4 records

DOE OSTI2023

Understanding the effect of specimen size on the properties of fine-grain isotropic nuclear graphite for irradiation studies: Mechanical properties

Programs at Oak Ridge National Laboratory are investigating the effects of neutron irradiation in the High Flux Isotope Reactor (HFIR) on properties of fine-grain isotropic nuclear graphites. Specimens were irradiated in the HFIR flux trap, which requires using specimens that are smaller than the sizes recommended by ASTM standards. Here, this work has investigated whether subsized specimens can be used to reliably predict strength behavior. The results show that (1) tensile strength was loosely coupled to specimen volume, (2) the compression specimens had a slightly higher strength for larger volumes, (3) the uniaxial flexural strength was nearly independent of specimen effective area for one orientation whereas the other orientation showed a slight strength–size scaling Weibull behavior, and (4) equibiaxial flexural strength followed traditional strength–size scaling Weibull behavior. These results suggest that fine-grain graphite is more similar to ceramics than to medium- and large-grained graphite with respect to both the strength-limiting flaws (Griffith theory) and the effect of machining on the strength behavior. This work shows that using specimens that are smaller than ASTM recommendations are suitable for investigating the strength changes caused by neutron irradiation because the primary interest is the relative change in the strength distribution parameters rather than their absolute values.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Equibiaxial Flexure Strength of a Superfine-Grained Nuclear Graphite

The strength of advanced graphite is reported in accordance with ASTM D7846-16 using a two-parameter Weibull distribution for uniaxial strength testing. The rule of thumb for Weibull distributions is to use a minimum of 30 strength measurements to have a high level of confidence in the Weibull characteristic strength and the Weibull modulus. These large sample sets for statistical confidence are easily obtained for as-manufactured graphite, but determination of the Weibull two-factor parameters on graphite that has been exposed to neutron irradiation is nearly impossible due to irradiation testing restraints on specimen size and space limitations in test reactors for the accommodation of specimens. These restrictions have resulted in irradiation programs that use sub-sized specimens to measure uniaxial strength change, but the specimen geometries still hinder the number of replicate specimens for each irradiation condition. In contrast, this work used an advanced ceramic standard, ASTM C1499-05, as the foundation for equibiaxial strength testing of a superfine-grained nuclear graphite to investigate the irradiation-induced strength change and any changes to the two-parameter Weibull distribution. The goal was to investigate the effect of specimen size on the two-parameter Weibull distribution parameters in support of the small specimens and geometry desired for irradiation. A study of the effect of a reduced sample population was also undertaken to investigate the reliability of using the two-parameter Weibull distribution to study changes to the materials properties caused by neutron irradiation damage. The results of this work suggest that these equibiaxial specimens would be ideal for statistically significant studies of the effects of irradiation on the Weibull characteristic strength (but not the modulus) and for providing a method for surveillance specimen campaigns for future operating commercial reactors.

Campbell, Anne↗

DOE OSTI2022

Rotational flexural strength of cylindrical brittle specimens

Conventional static flexural strength testing of brittle cylindrical rods only subjects a small fraction of the entire specimen's area or volume to the maximum tensile stress. Thus, a nonconservative measured strength likely results since most flaws on the surface or in the bulk are not subjected to a sufficiently high tensile stress that can cause fracture. Here, to mitigate this, a rotational flexural tester and corresponding test method were developed whereby rotation and monotonically increasing three-point flexure were superimposed to investigate fracture response of solid glass cylinders. This combination of rotation and flexure subjects more area and volume of a cylindrical test specimen to tensile stress than a standard static (nonrotating) flexural test. As anticipated, failure stresses were lower for the rotational flexural test. Expressions for effective area and volume are provided for rotating solid rods and tubes subjected to three-point, four-point, uniform, and uniformly distributed load bending configurations.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Industrial Scalable Additives for Enhanced Decomposition of Plastic Waste Through Photocatalysis

Polymer pollution is a dangerous environmental problem that can lead to the spread of toxic chemicals and microplastics throughout aquatic biomes. Commonly littered plastic from consumer goods and products with a limited or single use can be embedded with photocatalysts to avoid an increase in the amount of plastic present in Earth’s bodies of water. In this work, the photocatalyst nanoparticles, less than 100 nm particle size, were integrated into polyethylene terephthalate, high-density polyethylene, low-density polyethylene, and polystyrene and exposed under ultraviolet light over two independent experimental trials examining both the environmental factors impacting decay and the physical parameters required to implement this solution on a large scale. The plastics were chosen due to their prolific use in items such as grocery bags, bottles, and packaging. The first half of the project examined the effects of water and light frequency on polymer decay, and the second half of the project examined photodecomposition of polymer films. We report that low-density and high-density polyethylene films with titanium dioxide decayed approximately 11.7 and 9.6 faster than control samples, respectively. With an estimated price of less than half the cost of a shopping bag for titanium catalyst integration and a retention of the polymer’s tensile strength with a 2 wt% catalyst concentration, photocatalytic decomposition is a feasible, scalable method for the prevention and future reduction of polymer waste from realistic products littered in the environment.

36 MATERIALS SCIENCE↗