Weibel, Justin A. | Search NASA

DOE OSTI2025

Slippery liquid infused porous surface (SLIPS) condensers for high efficiency air gap membrane distillation

Abstract To address growing water scarcity, we must improve the energy efficiency of thermal desalination technologies such as air gap membrane distillation. However, promising functional materials such as slippery liquid infused porous surfaces have not yet implemented for any desalination technology. Here, we fabricate and test slippery liquid infused porous surfaces (using Krytox 16,256 lubricant and CuO nanostructures) in an air gap membrane distillation apparatus. System-level transport models, validated by experimental data, establish a framework for improving performance through enhanced condensation surfaces. Results are obtained across a range of temperatures (50–80 °C), salinities (5–105 g/kg), and module lengths. We find that small air gap thickness and efficient droplet shedding significantly improves performance. The CuO Krytox process achieves these with a conductive-self-limiting coating, high nanostructure rugosity, strong covalent and metallic bonding, high hydrophobicity, minimal droplet pinning sites, and ultra-low contact angle hysteresis. The greatest efficiency enhancement from SLIPS is derived from the improved droplet shedding, which allows for reduced gap sizes without flooding, and is further augmented by the increased permeate flux.

Yogi, Yashwant S.↗

DOE OSTI2021

Adhesive Bonding of Copper Prepared by Laser-Interference near the Interference Structuring Limits

Adhesive bonding requires adequate surface preparation for ensuring an appropriate joint quality. The interest in adhesive joining has recently expanded to thermal systems having a large number of joints employed for manufacturing and assembly. This study presents surface topology of copper 110 produced by a laser-interference setup that would theoretically yield a periodicity of 1.7 μm, which is near the 1.6–2 μm structuring limit that was estimated based on thermal diffusion length scale for an 8 ns laser pulse. The results show that although the expected periodic interference structuring was not attained, the melt-induced texturing was affected by the laser-interference profile. Single-lap shear tests were performed with specimen surfaces prepared by traditional abrasion and laser-interference structuring methods. Several laser processing parameters, such as the laser spot size, density, number of pulses, and raster speed, were studied. Scanning electron microscope and profilometry measurements were used to characterize the processed surface microstructures. Web-like structures, which indicate widespread melting, were shown to be formed at different processing conditions. Based on the surface topologies investigated, two laser raster speeds were selected to make single-lap-joint specimens. Baseline joints were prepared by abrading joining specimens. The shear-lap strength and displacement at maximum load were shown to be higher by 16.8% and 43.8% for the laser-structured specimens than those of the baseline specimens, respectively. Moreover, the load-displacement curves indicated that the laser-structured joints were more ductile than those without laser-structuring. The increased ductility for the laser-structured joints was found to yield an increase in the energy absorbed during shear-lap testing of approximately of 80–90% over those measured for baseline joints. It is another indicator that laser-interference structuring enhanced the bonding performance of single-lap shear joints.

36 MATERIALS SCIENCE↗