Engineering topics
Publications and source records attributed to Westover, Andrew.
A high temperature multibeam-optical-stress sensor (HTMOSS) was used to characterize the coefficient of thermal expansion (CTE) and yield stress of 1-micron thick Lipon films.
The development of a solid electrolyte that can impede dendrite growth while still maintaining an appropriate level of conductivity is essential for improving performance of solid-state Li-ion battery. In this paper, we report the synthesis of single Li-ion conducting hairy nanoparticle (NP) materials that improved the cycling stability of lithium bis(trifluoromethanesulfonyl)imide (LiTFSI)-doped poly(ethylene oxide) (PEO) solid electrolyte without significant reduction in conductivity. To unveil mechanisms leading to improved cycling stability, several characterization techniques including broadband dielectric spectroscopy, differential scanning calorimetry, small angle X-ray scattering, transmission electron microscopy, and shear rheology were used to study properties of polymer composites (PC) with added hairy NPs. It was found that hairy NPs influenced the Li/electrolyte interface and improved mechanical properties of bulk composites, all of which contributed to homogenous Li plating and stripping. The improved performance has been found in composites with concentrations of 4.8 and 9.1 weight % of added hairy NPs, which enabled Li cycling stability at 0.2 mA cm–2 critical current density (>300 h) that was otherwise not possible in either PEO-LiTFSI alone or PEO-LiTFSI composites containing a polymer identical to that attached to hairy NPs. Based on the discovered ability of hairy NP to influence bulk and interfacial properties of solid electrolyte, their use as additives is expected to be equally effective in reducing dendrite formation in other electrolytes relevant for the design of solid-state battery.
Integrating sulfide separators into solid-state batteries (SSBs) containing high energy cathodes typically requires one or more materials and engineering solutions including: (i) applying interfacial coatings to mitigate electrolyte decomposition, (ii) applying high stack pressures to form robust solid-solid contacts, and (iii) using alloying anodes to avoid Li dendrite formation. Despite the promise of these approaches, a lack of standardized testing protocols makes it difficult to directly compare results among different studies. To address this problem, the present work benchmarks the performance of SSBs containing β-Li 3 PS 4 (LPS) separators and composite cathodes. By systematically varying the anode/cathode composition and stack pressure, this work demonstrates that cathode design is a major bottleneck for solid-state cells cycled at low rates (<100 µA cm -2 ). Operando stack pressure measurements show that, while mechanical confinement generally promotes higher active material utilization and cycling stability, this strategy alone does not address interfacial reactivity between LPS and high voltage cathodes. Here, these results also demonstrate that stress evolution during cycling is dominated by volume changes at the Li metal anode. Finally, we show that FeS 2 cathodes with moderate operating voltages (<3 V vs Li/Li + ) exhibit superior cycling performance compared to high voltage cathodes by facilitating formation of stable cathode/electrolyte interfaces.
High-areal-capacity cathodes are needed for energy-dense solid-state batteries. Here, we demonstrate a bilayer polymer electrolyte design for cycling 3–6 mAh/cm 2 NMC811 composite cathodes. In this work, the bilayer electrolyte comprises a cross-linked poly(ethylene oxide) (PEO)-based electrolyte layer and a linear-PEO-based electrolyte layer. The former provides dendritic resistance, and the latter provides a seamless interface with the cathode during cycling. Using a single layer of either membrane led to severe shorting or extremely low Coulombic efficiency (CE) in the first cycle. The general concept of a rigid dendrites-inhibiting electrolyte facing Li anode and a softer, cathode-integrated electrolyte that ensures contact with the cathodes during cycling may present a pattern for enabling high-energy-density cathodes.
Solid-state lithium metal batteries (SSLMBs) containing polyethylene oxide (PEO)-derived polymer electrolytes and high-voltage (> 4 V vs. Li/Li + ) cathode materials suffer from three sources of failure: (1) instability between the polymer electrolyte and cathode at high voltage, (2) instability of the polymer electrolyte with Li metal, and (3) poorly-designed cathodes. In this study, these three sources of failure are deconvoluted by studying Ni-rich LiNi x Mn y Co 1-x-y O 2 (NMC, x ≥ 0.6) cathodes and a gel polymer electrolyte (GPE) derived from PEO. Initial cycling data reveals that rapid capacity fade occurs regardless of whether soft short circuits form due to Li dendrites. Cyclic voltammetry scans on cells featuring a Li metal electrode, GPE, and a NMC811 electrode free of additives suggest that there are no runaway reactions between the GPE and NMC811 up to 4.5 V vs. Li/Li + . Cathode/cathode symmetric cell cycling demonstrates that Li metal reactivity is a prime source of failure, though a poorly-designed cathode leads to subpar performance. A cathode with single-crystal NMC particles was demonstrated to achieve better initial capacity and longer cycle life, indicating room for improvement in SSLMB cathode design. Therefore, the sources of failure as enumerated may be ranked as follows from most to least concerning: 2 > 3 > 1.
Here we report the dependence of mechanical properties and ionic conductivity of the Na 1+ x Mn x /2 Zr 2– x /2 (PO 4 ) 3 (designated as NMZP) ionic conductor on its composition (with x = 0.5, 1.0, 1.5, and 2.0). Local mechanics was studied by instrumented nanoindentation, and the properties of interest included the elastic modulus, hardness, and fracture toughness. Overall, the material becomes more compliant and soft with the increase in the Na content. The elastic modulus reduces from 120 to 80 GPa, and nanoindentation hardness reduces from 7.8 to 4.2 GPa when x changes from 0.5 to 2.0. The relationship with fracture toughness ( K C ) is highly nonlinear: fracture toughness first decreases and then increases with the increase in the sodium content, reaching a maximum value of 0.89 MPa × m 1/2 at x = 2.0. Such a relationship was found to correlate with the formation of a glassy phase in NMZP at intermediate Na concentration. The maximum ionic conductivity coincides with the maximum fracture toughness in this material.