Passive Temperature Sensors for Nuclear Applications

Thermocouples are generally used to provide real-time temperature indications in instrumented tests performed at material and test reactors. Passive temperature monitors, such as Silicon Carbide (SiC) and melt wires, may be included in such tests as an independent technique of detecting peak temperatures experienced during irradiation. In less expensive static (drop-in) capsule tests, which have no leads attached for real-time data transmission, melt wires, and SiC temperature monitors (TMs) are essentially the only possibility for peak temperature indication. A melt wire involves placing materials (wires) of a known composition and melting temperature in a test. An inventory is maintained at Material Science Laboratory (MSL) for melt wires ranging in temperatures from 30°C to 1500°C. Unfortunately, melt wires are limited in that it can only detect whether a single temperature is or is not exceeded (melt wire melted or not). SiC TMs, which can also be used to detect peak irradiation temperatures, are advantageous because a single monitor can allow to determine the peak temperature reached within a relatively broad range (100 – 1200°C) resulting in accuracies within ±20°C. Irradiation temperature is determined by measuring a property change after isochronal annealing or during a continuously monitored annealing process using specialized equipment at MSL. Recent research has produced a passive monitor known as sublime temperature monitor. This passive sensor has the capability of recording temperature gradients and pinpointing exactly where a temperature is located along that gradient. Long measurement lengths are achieved with very high accuracy in the location of desired temperature measurements (±2 mm over a 1 m span); however, this sensor has not been deployed in a nuclear reactor. This article will focus only on passive temperature sensors currently being researched and implemented under the Advanced Sensors and Instrumentation (ASI) program at Idaho National Laboratory (INL).

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Silicon Carbide Passive Temperature Sensors at INL

Discuss the SiC passive thermometry methods currently performed at INL and ORNL, decide on best path forward for establishing an ASTM Standard for processing SiC temperature monitors, and expand this ASTM benchmarking efforts to international collaborators (Netherlands, Canada, and Poland).

36 MATERIALS SCIENCE↗
DOE OSTI2024

Instrumentation for the In-Core Real-Time Mechanical Testing of Structural Materials (INCREASE) Project

Idaho National Laboratory (INL), in collaboration with the Electric Power Research Institute (EPRI), the Nuclear Regulatory Commission (NRC), the French Atomic and Alternative Energies Commission (CEA), the Joint Research Center (JRC), the Nuclear Research and Consultancy Group (NRG), and the Research Center Rez (CVR), started a Joint Experimental Program (JEEP) project that operates within the Nuclear Energy Agency’s Framework for Irradiation Experiments (FIDES II) program in order to develop capabilities for the in-core real-time mechanical testing of structural materials. This effort will focus on designing a shared capsule capable of housing a variety of in-core mechanical testing instrumentation allowing enhanced experiments for the material science community. The outcome of the project would be high-priority, stress relaxation data for stainless-steel-based materials provided by EPRI and CEA. Stress relaxation is a major phenomenon that contributes to material degradation in nuclear reactor components. Currently, nuclear material stress relaxation is assessed both before and after irradiation, using complex and costly post-irradiation examination (PIE) activities. In-situ data would support the development of precision modeling and simulation of this degradation phenomena and would provide validation and benchmarking for existing models using the PIE data. As part of the U.S. Department of Energy Advanced Sensor and Instrumentation (ASI) program, INL has fabricated and tested out-of-core mechanical test instrumentation. This instrumentation was designed for easy adaptation to the irradiation capsule proposed under this JEEP, and can be deployed to measure real-time stress relaxation under pressurized-water reactor (PWR) conditions. This initial effort will partially serve to replace the testing capabilities lost because of shutting down the Halden Boiling Water Reactor (HBWR). The project would provide these capabilities to the international community via a shared capsule design that is easily adaptable to additional material test reactors. The design features will incorporate expansion to PWR and non-light-water reactor (LWR) environments that will be developed in future work. The capsule and instrumentation will be demonstrated in the Massachusetts Institute of Technology Reactor (MITR) for phase I and the Petten High Flux Reactor (HFR) for phase II irradiations to deliver real-time stress relaxation data on high priority stainless steel structural materials.

36 MATERIALS SCIENCE↗
DOE OSTI2024

INSTRUMENTATION FOR IN-CORE REAL-TIME MECHANICAL TESTING OF STRUCTURAL MATERIALS (INCREASE) PROJECT

Idaho National Laboratory (INL), in collaboration with the Electric Power Research Institute (EPRI), Nuclear Regulatory Commission, French Atomic and Alternative Energies Commission (CEA), Joint Research Centre, Nuclear Research and Consultancy Group, and Research Center Rez, is the operating agent of the In-Core Real-Time Mechanical Testing of Structural Materials (INCREASE) joint experimental program (JEEP) project that operates within the Nuclear Energy Agency (NEA)’s Framework for Irradiation Experiments (FIDES-II) program. The first objective of the INCREASE project is to design a shared capsule that can house a variety of in-core mechanical testing instrumentation for enabling smart irradiation experiments. The second objective is to collect in core stress relaxation data pertaining to high priority stainless steel (SS) materials under light water reactor conditions with target temperature of 340°C +/-20°C and a minimum neutron damage of 2 displacement per atom (dpa). The INCREASE project will be demonstrated in the Massachusetts Institute of Technology Nuclear Research Reactor (MITR).

36 MATERIALS SCIENCE↗
DOE OSTI2023

Post Irradiation Examination Results of Irradiated Yttrium Hydride

Department of Energy’s (DOE’s) Microreactor program (MRP) aims to provide the fundamental data to enable the development of microreactors. As such, material property data of critical materials for microreactor technologies are researched. Because substoichiometric yttrium dihydride (YHx, where x<2) is considered as a potential solid neutron moderator, its material property data has been combined in the Advanced Moderator Material Handbook which includes thermodynamic and thermophysical properties of YHx with the exception of irradiated material’s properties due to limited PIE. To fill the knowledge gap for the irradiated YHx, specimens and irradiation capsules were prepared at Los Alamos National Laboratory (LANL). Specimens were irradiated in the Advanced Test Reactor (ATR) at Idaho National Laboratory’s (INL’s). post-irradiation examination (PIE) was performed at INL’s Materials and Fuels Complex (MFC). This report compiles the PIE results of irradiated YHx specimens through fiscal years 2022 and 2023 (FY22-23) . The PIE data will directly be incorporated into the newer version of the Advanced Moderator Material Handbook. The main takeaways include that (i) the geometrical stability and mechanical integrity of YHx was intact with couple exceptions after high-temperature irradiations (600-800°C), (ii) hydrogen content variation due to manufacturing or irradiation in YHx caused visible surface discoloration, that is also related to the microstructural changes, (iii) qualitative comparisons of PIE methods implied that H retention was significantly higher at 600°C as compared to 800°C, (iv) thermal properties included signatures correlated with the H loss or re-gain, (v) importance of manufacturing readiness and initial as-manufactured specimens history was emphasized, (vi) the needs of targeted irradiations focusing on temperature and time parameters and very targeted PIE were specified.

08 HYDROGEN↗
DOE OSTI2023

Report on the Incorporation of Post-Irradiation Examination Results of Yttrium Hydride for Advanced Moderator Handbook

Department of Energy’s (DOE’s) Microreactor program (MRP) aims to provide the fundamental data to enable the development of microreactors. As such, material property data of critical materials for microreactor technologies are researched. Because substoichiometric yttrium dihydride (YHx, where x<2) is considered as a potential solid neutron moderator, its material property data has been combined in the Advanced Moderator Material Handbook which includes thermodynamic and thermophysical properties of YHx with the exception of irradiated material’s properties due to limited PIE. To fill the knowledge gap for the irradiated YHx, specimens and irradiation capsules were prepared at Los Alamos National Laboratory (LANL). Specimens were irradiated in the Advanced Test Reactor (ATR) at Idaho National Laboratory’s (INL’s). post-irradiation examination (PIE) was performed at INL’s Materials and Fuels Complex (MFC). This report compiles the PIE results of irradiated YHx specimens through fiscal years 2022 and 2023 (FY22-23) . The PIE data will directly be incorporated into the newer version of the Advanced Moderator Material Handbook. The main takeaways include that (i) the geometrical stability and mechanical integrity of YHx was intact with couple exceptions after high-temperature irradiations (600-800°C), (ii) hydrogen content variation due to manufacturing or irradiation in YHx caused visible surface discoloration, that is also related to the microstructural changes, (iii) qualitative comparisons of PIE methods implied that H retention was significantly higher at 600°C as compared to 800°C, (iv) thermal properties included signatures correlated with the H loss or re-gain, (v) importance of manufacturing readiness and initial as-manufactured specimens history was emphasized, (vi) the needs of targeted irradiations focusing on temperature and time parameters and very targeted PIE were specified.

08 HYDROGEN↗
DOE OSTI2022

Status of Research Activities on LVDTs: Modeling and Simulation Development and Performance Characterization of Commercial LVDTs

FY-22 research focused on two major areas. The first area was modeling and simulation with linked testing that will advance the Linear Variable Differential Transformers (LVDT) technology for use by stakeholders requiring LVDTs in upcoming irradiation tests. The second area focused on testing LVDTs purchased from U.S. suppliers that were investigated in FY-21. These cross-cutting development activities will ensure stakeholders have the current state-of-the-art LVDT-based technologies for deployment in future irradiation tests. Two stand-alone reports are included in the appendixes. The purpose of this report is to provide a convenient body of work to access the reports and to evaluate the data and conclusions provided. Appendix A, “Testing of the RDP Translation Transducer,” contains a complete evaluation of an RDP Electrosense linear transducer that has the capability of replicating the form, fit, and function of LVDTs currently being used at Idaho National Laboratory (INL). Appendix B is an extract from the report, “Advanced Sensors and Instrumentation Program at Boise State University (BSU), August 2022, Linear Variable Differential Transformers.” This report contains modeling and testing results conducted at BSU and INL.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗