Novel Fast Cure Silicone Inks for Single-Step, Support-Free 3D Printing of Tall, Overhanging, and High Aspect Ratio Structures

Silicone elastomers have a broad variety of applications, such as soft robotics, biomedical devices, and structural metamaterials. The extrusion-based method known as direct ink write (DIW) has enabled the production of additively manufactured silicone structures. However, this method is limited to manufacturing mostly planar or pseudo-3D structures. Due to the low self-supporting capabilities of extruded strands for traditional silicone-based “inks,” obtaining tall or overhanging structures, or structures comprised by thin walls is not feasible. Here, in this study, a novel Fast Cure silicone-based ink is demonstrated that enables manufacturing of complex 3D structures. The Fast Cure ink is a two-part mixture and silicone structures are produced by inline mixing and coextrusion of a part containing a catalyst (part A) and a part containing a crosslinker (part B). By the virtue of crosslinking, the extruded strands rapidly rigidize, increasing their self-supportive capacity. Hence, structures can be obtained with superior shape retention and previously unobtainable parts are realized that are tall, with aspect ratios higher than 3, and have overhanging features, achieving inclination angles smaller than 35° with respect to the printing plane. These minimal sag parts are achieved without requiring extra curing or mechanisms, support structures, or suspension baths.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Modeling of Sagging for 3D Printed Layers During the Curing Process

Here, a printed layer of silica-enforced poly(dimethylsiloxane)-co-(diphenylsiloxane) is modeled as a two-phase system consisting of air and polymer with an interface set up during the printing process. The structural geometry changes mostly due to the action of surface tension, while all material properties are strongly temperature dependent. Polymer flow is described using equations of the extended Herschel–Bulkley model, with parameters strongly dependent on temperature and degree of curing. Parameters of the model are determined using flow sweep measurements and separate experiments with vertical structure sagging at different temperatures. The curing process is modeled using dependencies between the curing rate, degree of curing, and temperature obtained in studies by differential scanning calorimetry. The developed model is used for simulations of printed structure deformations with different initial and boundary conditions.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Controlled In Situ Foaming for Mechanical Responsiveness of Architected Foams

Addition of chemical blowing agents to polysiloxane resins produces foams with closed–cell morphology. Combining this chemistry with the 3D–printing technique direct ink writing (DIW) permits the creation of architected foams with controllable, hierarchical tiers of porosity. Here, using a two–component foaming ink, the extent of foaming can be controlled by incorporating an active mixing printhead as part of the fabrication process. Changes in the mixing speed allows for in situ control of the foaming reaction where the mixing speed is directly correlated with the resulting foaming that occurs upon extrusion. These architected foams display tunable mechanical responses, porosities, and open–to–closed cell ratios. While chemically blown polysiloxane foam is a well–established material, utilizing DIW as fabrication technique presents a novel approach for creating tailored, architected foams that require minimal post–processing.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Virtual Volumetric Additive Manufacturing (VirtualVAM)

Abstract Tomographic volumetric additive manufacturing (VAM) produces arbitrary 3D geometries by exposure of a rotating volume of photopolymer resin to tomographically‐patterned illumination. This enables high speed, layer‐less printing of parts from a wide range of photopolymers not amenable to layer‐by‐layer processes. Since the entire geometry is produced at once over the course of a few seconds to minutes, molecular diffusion length scales become significant to the printing process. Understanding these molecular reaction and diffusion processes is imperative for advancing VAM to a usable technology. These processes are experimentally very difficult to monitor and measure. Herein, VirtualVAM ‐ a simulation framework for modeling the tomographic VAM process, is developed and experimentally validated. VirtualVAM simulates reaction, diffusion, and heat generation processes over the course of a print with single‐voxel resolution. From a few experimentally‐determined input parameters and a set of images for projection, VirtualVAM is able to generate a large spatio‐temporal data set for any given tomographic VAM print. Using VirtualVAM, a number of experimentally‐unattainable aspects of the VAM process are investigated such as single‐voxel conversion profiles, effect of molecular oxygen, and stopping time determination. VirtualVAM also enables the optimization of exposure patterns to further improve contrast between in‐part and out‐of‐part delivered dose.