DOE OSTI2025

Phase Field Modeling of Chemical Reaction Related Damage Evolution in Environmental Barrier Coatings

The advent of next-generation engines necessitates materials capable of withstanding temperatures beyond the reach of current superalloys. SiC-based ceramic matrix composites, augmented with environmental barrier coatings (EBCs), present a promising materials solution. Given the active search for effective and durable EBCs, there is a pressing need for modeling tools to understand and predict damage evolution in these materials to help accelerate their development. This study introduces a phase-field model (PFM) designed to simulate the thermally grown oxides (TGO) and phase transformation in the degradation and failure of EBCs. The model accounts for the severe volume expansion due to oxidation, alongside phase transformations and porosity evolution during thermal cycling, offering a comprehensive view of the damage processes. Simulation results are validated against experimental findings reported in the literature, establishing the model's potential as a significant tool for understanding and improving the resilience of EBCs in cyclic oxidative environments.

fast-diffusion path↗

DOE OSTI2025

Combined Creep and Fatigue Modeling

Simultaneous consideration of creep and fatigue is of paramount importance to accurately predict component life in many industrial applications. For example, growing penetration of renewable energy onto the grid is forcing many power plants to transition from base-load power generation to more complex operation modes, characterized by a combination of base-load generation and frequent start-up and shut-down cycles. The frequent start-stop of power plants is causing a significant toll in the component life due to fatigue. As such, creep alone is not adequate anymore to predict the component life. Most existing life prediction models consider creep or fatigue independently while neglect their interactions. In this presentation, we talk about some recent efforts at NETL to develop a unified modeling framework where both creep and fatigue can be considered. The creep-fatigue interaction mechanism is studied. High-throughput simulations are performed under various hold stress and hold time, and analytical expressions are fitted for the crack growth rates under creep and/or fatigue conditions demonstrating some applications of this newly developed modeling capability.

advanced alloy development↗

DOE OSTI2025

Microstructure-Based Degradation Modeling in Solid Oxide Cells

The presentation is intended for a graduate class in Georgia Southern University taught by Dr. Hayri Sezer on electrochemistry, SOFC and Li ion battery. It summaries NETL's recent works on microstructure-based modeling of degradation in solid oxide cells. It covers the degradation mechanism of Ni coarsening, Ni migration and the build-up of oxygen partial pressure inside the electrolyte. The phase-field models developed for Ni coarsening and migration are reviewed and the results are compared to experiments in literature to examine different diffusion mechanisms (Ni self-diffusion, Ni(OH)2 diffusion in pores and Ni(OH) surface diffusion) and driving forces (Ni(OH)x concentration and Ni-YSZ contact angle change). It also demonstrates the developed model for oxygen partial pressure and shows that the predicted oxygen partial pressure can explain the Ni oxidation in the hydrogen electrode and crack growth on the electrolyte-oxygen electrode interface under certain operating conditions.

nickel coarsening↗

DOE OSTI2025

Phase-Field Modeling of Damage Evolution in Ceramic Matrix Composite (CMC) and Environmental Barrier Coating (EBC)

Ceramic matrix composites (CMCs) protected by environmental barrier coatings (EBCs) present a promising materials solution for next generation gas turbines. Developments of more robust and efficient EBCs and mechanically tougher CMCs are thus of significant technological importance. Here we develop a phase-field modeling framework that incorporates the thermally grown oxide (TGO), recognized as a critical factor for degradation and failure of EBCs. We simulate crack growth in the TGO and the potential extension into the bond coat / CMC substrate. The model efficiently takes account of the large inelastic deformation induced by the severe volume expansion of TGO, thanks to our recently developed, so-called incremental realization of inelastic deformation (IRID) algorithm. A phase-field model is built for damage evolution in CMCs including crack growth and interfacial sliding. The effects of fiber layout and interfacial sliding on the macroscopic toughness of CMCs are revealed by large-scale simulations and compared to experiments.

advanced energy systems and materials↗