NASA NTRS1984

High-efficiency silicon solar cells

Silicon solar cells are described which operate at energy conversion efficiencies independently measured at 18.7 percent under standard terrestrial test conditions (AM1.5, 100 mW/sq cm, 28 C). These are apparently the most efficient silicon cells fabricated to date. The high-efficiency results from a combination of high open-circuit voltage due to the careful attention paid to the passivation of the top surface of the cell, high fill factor due to the high open-circuit voltage and low parasitic resistance losses, and high short-circuit current density due to the use of shallow diffusions, a low grid coverage, and an optimized double layer antireflection coating.

Green, M. A.↗

NASA NTRS1984

18-percent efficient terrestrial silicon solar cells

Silicon solar cells are described which operate at energy conversion efficiencies in excess of 18 percent under standard terrestrial test conditions (AM1.5, 100 mW/sq cm, 28 C). These are believed to be the most efficient silicon cells reported to date. The high efficiency is a result of the combination of high open-circuit voltage due to the careful attention paid to passivation of the top surface of the cell; high fill factors due to the high open-circuit voltage and low parasitic resistance losses; and high short-circuit current due to the use of shallow diffusions, a low grid coverage, and an optimized double-layer antireflection coating.

Blakers, A. W.↗

NASA NTRS1984

Towards a 20 percent efficient silicon solar cell

A project is underway at the University of New South Wales aimed at producing a 20 percent efficient silicon solar cell. A prerequisite for obtaining such a significant increase in cell efficiency is the improvement of the open circuit voltage of these cells. Two techniques are described which have produced experimental devices with open circuit voltages of 690 mV or higher. These high voltage techniques have been combined with other high efficiency design features to produce silicon cells with independently measured energy conversion efficiencies in excess of 19 percent under standard terrestrial test conditions (direct beam AM1.5 spectrum, 100 mW/sq cm, 28 C).

Green, M. A.↗