vacancy concentration and diffusion are enhanced by the irradiation damage rate, the lack of time for thermal diffusion and ballistic displacements of solutes are significant limiting factors for Ni/Si cluster formation. This work demonstrates the effect of irradiation damage rate on elemental segregation and clustering when using ion irradiation to simulate reactor irradiation.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Predicting structural material degradation in advanced nuclear reactors with ion irradiation

Swelling associated with the formation and growth of cavities is among the most damaging of radiation-induced degradation modes for structural materials in advanced nuclear reactor concepts. Ion irradiation has emerged as the only practical option to rapidly assess swelling in candidate materials. For decades, researchers have tried to simulate the harsh environment in a nuclear reactor in the laboratory at an accelerated rate. Here we present the first case in which swelling in a candidate alloy irradiated ~ 2 years in a nuclear reactor was replicated using dual ion irradiation in ~ 1 day with precise control over damage rate, helium injection rate, and temperature and utilize physical models to predict the effects of radiation in reactors. The capability to predict and replicate the complex processes surrounding cavity nucleation and growth across many decades of radiation dose rate highlights the potential of accelerated radiation damage experiments. More importantly, it demonstrates the capability to predict the swelling evolution and the possibility to predict other features of the irradiated microstructure evolution that control material property degradation required to accelerate the development of new, radiation-tolerant materials.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

Corrosion behavior of ferritic FeCrAl alloys in simulated BWR normal water chemistry

Ferritic iron-chromium-aluminum (FeCrAl) alloys with varying Cr content were subjected to in-situ irradiation-corrosion with energetic protons or electron beams in pure water with various oxygen concentrations. Oxide microstructure and composition were characterized to compare the corrosion under irradiation with the thermal corrosion in the same water conditions. The dominant effect seems to be the production of H 2 O 2 at the surface by the intense proton and electron beams. The corrosion potential of FeCrAl under BWR-NWC condition is somewhat above the Cr 2 O 3 /CrO 4 2- phase boundary, oxidizing the Cr(III) to Cr(VI) in the outer part of the film, but with some Cr(III) remaining in the interior of the oxide. The beam increases the corrosion potential, significantly reducing Cr(III) content throughout the oxide. Finally, the crystallites on the surface, which form by re-precipitation from solution, do not contain Cr because at low potential Cr(III) is not soluble, and at high potential Cr(VI) is quite soluble.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Microstructural characterization of cold-worked 316 stainless steel flux thimble tubes irradiated up to 100 dpa in a commercial Pressurized Water Reactor

Two flux thimble tubes (FTT) made of 15% cold-worked 316 stainless steel (SS) were harvested from Ringhals Pressurized Water Reactor (PWR) Unit 2, with peak damages of 76 and 100 displacements per atom (dpa) after 29 and 34 years’ service, respectively. Specimens sectioned from parent tubes were comprehensively characterized with nominal damage levels of ~0, ~41, ~74, 76, and 100 dpa at a nominal temperature range of 285-323 °C. Both FTTs contained helium and hydrogen gases as transmutation products. The helium follows a production rate of ~9.8 appm/dpa, while environmental factors complicate hydrogen production obscuring an exact H/dpa ratio. Irradiation-induced dislocation loops, nano-cavities, solute clusters, and microsegregation were all observed. The dislocation loops and nano-cavities indicated saturation at 41 dpa. The solute clusters continued to evolve with Ni-Si clusters formed at 41 dpa, and Ni-Si-Mn-P clusters formed at 74 and 100 dpa, but neither clusters exhibited distinct diffraction patterns at any damage levels. Solute clusters were observed to frequently be co-located with dislocation loops, but fully decorated loops were rarely detected. Significant radiation-induced segregation (RIS) was observed around grain boundaries at all damage levels. The modified inverse Kirkendall (MIK) model captured the RIS behavior of major elements. Large cavities within or around an Mn-S rich region were observed for the first time. Through all the damage levels, void swelling is always below 0.05%, making significant dimensional change unlikely in core internals when used at similar conditions. Meanwhile, the role of overwhelming nanocavities, presumably helium bubbles, should be considered in other potential degradation mechanisms, including irradiation-assisted stress corrosion cracking, embrittlement, and loss of fracture toughness, which remain the concerns for extended operation of nuclear power plants.

Post Irradiation Examination, Isotope Dilution Mas↗
DOE OSTI2020

A methodology for customizing implantation profiles of light ions using a single thin foil energy degrader

We report a method was developed to quantify the spatial distribution and implantation depth of energy-degraded light ions with a thin foil rotating energy degrader for use during multiple ion beam irradiation. The methodology covers three physical phenomena: ions passing through the thin foil, ions travelling through the vacuum to the target, and ion implantation into the target, and accounts for the distribution of ions both in depth and in plane. The processes of energy straggling and scattering were calculated using SRIM. The effects of raster-scanning, and the geometry of the system were implemented in scripts handling the SRIM output files. Elastic backscattering (EBS) using 2.38 MeV H+ protons was used to measure the helium depth profiles after implantation with and without thin foil energy degradation. Defect analysis with transmission electron microscopy confirmed the implantation profiles measured with EBS and calculated with SRIM.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗