Local Background Hole Density Drives Nonradiative Recombination in Tin Halide Perovskites
In this study, we use multimodal microscopy to study carrier recombination in semiconducting tin halide perovskite films based on PEA 0.2 FA 0.8 SnI 3 (PEA = phenethylammonium; FA = formamidinium). We use the observation of pseudo-first-order photoluminescence (PL) decay kinetics to establish a method for quantifying the hole dopant level and nonradiative recombination rate constant. We find that untreated PEA 0.2 FA 0.8 SnI 3 films exhibit large hole doping concentrations of p 0 ≈ 10 19 cm –3 , which is reduced to p 0 ≈ 10 16 cm –3 after SnF 2 treatment. While it is well-known that the radiative recombination rates are increased with p 0 , we reveal that the nonradiative rate is also increased. We find that p-type regions in untreated PEA 0.2 FA 0.8 SnI 3 films are centers for nonradiative recombination, which are diminished in films with p 0 ≈ 10 16 cm –3 . We discover significant PL heterogeneity even in PEA 0.2 FA 0.8 SnI 3 films with moderate dopant levels, suggesting that new strategies to eliminate deleterious defects in PEA 0.2 FA 0.8 SnI 3 must be developed.